板料渐进成形半球形件的路径研究

英文标题：Research on incremental forming path of hemispherical workpiece

作者：沈黎萍高锦张蒋松贾俐俐

分类号：TG376.9

出版年,卷(期):页码：2010,35(6):40-44

摘要：

基于ANSYS/LS-DYNA平台对半球形件的板料渐进成形过程进行模拟。根据单道次、两道次、三道次以及四道次成形路径的模拟结果，分析了不同道次对壁厚均匀性的影响。另外，通过对自上而下和自下而上两种成形顺序获得的模拟结果对比，研究了成形方式对壁厚均匀性的影响。最后，以壁厚均匀性为原则设计出半球形工件最佳成形路径，并通过实验得以验证。

Based on ANSYS/LS-DYNA platform, the incremental forming process of the hemispherical workpiece was simulated. According to the simulating results of one-stage, two-stages, three-stages and four-stages forming path, the influences of different passes on wall thickness were analyzed. In addition, the simulating results of two forming sequences, top-down and bottom-up were compared to study the influence forming pattern for wall thickness. Thickness uniformity was taken as the principles to design the path of the hemispherical workpiece, and finally the optimal path was given. Experiment was also taken to verify the path.

基金项目：

先进数控技术江苏省高校重点建设实验室开放基金项目（KXJ05017）

参考文献：

［1］邹建华，李庆，莫健华，等.薄板无模分层成形技术[J].新技术新工艺,2001,(7):3435.
［2］Kim T J, Yang D Y. Improvement of formability for the incremental sheet metal forming process[J]. International Journal of Mechanical Sciences, 2000, (42): 12711286.
［3］方漪，戴昆，王仲仁.板料数控增量成形过程的研究[J].塑性工程学报,1999,6(3):4954.
［4］倪向贵，吴恒安，王宇，等.各向异构本构关系在板料成形数值模拟中的应用[J].计算力学学报,2003,20（2）：231234.
［5］孙成智，陈关龙，林忠钦，等.各项异性屈服准则对铝合金板成形预测精度的影响[J].塑性工程学报,2004,11(3):5963.
［6］史艳莉，吴建军.各项异性屈服准则的发展及应用[J].锻压技术,2006,31(1):99103.
［7］张秀娟，刘彦奎，魏延刚，等.各向异性铝合金板材本构关系及其有限元模拟[J].大连交通大学学报,2008,29(6):4447.
［8］汤井伦，江五贵，黎军玩.各向异性屈服准则对铝合金板深冲起皱预测的影响[J].南昌航空工业学院学报,2006,20(4):5963.
［9］蒋松，高锦张，贾俐俐. 金属板料多道次渐进成形过程的数值模拟[J]. 中国设计与先进制造技术,2009,38(5):1720.

服务与反馈：

【文章下载】【加入收藏】