锻压技术

镀锌板冲压成形性的模拟与实验研究

英文标题：Simulation and experimental research of galvanized sheet stamping formability

作者：张笑笑王雷刚黄瑶

单位：江苏大学

分类号：TG386

出版年,卷(期):页码：2011,36(6):19-23

摘要：

镀锌板冲压成形时，常常由于镀锌层失效而使成形性下降。本文采用杯突实验和有限元分析相结合的方法，将镀层和基板看作两种材料，运用固连失效接触模型将镀锌板的基板和镀层连接，建立一系列镀锌板的冲压成形极限图。研究结果表明：由于镀锌层本身材料较软以及摩擦导致镀锌层的粉化、剥落，镀锌板的成形极限小于裸板5%~10%左右。研究结果为镀锌板冲压工艺设计提供了理论指导。

When galvanized sheet is formed, its forming performance usually decreases for galvanized coating failure. Using the combined method of cupping test with finite element analysis, the galvanized coating and base sheet were considered as two kinds of materials and put galvanized coating and base sheet in connection with automatic-surface-to-surface-tiebreak，and a series of the forming limitation diagrams of galvanized sheet were set up. The result of research states that the limitation of galvanized sheet compared with bared sheet is less than about 5%10% because the material of galvanized coating is soft and crushed and dropped off resulted from the friction. The result provides theory guidance for the design of process about galvanized sheet.

基金项目：

参考文献：

[1]董志洪.我国镀锌板生产现状与未来发展趋势[J].中国金属通报，2009，(20)：13-15.

[2]邱晓刚，唐静，王飞龙.锌层对热镀锌钢板成形性的影响[J].理化检验：物理分册，2009，(45)：9-12.

[3]MichalG M, Paik D J. The Effect of Forming Velocity and Stain Path on the Performance of Galvannealed SheetSteels[A]. Galvatech′01 Conference Proceedings[C]. Galvatech,2001.

[4]王辉，高霖.凸模直径以及试件形状对成形极限图的影响[J].机械科学与技术，2006，11(25)：1291-1293.

[5]张建卿，谢桂兰，安小军.ANSYS/LS-DYNA在热镀锌板拉深成形中的运用[J].现代制造工程，2009，(6)：51-60.

[6]张小兵.带镀层薄板的成形有限元模拟方法[J].机床与液压,2008，11(36)：163-166.

[7]杨骏，王雷刚，黄瑶.基于界面结合镀锌板不同摩擦系数拉深的数值模拟[J].模具技术，2010，(5)：1-5.

[8]GB/T15825.115825.81995, 金属薄板成形性能与实验方法[S].

[9]安小军.镀锌板的界面特性和成形性能的数值模拟分析[D].湖南：湘潭大学，2007.

[10]陈思琪.镀锌板冲压成形的摩擦与成形特性研究[D].镇江：江苏大学，2011.

[11]蒋浩民，陈新平，俞宁峰.镀锌钢板的锌层附着特性及成形性研究[J].塑性工程学报，2008，15(2)：58-60.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】