锻压技术

基于三辊楔横轧成形的合理不均匀温度场应用研究

英文标题：Application study on practical optimal non-uniform temperature field based on

作者：仇平谢红飙王健吕知清肖宏

单位：燕山大学

分类号：TG316.1

出版年,卷(期):页码：2011,36(6):42-46

摘要：

借鉴锻压领域的中心压实法，研究采用不均匀温度场方法改善楔横轧件芯部质量。为获取最佳改善楔横轧件心部质量的合理不均匀温度场，本文利用有限元技术，研究了相关热力学参数对不均匀温度场的影响规律，并结合冷却实验，得到合理不均匀温度场温度梯度曲线。通过力学分析和楔横轧实验验证，研究了获取合理不均匀温度场实际工作方法。

With reference to the center-pressure method used often in the forging, the quality of rolled pieces internal part can be improved during three-roll cross wedge rolling by non-uniform temperature field. For gaining optimal non-uniform temperature field which improves the quality of rolled pieces internal part as much as possible, the influence of relevant thermodynamics parameters on non-uniform temperature field was studied by FEM. Combined with water-cooled experimental, the internal temperature gradient of rolled pieces on optimal non-uniform temperature field were ascertained. The method of practical optimal non-uniform temperature field was checked by mechanical analysis and three-roll cross wedge rolling experiment, and it may apply to the practical work.

基金项目：

河北省高等学校科学研究计划资助项目(2010287)

参考文献：

[1]Qiang Li, Lovell Michael R, Slaughter William,et al.Investigation of the morphology of internal defects in cross wedge rolling[J]. Journal of Materials Processing Technology, 2002, (125-126): 248-257.

[2]曹鸿德. 塑性变形力学基础与轧制原理[M].北京：机械工业出版社, 1981.

[3]杨翠苹, 张康生, 刘晋平, 等. 三辊楔横轧应力应变场对内部缺陷的影响[J]. 北京科技大学学报, 2006, 28(5): 464-467.

[4]曹芳, 杨翠苹, 张康生, 等. 交变次数对楔横轧心部疏松的影响[J]. 锻压技术, 2005,30(4):38-41.

[5]仇平, 王健, 肖宏. 不均匀温度场对改善三辊楔横轧轧件心部质量的研究[J]. 中国机械工程,2011,22(13):1550-1554.

[6]关野万吉,鹿野昭一. 大型锻钢件の温间锻造[J].塑性と加工, 1966, 55 (7): 299-394.

[7]宋玉泉. 连续局部塑性成形的发展前景[J].中国机械工程2000,11(12): 65-67.

[8]邓陟, 曹起骧. 温度分布状态对锻件锻造变形的影响[J]. 北京科技大学学报, 1991, 13(3): 245-251.

[9]廖培根, 方刚, 雷丽萍, 等. 大锻件中心压实法锻造过程有限元分析[J]. 锻压技术, 2007, 32(6): 43-46.

[10]惠卫军, 田鹏, 董瀚, 等. 形变温度对中碳钢组织转变的影响[J]. 金属学报, 2005, 41(6): 611-616.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】