超高强铝合金7A04高温流变行为的研究

英文标题：Study on flow deformation behavior of high strength aluminum alloy 7A04 at elevated temperature

作者：郭小艳肖艳红兰辉刘汉雄郭成

分类号：TG376.2

出版年,卷(期):页码：2011,36(4):138-142

摘要：

通过在Gleeble 1500热模拟实验机上对7A04铝合金进行高温压缩实验，研究了该合金变形温度在300～450℃，应变速率在0.01～10 s-1范围内的高温流变变形行为。结果表明:流变应力随变形温度的升高而降低，随着应变速率的增加而升高。建立了一个综合考虑应变、温度、应变速率三者影响的流变应力方程，预测值与拟合实验值非常接近，结果表明：该流变应力方程用来预测7A04铝合金材料一般加载情况下的热成形过程是比较可靠的。

The elevated temperature flow deformation behavior of 7A04 aluminum alloys was studied by thernal compression test at the temperature of 300500 ℃ and at strain rate of 0.0110s-1 with Gleeble 1500 thermal simulator．The results show that the flow stress increases with the increase of strain rate and decreases with the increase of deformation temperature．A flow stress equation incorporating the effects of temperature, strain rate and strain was proposed. Comparisons between the experimental and predicted results were satisfactory，which confirms that the flow stress equations can be used in computer code to model the hot forming process of 7A04 aluminum alloy part under the prevailing loading conditions.

基金项目：

参考文献：

[1] 刘静安.变形铝合金可挤压性的分析与评价[J].轻合金加工技术,2003, 31(10):24-26.

[2] Lin Shun yan, Lin Jun, Tian Shi. Development and trends of new aluminum alloy materials[J]. Aluminium Fabrication, 2007,1:29-34.

[3] Li Huizhong,Zhang Xinming,Chen Ming an,et al.Hot deformation behavior of 2519 aluminum alloy [J].Chinese Journal of Nonferrous Metals,2005,15(4):621-625.

[4] 蔡一鸣，李慧中，梁霄鹏，等.7039铝合金的热压缩变形本构方程[J].机械工程材料，2009，33(7):48-51.

[5] 李俊鹏，沈健，许小静，等.7050高强铝合金高温塑性变形的流变应力研究[J].稀有金属，2009，33(3):319-322.

[6] 宁爱林，曾苏民.7A04铝合金快速热处理工艺研究[J].轻金属，2004，(6) ：51-54.

[7] 王志云.提高7A04超硬铝合金塑性和韧性的热处理工艺[J].材料热处理技术，2009，(8):136-140.

[8] 甘卫平，王义仁，陈铁平，等.6013铝合金热变形行为研究[J].材料导报，2006，20(5) ：111-113.

[9] Ning Ai lin,LiuZhi yi. Effect of large cold deformation after solution treatment on precipitation characteristic and deformation strengthening of 2024 and7A04 aluminum alloys[J]. Trans. Nonferrous Met. Soc. China,2006，(16)：1341-1347.

[10] Lin Y C,YuChiXia.Constitutive descriptions for hot compressed 2124-T851 aluminum alloy over a wide range of temperature and strain rate[J].Computational Materials Science, 2010，50：227-233.

[11] 刘杰，李落星，李光耀.AZ61镁合金高温变形应力修正及本构方程的建立[J].热加工工艺，2007，36（17）:1-4.

服务与反馈：

【文章下载】【加入收藏】