摘要：
|
|
借助于有限元分析软件,研究了单面楔压变形时不同下压速度和不同压制温度对喷射沉积5A06铝合金变形与致密化的影响。结果表明:平均相对密度ρ随着下压速度的提高而提高,致密化较好;随着变形温度的升高,损伤值先增大后减小,在400℃时损伤值较大。综合分析后得出:合理的压制速度应取0.5~1 mm.s-1,合理的楔压温度应控制在450~500℃之间。
|
|
By the finite element analysis software,the influence of one-sided wedge pressing was studied under different pressing speeds and different cyclic pressing temperatures on the deformation and densification of spraying deposited 5A06 aluminum alloy.The result shows that the average relative density ρ rises with pressing down speed's rising,densifying fairly good.With the deformation temperature rising,damage value increases first,and then decreases.Damage value is bigger at 400 ℃.After analying in general,it is found that the reasonable velocity of cyclic pressing is 0.5-1.0 mm·s-1 and the reasonable temperature of cyclic pressing is 450-500 ℃.
|
|
基金项目：
|
|
国家科技部创新基金立项项目(07C26214301749);;
湖南省自然科学基金资助项目(07JJ5067)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈振华.多层喷射沉积技术及应用[M].长沙:湖南大学出版社,2003.
[2]袁武华,陈振华.多层喷射沉积技术的研究及进展[J].材料导报,2000,6(1):17-21.
[3]詹美燕,夏伟军,张辉,等.喷射沉积-挤压FV0812耐热铝合金的热压缩变形流变行为研究[J].湖南科技大学学报:自然科学版,2004,19(2):37-41.
[4]袁武华.喷射沉积轻量化材料的研制-高性能7075/SiCp复合材料、8009合金板材的制备及应用研究[R].长沙:湖南大学,2005.
[5]华林,秦训鹏,毛华杰,等.可压缩粉末烧结材料塑性变形与屈服条件[J].塑性工程学报,2003,10(6):62-62.
[6]詹美燕,陈振华.喷射沉积多孔材料的轧制变形理论[J].材料研究学报,2004,18(6):662-668.
[7]陈刚,刘鹏飞,范才河,等.大型喷射沉积环件的楔压致密化加工[J].矿冶工程,2006,26(2):100-102.
[8]Zhang Hui,Yang Libin,Peng Dashu,et al.Flow stress e-quation for multipass hot-rolling of aluminum alloys[J].Journal of Central South University of Technology,2001,8(1):13-17.
[9]张深根,姚德超,杨屹,等.快速凝固Al-11.5Fe-3.8V-2.3Si-Re耐热铝合金的挤压过程[J].中南工业大学学报,1996,27(1):61-64.
[10]张兴全,彭颖红,阮雪榆,等.多孔体材料在镦粗变形过程中表面裂纹的有限元预测[J].上海交通大学学报,1998,32(5):14-17.
[11]周朝辉,曹海桥,吉卫,等.DEFORM有限元分析系统软件及其应用[J].热加工工艺,2003,24(4):51-52.
[12]陈素莹,张康生,杨翠萍,等.楔横轧工艺参数对心部疏松的影响[J].锻压技术,2006,31(4):38-40.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|