钢挤压工模具材质选择、热处理硬度及使用规范

英文标题：Material selection, hardness after heat treatment and use specification of steel extrusion toolings

作者：包进平赵云路薛荣敬

分类号：TG76

出版年,卷(期):页码：2012,37(6):72-76

摘要：

由于传统热作模具钢的高温强韧性不能满足钢挤压工模具的要求以及综合成本较高等原因，提出了适合用于钢挤压工模具的热作模具钢材质1.2367，并将其与传统热作模具钢进行对比；对各种钢挤压工模具材质选择、适宜的热处理硬度及使用规范进行了较为详细的叙述；对频繁水冷容易造成模具钢热疲劳的问题，提出了利用多件工模具循环使用并采取自然冷却的方法代替水冷的观点。

For the high temperature strength and toughness of the traditional hot working die steel materials can not meet the requirement of the steel extrusion toolings, and their comprehensive costs are high, so the hot working die steel material 1.2367 suiting for steel extrusion toolings was proposed. And the differences between them and the traditional hot working die steel materials were compared. The material selection, suitable hardness after heat treatment and use specification of each steel extrusion toolings were described in detail. The frequently water cooling usually resulted in the die steel thermal fatigue, so the viewpoint of water cooling replaced by several toolings cycle use and natural cooling was proposed.

基金项目：

参考文献：

［1］孙舒明，李静.热作模具钢发展现状综述[J].科技致富向导，2011，（20），99.
［2］中国模具工业协会经营管理委员会.“十二五”模具行业信息化规划建议[J].模具工业，2011，37（3）：1-6，10.
［3］薛荣敬，赵云路.挤压工模具材料及其热处理与表面处理现状[J].轻合金加工技术，2002，30（4）：32-37.
［4］刘静安. 铝合金挤压工模具技术的发展概况与趋势[J]. 铝加工， 2010, 192（1）：16-23.
［5］赵云路. 固定挤压垫片的设计及主要结构形式[J]. 锻压技术， 1998, 23（5）：51-54，60.
［6］刘静安，邵莲芬. 铝合金挤压模具的修正技术[J]. 铝加工， 2010, 193（2）：17-24.
［7］王健，丁培道，黄光杰，等. 镁合金用挤压模具清模技术的初步研究[J]. 材料导报，2007, 21（5A）：400-401.
［8］Donati L, Tomesani L. The effect of die design on the production and seam weld quality of extruded aluminium profiles[J]. Mater. Process. Technol.， 2005, 164/165（AMPT/AmmE05 Part 2）: 1025-1031.
［9］Flitta I, Sheppard T. Simulation of bridge die extrusion using the finite element method [J]. Mater. Sci. Technol.，2002, 18: 987-994.
［10］Asher D M. Extrusion Die and Method for Extruding Aluminium: U.S., Patent, No. 5095734 [P]. 1992.
［11］Nick M, Guy E, Alan M. Bearing lengths for extrusion dies: rationale, current practice and requirements for automation[J]. Journal of Materials Processing Technology,1997, 72: 162-176.
［12］Arif A F M, Sheikh A K, Qamar S Z. A study of die failure mechanisms in aluminum extrusion[J]. Journal of Materials Processing Technology,2003, 134: 318-328.
［13］陈英伟，吴晓春. 热作模具钢1.2367的性能研究[J]. 上海金属， 2009, 31（6）：1-5.
［14］赵云路. 中国模具设计大典：第15篇——铝型材挤压模设计[M]. 江西：江西科学技术出版社，2003.
［15］包进平. 大吨位卧式双动正向钢挤压机设备及工艺优化[J]. 锻压技术， 2012, 37（4）：78-82.
［16］杨建华，邱建林，张通和. 模具钢的离子束表面处理[J]. 热加工工艺，1995, (5)：27-29.
［17］阳喜，李军. 模具钢激光表面改性技术的研究进展[J]. 模具工业，2007, 33（9）：65-68,72.
［18］张晓艳，王云红，徐显贲. 气体氮化在4Cr5MoSiV1钢压铸模具上的应用[J]. 机械工人：热加工， 2002, （7）：15-16.
［19］闵永安，许珞萍. 表面处理对热作模具钢使用性能的影响[J]. 国外金属热处理，2002, 23（2）：13-18.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】