粉末冶金工艺对4A11铝合金致密度的影响

英文标题：Influence of powder metallurgy process on density of 4A11 aluminum alloy

作者：杨永顺冯科郭俊卿尹甜甜

单位：河南科技大学

关键词：粉末冶金 4A11铝合金致密度挤压烧结

分类号：TG376

出版年,卷(期):页码：2012,37(6):104-107

摘要：

采用粉末冶金法制备4A11铝合金，分析了压制力、烧结工艺以及挤压工艺对铝合金致密度的影响。研究表明：在一定压力范围内，铝合金的致密度随着压制力的增加而增加，当压制力到达一定值后，致密度趋于稳定。常规烧结过程不能使铝合金致密化，反而会使材料致密度有所下降。挤压使材料发生塑性变形，填补了材料中的孔洞，同时金属的流动划破了颗粒表面的氧化层，促进物质的扩散迁移，能够大幅度提高铝合金的致密度，其致密度最高达到97.8%。

4A11 aluminum alloy was prepared using powdermetallurgy method. The influences of forming pressure, sintering process and extruding on the density of aluminum alloy was analyzed. The research shows that the density of aluminum alloy is improved with the increase of pressing force in the certain pressure range, and the density tends to be stable when the pressing force arrives to a certain value. Conventional sintering process cant make aluminum alloy densification, on the contrary，which would lead to drop of the density. Plastic deformation occurred by squeezing, the holes in the material would be filled and at the same time, the oxide in the surface was destroyed by metal flow, which promoted diffusion and transference of material. By this way，the density of aluminum alloy was greatly improved, and the highest density was 97.8%.

基金项目：

河南省教育厅自然科学基金资助项目（2011B590001）

参考文献：

［1］刘改华,查五生.粉末冶金法制备铝合金块体材料的研究[J].轻金属,2007,(3):56-57.
［2］张春芝,边秀芳.粉末冶金铝合金的研究现状和发展趋势[J].特色铸造及有色合金,2008,1(17):56-58.
［3］黄培云.粉末冶金原理[M].北京：冶金工业出版社,1997.
［4］潘复生,张津,张喜燕.轻合金材料新技术[M].北京:化学工业出版社,2008.
［5］刘静安,谢水生.铝合金材料的应用与技术开发[M].北京：冶金工业出版社，2003.
［6］武涛，柴东朗，宋余九，等.粉末冶金制备颗粒增强5052铝基复合材料的压力加工工艺研究[J].热加工工艺，2005,(6)：65-67.
［7］李倩.几种镍基合金的高温抗氧化和耐腐蚀性能研究[D].长沙：中南大学，2009.
［8］杨林.纳米钨铜复合材料的制备及其合成机理的探讨[D].成都：西华大学，2006.
［9］程羽，郭生武，郭成,等.热挤压对颗粒增强金属基复合材料组织和性能的影响[J].兵器材料科学与工程，2000，2(23)：31-34.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】