摘要：
|
|
用机械合金化制备的GdSiGeDy系合金粉末作为真空热压烧结的原料,研究了真空热压烧结温度、烧结时间及升温速率对烧结体磁制冷性能的影响,并用VSM测出的数据作了磁熵变曲线图。经实验研究后得出结论:升温速率对磁熵变的影响较大,且随升温速率减小,最大磁熵变增加;随着烧结温度的提高,样品的最大磁熵变是先增加,后减小,到达1050℃时,样品失去铁磁性。
|
|
The influence of hot pressing sinter process(HPS)on room temperature magnetic refrigeration properties of GdSiGeDy serial alloys was studied.GdSiGeDy powder was made by mechanical alloying method.Sinter temperature,sinter time and heat rate of HPS were investigated.The magnetic entropy change(MEC)curves were made after VSM test.The conclusion is that the heat rate has a greater influence on MCE.The value of MEC increases with the decrease of heat rate.The value of MEC increases firstly,and then decreases with the increase of sinter temperature and ferromagnetism lost when temperature reaches 1050 ℃
|
|
基金项目：
|
|
江西省科技厅重点资助项目(03Z02594)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈鹏,王敦辉,都有为.磁制冷工质材料的研究进展[J].物理学进展,1999,19(4):371 385.
[2]陈伟,钟伟,都有为.室温磁制冷材料最新进展[J].功能材料,1998,29(3):236 239.
[3]陈远富.室温磁致冷GdSiGe系合金的磁热效应、磁相变及其机制研究[D].成都:四川大学,2001.
[4]Pecharsky V K,Gschneidner Jr K A.Giant magnetocaloriceffect Gd5(Si2Ge2)[J].Phys.Rev.Lett.,1997,78(23):4494 4497.
[5]Pecharsky A O,Gschneidner Jr K A,Pecharsky V K,et al.The room temperature metastable/stable phase relationshipsin the pseudo-binary Gd5Si4-Gd5Ge4 system[J].Journal ofAlloys and Compounds,2002,338(16):126 135.
[6]沈亚涛,郭载兵,都有为.钙钛矿La0.75Ca0.25-xSrxMnO3的磁卡效应与复合材料[J].物理学报,1999,48(11):2137 2141.
[7]陈伟,钟伟.La-Na-Mn-O纳米颗粒的磁卡效应[J].材料研究学报,1999,13(5):552 554.
[8]胡凤霞,沈保根.Heusler合金Ni-Mn-Ga和NaZnl3型化合物La(Fe,Co,M)13,M=Al,Si的巨大磁熵变[J].中国科学院研究生学报,2002,19(2):192 197.
[9]朱根松.机械合金化制备GdSiGeDy合金系室温磁制冷性能研究[D].赣州:江西理工大学,2003.
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|