等温模锻对AZ91D镁合金组织和性能的影响

英文标题：Effects of isothermal forging on microstructures and mechanical properties of AZ91D magnesium alloy

作者：于俊才

分类号：TG146.2

出版年,卷(期):页码：2011,36(1):144-146

摘要：

采用金相分析、拉伸试验、SEM分析等方法测试和分析了AZ91D镁合金在铸态、锻压态及锻后+人工时效处理态下的金相显微组织和力学性能。研究表明：锻前均匀化退火能使沿晶界分布的网状β-Mg17Al12相全部溶入基体α-Mg中；等温模锻成形过程中，合金发生了明显的动态再结晶，形成细小的再结晶等轴晶粒组织，合金力学性能相对铸态有大幅提升；锻后人工时效，合金中重新弥散析出β-Mg17Al12相，合金强度提升，而塑性有所下降。3种状态下合金断口形貌均呈现出混合断裂的特征。

The microstructure analysis, tensile test and SEM analysis were used to investigate the microstructure and properties variation of AZ91D alloy in under cast, forged and artificial aging states. The results show that the net β-Mg17Al12 distributed along the grain boundary is almost dissolved during homogenization before forging. The mechanical properties are remarkably improved after isothermal forging with the refinement of the grain size due to the DRX occurs. After artificial aging treatment, with the dispersed precipitation of β-Mg17Al12 phase, the ultimate tensile strength is improved but with a slight decrease of elongation. The fracture morphology of the alloy in different states is all characterized by mixed fracture.

基金项目：

参考文献：

［1］曾小勤，王渠东，吕宜振. 镁合金应用新进展[J]. 铸造，1998，（11）：39-42.
［2］陈振华. 变形镁合金[M]. 北京：化学工业出版社，2005.
［3］王渠东，丁文江. 镁合金研究开发现状与展望[J]. 世界有色金属，2004，（7）：8-11.
［4］余琨，黎文献.变形镁合金的研究、开发及应用[J]. 中国有色金属学报，2003，（2）：277-288.
［5］马哈图K H.材料科学与技术丛书(8)：非铁合金的结构与性能[M].丁道云, 蒋次雪, 李松瑞,等,译.北京：科学出版社，1999.
［6］薛勇，张治民，郎利辉，等. AZ91D镁合金高温压缩变形行为[J]. 锻压技术，2009，34（1）：135-153.
［7］张康，张奎，李兴刚，等. AZ80镁合金热变形行为研究[J]. 特种铸造及有色合金，2009（5）：480-483.
［8］梁海成，崔建忠. AZ80镁合金高温热变形流变应力研究[J]. 锻压技术，2009，34(2)：113-116.
［9］郭强，严红革，陈振华,等. AZ31镁合金高温热压缩变形特性[J]. 中国有色金属学报，2005，15（6）：900-906.
［10］吴立鸿，王利国，关绍康. 镁合金热变形抗力模型的构建技术[J]. 锻压技术，2007，32（4）：7-11.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】