汽车半轴管挤压成形缺陷分析与工艺改进

英文标题：Research on extrusion defects of auto half shaft bushing and technology improvement

作者：贾建波徐岩

单位：北华大学

关键词：汽车半轴管挤压缺陷

分类号：TG316.3

出版年,卷(期):页码：2011,36(1):26-29

摘要：

应用有限元分析软件Deform对半轴管的挤压过程进行有限元模拟，分析了第3次热挤过程中半轴管开裂缺陷产生的原因。以此为基础提出双凸模挤压成形的改进工艺，通过对比破坏系数、速度场分布、等效应力和等效应变等主要参数，阐明双凸模挤压工艺的优越性。利用试验方法验证了有限元模拟结果的正确性。最后对双凸模挤压方法制备出的合格半轴管产品的微观组织进行分析，结果表明双凸模挤压工艺具有实际应用价值。

Extrusion forming process of half shaft bushing was numerically simulated by using finite element analysis software Deform. Cracking causes of half shaft bushing were simulated in the third extrusion process. Based on this, improved technology of extrusion forming with double punches was proposed. Through the comparison of main parameters, including damage, velocity, effective stress and effective strain, the superiority of double-punch extrusion technology was stated. Finally, correctness of finite element simulation results was verified with experimental method. Analyzing the microstructure of good products fabricated by double-punch extrusion, the results show that double-punch extrusion technology is a better technology with practical application value.

基金项目：

全国大学生创新性实验计划项目(091020111)

参考文献：

［1］温志高,李克敏.重型汽车半轴套管热挤压工艺及模具[J].锻压技术,2001,26(4):6-8.
［2］余光中,蒋鹏,胡福荣,等.半轴套管锻造及深孔挤压复合工艺数值模拟[J].锻压技术,2007,32(2):102-104.
［3］温志高.轮毂轴管热挤压新工艺[J].金属压力加工,2002,20(2):40-41.
［4］胡亚民.半轴套管的精锻成形[J].锻压装备与制造技术,2005,40(2):61-64.
［5］温志高,熊运昌,彭晓南.汽车轮毂管复合挤压工艺的研究[J].锻压技术,2005,30(6):4-61.
［6］韩英淳,王学明,唐志强,等.CA1040 轻型车后桥半轴套管正挤与横轧工艺研究[J].中国机械工程,1997,8(4):71-72.
［7］邓玉山,姚晓静.三辊横轧工艺在轻型车后桥半轴套管中的应用[J].吉林工业大学:自然科学学报,2000,30(3):96-98.
［8］王宗华.半轴套管的锤上锻造工艺[J].锻压机械,1999，(3):25- 26.
［9］张力,卢立伟,刘天模,等.AZ31镁合金双向挤压有限元模拟与实验分析[J].材料导报：研究篇,2009,23(5):75-78.
［10］尹云.石油钻杆接头挤压数值模拟及专机结构设计[D].秦皇岛：燕山大学,2008.
［11］陈济瑞,周明,杨强,等.车轮轮辐螺母座孔加工方法[P].中国专利：200810159097，2009-04-22.

服务与反馈：

【文章下载】【加入收藏】