锻压技术

大直径5A02铝合金薄壁管材生产工艺的研究

英文标题：Research on production process of 5A02 aluminum alloy pipe with large diameter and thin-wall

作者：胡捷郭青苗李德富郭胜利彭海健杜鹏

单位：北京有色金属研究总院

分类号：TG335.71

出版年,卷(期):页码：2011,36(1):65-68

摘要：

采用LD60三辊精密管材轧机对5A02铝合金管坯进行了轧制，利用光学显微镜、硬度计和万能试验机分析了冷加工率、中间退火温度及保温时间对5A02 铝合金薄壁管材组织及性能的影响。确定了5A02铝合金薄壁管材在轧制中选择57.2%作为第一道次加工率，在380~410 ℃时退火保温30~60 min后组织性能较好;轧制后的成品管材在410℃保温60 min后,管材中的纤维状组织完全消失，且再结晶组织较细小，力学性能满足了使用要求。

The 5A02 aluminum alloy thin-wall pipe was rolled using a three-roller precision tube mill. Optical microscope, hardness testing machine and universal testing machine were used to investigate the microstructure and properties of the 5A02 aluminum alloy pipe rolled with different processing rates and annealing with different temperatures and holding time. The 5A02 aluminum alloy was firstly rolled with a strain of 57.2%, then it was annealed at 380-410 ℃ for 30-60 min, which was finally determined as the reasonable rolling process. After rolling process, the finished pipe was annealed at 410 ℃ for 60 min. The microstructure of the pipe is composed of fine recrystallized grains with all fibrous structure completely disappeared, the mechanical properties of which is satisfied with the application requirements.

基金项目：

参考文献：

［1］韩秀坤, 王铭霁. 大直径铝合金薄壁管材工艺研究[J]. 轻合金加工技术, 1994, 22(9):19-25.
［2］刘静, 杨合, 詹梅, 等. 铝合金管力学性能的拉伸试验研究[J]. 锻压技术, 2010, 35(2):113-116.
［3］田荣璋、王祝堂.铝合金及其加工手册[M].2版.长沙: 中南大学出版社, 2000.
［4］徐贺年, 雷正平. 5083-O 铝合金管材生产工艺研究[J]. 轻合金加工技术, 2008, 36(3):37-38.
［5］付忠国, 姚洪强, 赵海龙, 等. 5086H34铝合金薄壁管材生产工艺的研究[J]. 有色设备, 2007, (3): 34-36.
［6］邓小民. 5056合金薄壁管冷加工工艺研究[J]. 有色金属加工, 2006, 35(1): 34-36.
［7］秦丽艳, 刘丽英, 赵海龙. 5A02合金薄壁管材粗晶原因分析[J]. 黑龙江冶金, 2007, (3): 1-2.
［8］王进宇. 6082铝合金筒形件冷强旋组织和织构演变及性能研究[D].哈尔滨: 哈尔滨工业大学工学, 2007
［9］吴永玉. 5A06铝合金晶粒细化及其薄壁管材的成形工艺研究[D]. 长沙: 中南大学, 2004.
［10］张小刚,潘清林,梁文杰,等. 01570 铝合金热压缩变形的流变应力本构方程[J]. 锻压技术, 2009, 34(1):139-142.
［11］刘黎明, 陶华, 肖于德. Al-Mg系铝合金超塑性薄壁管材[J]. 中南大学学报, 2007, 38(4): 608-611.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】