研究了不同通道间隙下,AZ31镁合金板材在等径角轧制过程中晶体取向的演化特征以及通道间隙对其显微组织和力学性能的影响。X射线衍射分析表明在等径角轧制过程中,随着通道间隙的减小,晶体取向变化加大,(0002)基面取向减弱。等径角轧制后,孪晶明显增多,且随着通道间隙的减小,孪晶数量逐渐增多。单向拉伸试验表明,等径角轧制后的板材,其变形行为和力学性能存在明显的各向异性特征,与等径角轧制前的板材相比,在轧向其屈服强度明显降低由轧制前的240MPa降至155MPa,抗拉强度略有增加,但随着通道间隙的减小,断裂延伸率略有增大;在横向其屈服强度和抗拉强度均增大,随着通道间隙的减小,屈服强度和抗拉强度略有减小,但断裂延伸率增大。
|
|
The evolvement characteristic of crystal orientation of AZ31 magnesium alloy sheet at different channel clearances and effects of channel clearances on its microstructures and mechanical properties during equal channel angular rolling(ECAR) are investigated.By XRD patterns,it is found that the change of crystal orientation increases and(0002) basal plane orientation decreases with channel clearance decreasing during ECAR.After ECAR,twins increase obviously and increase gradually with channel clearance decreasing.By tensile test,it is known that distortion behavior and mechanical properties of the sheet processed by ECAR have obvious anisotropy,and compared with as-received sheet,in rolling direction its yield strength decreases from 240MPa to 155MPa and ultimate tensile strength increases slightly,while the elongation to failure is increased slightly with channel clearance decreasing;but in horizontal direction both its yield strength and ultimate tensile strength increase,and with channel clearance decreasing they decrease slightly but elongation to failure is also increased.
|
|
基金项目：
|
|
国家自然科学基金资助项目(50674043)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈振华,等.镁合金[M].北京:化学工业出版社,2004.
[2]Mukai Toshiji,Yamanoi Masashi,Watanabe Hiroyuki,etal.Ductility enhancement in AZ31 magnesium alloy by control-ling its grain structure[J].Scripta Materialia,2001,45:89 94.
[3]姜巨幅,罗守靖.等径角挤压对AZ91D镁合金力学性能的影响[J].热加工工艺,2004,(8):3 5.
[4]刘英,陈维平,张大童,等.不同路径等通道转角挤压镁合金的结构与力学性能[J].华南理工大学学报,2004,32(10):10 14.
[5]Huang Zan Wen,Yoshida Yu,Cisar Lawrence,et al.Micro-structures and tensile properties of wrought magnesium alloysprocessed by ECAE[J].Materials Science Forum,2003,419 422:243 248.
[6]Saito Y,Utsunomiya H,Suzuki H,et al.Improvement inthe r-value of aluminum strip by a continuous shear deforma-tion process[J].Scripta Materialia,2000,42:1139 1144.
[7]Lee Jae-Chul,Seok Hyun-Kwang,Han Jun-Hyun,et al.Controlling the textures of the metal strips via the continuousconfined strip shearing(C2S2)process[J].Materials Re-search Bulletin,2001,36:997.
[8]程永奇,陈振华,夏伟军,等.等径角轧制AZ31镁合金板材组织与性能研究[J].中国有色金属学报,2005,15(9):1369.
[9]Utsunomiya H,Hatsuda K,sakai T,et al.Continuous grainrefinement of aluminum strip by conshearing[J].MaterialsScience and Engineering,2004,A372:199 206.
[10]Han Jun-Hyun,Oh Kyu Hwan,Lee Jae-Chul.Effect of accu-mulative strain on texture evolution in 1050 Al alloys processedby continuous confined strip shearing[J].Materials Scienceand Engineering,2004,A387 389:240 243.
[11]Huang W H,Yu C Y,Kao P W,et al.The effect of strainpath and temperature on the microstructure developed in cop-per processed by ECAE[J].Materials Science and Engineer-ing,2004,A366:221 228.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|