锻压技术

AZ31镁合金薄带立式双辊铸轧试验研究

英文标题：Experimental study on vertial twin-roll casting for preparing AZ31 magnesium alloy strip

作者：王广山邸洪双黄峰

关键词：镁合金双辊铸轧等轴晶

分类号：TG339

出版年,卷(期):页码：2009,34(4):52-55

摘要：

利用近终形双辊铸轧薄带新工艺快速凝固、动态直接成形的特点,直接制备镁合金薄带坯。研究了镁合金立式铸轧成形工艺及退火工艺,分析了不同工艺下的微观组织。结果表明:采用铸轧工艺很好的解决了坯料成形问题,同时细化晶粒,提高镁合金薄带坯的加工成形性能。经400℃,60 min退火,可以获得平均直径9～10μm分布均匀的等轴细晶组织。

Using the characteristic of flash set and dunamic compaction in the twin roll strip casting,the magnesium alloy thin strip of near net shape was prepared.The forming technology and annealing technology of the vertical twin-roll casting technology for AZ31 mgnesium alloy were studied,and the different processes on microstructure evolution were analysed.The results show that the problem of formation in ingot is solved by twin-roll casting.Therefore,the technology can refine grain size and improve the workability of the magnesium alloy.The average equiaxed grain in diameter of 9~10 μm was obtained after annealing at 400 ℃for 60 min.

基金项目：

国家重点基础研究发展计划项目(2006CB605208-1);; 教育部高等学校博士学科点专项科研基金资助项目(20050145021)

参考文献：

[1]姚素娟,张英,梁东梅.镁及其镁合金的应用与研究[J].世界有色金属,2005,(1):26-30.
[2]王渠东,丁文江.镁合金及其成形技术的国内外动态与发展[J].世界科技研究与发展,2004,26(3):39-46.
[3]张津,章宗和.镁合金及应用[M].北京:化学工业出版社,2004.
[4]麻惠丽,王祝堂.世界镁及镁合金板带轧制回眸与展望[J].轻合金加工技术,2007,35(6):1-12.
[5]蒋斌,王健,潘复生.镁合金薄板双辊连铸的研究开发[J].材料导报,2007,21(5):330-334.
[6]李永林,李铮,邸洪双,等.AZ31镁合金薄带直接铸轧新工艺[J].轻合金加工技术,2004,32(7):15-17.
[7]Ju Dong-ying,Hu Xiao-dong.Effect of casting parametersand deformation on microstructure volution of twin-roll cast-ing magnesiumalloy AZ31[J].Transactions of NonferrousMetals Society of China,2006,16(SI):874-877.
[8]陈绪宏,丁培道,杨春楣.双辊快速凝固AZ31镁合金薄带试验研究[J].轻合金加工技术,2003,31(5):19-22.
[9]邸洪双,鲍培玮,王国栋,等.双辊铸轧薄带钢实验研究及工艺稳定性分析[J].东北大学学报(自然科学版),2000,21(3):274-277.
[10]杨春楣,丁培道,任正德,等.2002年材料科学与工程新进展[M].北京:冶金工业出版社,2002.
[11]Ju D Y,Zhao H Y.Thermal flow si mulation on twin rollcasting process for thin strip production of magnesium alloy[J].Materials Science Forum,2005,488-489:439-444.
[12]Liang D,Cowley C B.The twin-roll strip casting of magnesi-um[J].JOM TMS,2004,55-56:26-28.
[13]Kopp R,Hagemann F,Hentschel L.Thin-strip casting mod-eling of the combined casting metal-forming process[J].Journal of Materials Processing Technology,1998,(80-81):458-462.
[14]美国金属学会.金属手册[M].北京:机械工业出版社,1984:146-153.
[15]王祝堂.镁板带轧制工艺及其性能[J].中国镁业,2003,4(9):7-17.
[16]Avedesian M M,Baker H.Magnesium and Magnesium Al-loys:ASMSpecialty Handbook[M].Ohio:ASMInterna-tional,1999.

服务与反馈：

【文章下载】【加入收藏】