研究了轧制方式、轧制温度等对SiC颗粒增强铝基复合材料显微组织和力学性能的影响。轧制温度为410℃,沿平行于挤压方向进行交叉轧制可以制备出高质量、高性能的薄板。轧制态7075/SiCp复合材料薄板的力学性能为:sσ=542.51 MPa,bσ=666.09 MPa,δ=4.91%。轧制变形对挤压过程中形成的SiC颗粒条带状不均匀分布也具有改善的作用:轧制过程中,SiC颗粒破碎,尺寸明显变小,形貌呈钝化趋势,随着轧制变形量的增加,SiC颗粒分布趋于均匀。
|
|
The effects of rolling process on the microstructure and mechanical properties of the extruded spray co-deposited 7075/SiCp composite were investigated.The extruded thick sheet exhibits excellent formability along the extrusion direction.Cross rolling process can enhance the formability and mechanical properties of the 7075/SiCp sheet.Furthermore,the optimal properties of the sheet are as follows:σs=542.51 MPa,σb=666.09 MPa,and δ=4.91%.As the results of experiment,the rolling process leads to the refinement of SiC particles and the distribution state also.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]崔岩.碳化硅颗粒增强铝基复合材料的航空航天应用[J].材料工程,2002,(6):3-6.
[2]王治海.碳化硅颗粒增强铝合金复合材料特性[J].中国有色金属学报,1995,5(3):123-125.
[3]张发云,闫洪,周天瑞,等.金属基复合材料制备工艺的研究进展[J].锻压技术,2007,31(6):100-102
[4]Lee Kon Bae,Kwon Hoon.Strength of Al-Zn-Mg-Cu matrixcomposite reinforced with SiC particles[J].Metallurgical andMaterials Transaction A,2002,33A:(1):455-456.
[5]傅定发.多层喷射沉积高硅铝合金的工艺及性能研究[D].长沙:中南大学非平衡材料研究所,2001.
[6]胡代忠,陈礼清,赵明久,等.SiC颗粒增强铝基复合材料薄板的力学性能[J].中国有色金属学报,2000,10(6):831-835.
[7]陈素莹,张康生,杨翠萍,等.楔横轧工艺参数对心部疏松的影响[J].锻压技术,2007,31(4):38-39.
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|