刚模热胀形TC1半球零件试验与数值模拟研究

英文标题：Experimental research and numerical simulation of hot bulging tests for TC1 hemisphere part

作者：肖军杰李东升李小强金朝海黎俊麟

单位：北京航空航天大学

分类号：TG386

出版年,卷(期):页码：2011,36(6):11-14

摘要：

为研究室温难成形TC1钛板的高温成形能力，对TC1钛板半球零件在700℃进行了刚模胀形试验。研究了在TC1表面涂敷不同种类、不同浓度涂料、保持高温环境下钛板表面的抗氧化能力，确定了热胀形试验的工艺条件和参数；采用Dynaform软件，基于TC1高温单拉试验的真实应力应变曲线和高温性能参数，选用36*MAT3_PARAMETER_BARLAT模型对TC1半球零件进行了刚模热胀形过程数值模拟。最后，对热胀形TC1半球零件的试验结果和模拟结果从厚度减薄率和主次应变两方面进行比较，发现两者基本吻合，验证了所选模型对钛板高温成形模拟的有效性和准确性。

The rigid die bulging experiment for TC1 sheet was carried out at 700℃ to investigate the forming ability of TC1 at elevated temperature. The resistance to oxidation of the titanium sheet was studied at the different kinds and consistency dopes coating in different heating times. The process conditions and parameters of the rigid die hot bulging of the titanium sheet were determined. Using 36*MAT3_PARAMETER_BARLAT model, the rigid die hot bulging TC1 sheet hemisphere part was simulated by DYNAFORM utilizing the true stress-strain curve and the property parameters which came from the uniaxial tensile test at 700℃. Finally, the experimental results were compared with the simulated results in two aspects: the thinning rate and the strains. The comparison shows that they are basically agreed with each other. This verifies the validity and accuracy of the simulation of the high temperature forming for titanium sheet with the chosen material model.

基金项目：

航空科学基金资助项目（2010ZE51050）；中国博士后科学基金特别资助项目（201003038）；中央高校基本科研业务费专项资金资助项目（YWF-10-01-B08）;国家自然科学基金资助项目(51175022)

参考文献：

[1]韩明臣，黄淑梅. 钛在美国军工中的应用[J]. 钛工业进展，2001，(2)：28-32.

[2]瓦利金 N莫依谢耶夫. 钛合金在俄罗斯飞机及航空航天上的应用[M]. 北京:航空工业出版社，2008.

[3]张喜燕，赵永庆，白晨光. 钛合金及应用[M]. 北京：化学工业出版社，2005.

[4]Yin S, Luo Y, Cao Z, et al. Research on the effect of entry angle and pressure-pad force on deep-draw thermo-rheological forming of a TC1 Ti-alloy sheet[J]. Key Engineering Materials,2007,(353358):635-638.

[5]Luo Y, Liu F, Yang L, et al. The numerical simulation and mechanics analysis for deep-draw thermo- Rheological forming of one Ti alloy rectification internal hood[J]. Key Engineering Materials,2004, 274276(1): 721-726.

[6]Erdin M E, Aykul H, Tunalioglu M S. Forming of high strength / low formability metal sheets at elevated temperatures[J]. Mathematical and Computational Applications,2005, 10(3): 331-340.

[7]Galkin V V, Belkin A S, Kartashev A A. Evaluation of plasticity resource of thin-sheet OT4-1 titanium alloy while hot forming[J]. Kuznechno-Shtampovochnoe Proizvodstvo (Obrabotka Metallov Davleniem),2001,(12): 12-16.

[8]Odenberger E, Pederson R, Oldenburg M. Thermo-mechanical material response and hot sheet metal forming of Ti-6242[J]. Materials Science and Engineering: A,2008, 489(12): 158-168.

[9]Odenberger E. Concepts for Hot Sheet Metal Forming of Titanium Alloys[D]. Lula。: Lulea。 University of Technology, 2009.

[10]杨伟俊，李东升，李小强.等. 复杂形状钛合金热成形零件工艺仿真及参数优化研究[J]. 塑性工程学报，2009，16(1)：42-46.

[11]周全. 汽车超高强度硼钢板热成形工艺研究[D]. 上海：同济大学，2007.

[12]苏海波，蒋浩民，陈新平. 管材弯曲有限元仿真分析及试验研究[J]. 锻压技术，2009，34(6)：133-136.

[13]宗影影. 钛合金置氢增塑机理及其高温变形规律研究[D]. 哈尔滨：哈尔滨工业大学，2007.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】