GH4413合金高温压缩变形行为与叶片模锻

英文标题：High temperature compressing deformation of GH4413 alloy and blade die forging

作者：李岩袁超郭建亭

分类号：TG316

出版年,卷(期):页码：2011,36(2):10-14

摘要：

在Gleeble 3800热模拟试验机上，在接近叶片模锻变形速率条件下，系统分析了GH4413合金的高温压缩变形行为，建立了合金热塑性图和热加工再结晶图，获得的最佳热加工工艺成功应用于大尺寸叶片的模锻生产。叶片解剖分析表明，叶片组织均匀、致密，晶粒细小，无明显冶金缺陷和热加工缺陷，性能完全满足技术条件要求。

The compressing deformation behaviors of a superalloy GH4413 at high temperature and high strain rate, which was close to the die forging process of the blade, were investigated systemically on a Glleeble-3800 simulator. The hot ductility and processing recrystallization maps were developed to result in the hot working schedules, which had been successfully applied for the practical process of the blades with the largest size in China. Anatomical examination shows that the whole blade has well-distributed structure with the fine grains, but no obvious metallurgical and processing defects, and favorable mechanical properties.

基金项目：

参考文献：

［1］钟杰，胡楚江，郭成. 叶片精密锻造技术的发展现状及其展望[J]. 锻压技术, 2008，33（1）：1-5.
［2］李柏茹，张鹤，陈洪玉. 2618铝合金等温成形工艺热模拟试验研究[J]. 锻压技术，2008，33（5）：20-22.
［3］薛勇，张治民，郎利辉，等. AZ91D镁合金高温压缩变形行为[J]. 锻压技术，2009，34（1）：135-138.
［4］罗晋平，钟约先，马庆贤，等. 镜板材料25CrMo4高温力学模拟试验及分析[J]. 锻压技术，2010，35（1）：117-120.
［5］余兴强，鲁世强，李鑫，等. 基于加工图技术的铸态TB6钛合金锻造工艺优化[J]. 锻压技术，2010，35（3）：11-14.
［6］郭建亭. 高温合金材料学(中册)：制备工艺[M]. 北京: 科学出版社, 2008.
［7］邹敦叙,陈振兰,龚风阶. GH826合金的热加工工艺塑性[J]. 物理测试, 1987, (2): 15-17.
［8］程晓茹,李虎兴,葛懋琦,等. 管线钢X65高温变形动态再结晶研究[J]. 金属学报, 1997, 33(12): 1275-1281.
［9］梁皖伦,方金风,曹军. 热模拟试验在金属热变形研究中的应用[J]. 理化检验：物理分册, 2001, 37(11): 470-473.
［10］鞠泉,李殿国,刘国权. 15Cr25NiFe基合金高温塑性变形行为的加工图[J]. 金属学报, 2006, 42(2): 218-224.
［11］龚羽,郑芳,焦四海. 热模拟圆柱形压缩试样上金相观测点的选取[J]. 理化检验：物理分册, 2004, 40(6): 282-285.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】