摘要：
|
|
采用晶体取向分布函数(ODF)对织构进行检测及金相组织观察,研究不同的均匀化退火制度对纯铝铸轧-冷轧板材各向异性的影响。结果表明,对1100板材进行不同方案的均匀化退火,当均匀化退火制度为580℃/13 h时,板材立方织构组分比例迅速下降,同时铜织构也有所下降,但散漫度较大,同时晶粒细小均匀,随机织构比例增大,制耳率低于2.5%,板材各向异性减小。均匀化退火制度主要通过改变板材织构组分、比例、晶粒度以及改变Fe和Si组织形态的变化等影响纯铝铸轧板材的各向异性。
|
|
Influence of homogenizing annealing on anisotropy of aluminum sheet with roll-casting and cold rolling was investigated by means of texture analysis using orientation distribute function and metallographical structure observation.The results show that the content of both cubic texture {001}<100> and copper {112}<111> depress and a large amount of random texture are obtained when annealing at 580 ℃/13 h.Because of low anisotropy and homogeneous fine grain structure,earing rate of the plate is under 2%.Anisotropy of the roll-casting sheet is influenced by texture content,grain size and structure of Fe and Si which are changed by different homogenizing annealing processes.
|
|
基金项目：
|
|
江苏省自然科学基金重点项目(BK2007707)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈玉珊.工艺因素对对连续铸轧坯冷轧纯铝薄板组织性能的影响[J].轻合金加工技术,2000,28(2):16-17.
[2]史艳莉,吴建军.各向异性屈服准则的发展及应用[J].锻压技术,2006,31(1):99-103.
[3]毛卫民.金属材料的晶体学织构与各向异性[M].北京:科学出版社,2002.
[4]毛卫民,张新明.晶体材料织构定量分析[M].北京:冶金工业出版社,1991.
[5]尹德艳,梁惠冬.铝连续铸轧板冲压性能的改善[J].轻合金加工技术,1998,26(9):32-34.
[6]潘复生,张静.铝箔材料[M].北京:化学工业出版社,2005.
[7]刘楚明,张新明,陈志永,等.中间退火对高纯铝箔立方织构的影响[J].金属热处理,2001,26(3):28-30.
[8]何保得,铝合金成形过程的X射线衍射分析[J].物理测试,1990,(6):9-10.
[9]沈健,张新明.深冲用铝板的织构和各向异性[J].轻合金加工技术,1994,22(7):27-33.
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|