激光表面熔覆技术提高斯太尔曲轴模具寿命的研究

英文标题：Research on service life improvement of Style crank die using laser cladding cermet technology

作者：李德超陈海鹏韩海河杨岚董俊慧

分类号：TG315.2

出版年,卷(期):页码：2012,37(6):77-80

摘要：

为了提高斯太尔曲轴模具的使用寿命，在斯太尔曲轴模具材料5CrMnMo钢的堆焊层表面进行了激光合金化处理实验。通过工艺实验，分析了堆焊层激光合金化处理后的组织和显微硬度；通过优化工艺参数，获得了表面光洁、与基材形成良好冶金结合的模具表面强化层；合金强化层平均硬度达到HV0.2750。激光表面熔覆技术已应用于热锻模具，使斯太尔曲轴模具寿命提高了60%。

Laser alloying treatment test was carried out on Style crank die material 5CrMnMo steel surface in order to improve its service life. Both microstructure and distribution of micro hardness of the material were investigated after laser alloying. Crack free and shaped alloying layer which was metallurgically boned with substrate was fabricated through processing parameter optimization. The experimental results show that laser alloying with the allying material as coat improves the original microstructure evidently, the average hardness is proved to be HV0.2750, and the service life of Style crank die is significantly increased by 60%.

基金项目：

参考文献：

［1］卢吉连. 我国模具钢应用技术现状与发展[J]. 模具技术，2000，(6)：90-92.
［2］张志文.锻造工艺学[M].北京：机械工业出版社, 1984.
［3］谢秀红，韩云. 模具堆焊技术的应用[J]. 机械制造与研究，2007，36（5）：76-77.
［4］郑晓庆，杨义忠，马明星，等. 切边模堆焊层表面激光合金化组织及应用的研究[J]. 应用激光,2010，30(06)：438-441.
［5］张国顺. 现代激光制造技术[M]. 北京：化学工业出版社，2006.
［6］李正阳，钟敏霖，张红军，等. 激光点状合金化对42CrMo 钢疲劳裂纹扩展速率的影响[J]. 应用激光，2007，(27)：1-4.
［7］熊绪刚，刘文今，张红军，等. 球墨铸铁活塞环激光合金化及其摩擦磨损特性的研究[J].金属热处理，2000，(7)：5-7.
［8］刘文今，赵海云，钟敏霖，等. 高耐磨激光陶瓷合金化活塞环[A]. 国家“八五”科技攻关“高性能陶瓷及其应用”成果论文集[C]. 北京：人民交通出版社，1998.
［9］杨义忠. 5CrMnMo钢及其堆焊材料激光强化层高温性能的研究[D]. 北京：清华大学，2011.
［10］郑晓庆. 5CrMnMo 切边模及其堆焊层表面激光强化[D]. 北京：清华大学，2010.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】