Weldox 960钢V形弯曲成形工艺实验研究

英文标题：Study on Vshaped bending forming of Weldox 960 steel

作者：吴薇薇林高用贺家健张宗鹏张锐

关键词：Weldox 960钢 V形弯曲成形工艺优化

分类号：TG386.3+1

出版年,卷(期):页码：2012,37(6):126-130

摘要：

通过100 t单柱油压机对厚度为6 mm的Weldox 960钢板材进行V型弯曲成形实验，并采用增加软金属缓冲垫板的方法对弯曲成形工艺进行优化，分析并对比优化前后Weldox 960钢在不同凸模半径下弯曲回弹、开裂、以及变形量特点。实验表明，对于厚度为6 mm的Weldox 960钢板材,当凸模半径增大到15~25mm以上或在下模处增加较软金属垫板，均可有效减少弯曲成形时的纵向裂纹。

The research was done for bending properties of 6 mm Weldox 960 steel with 100 t single pillar oil hydraulic press. Optimization for bending technology was finished by setting soft metal cushioning pad. The optimization was compared with old design, and bending springback, crack and deflection were studied in different radius of marking dies. The results indicate that increase of marking die radius to 1525 mm or setting cushioning pad can reduce the longitudinal crack of Weldox 960 steel when bending.

基金项目：

参考文献：

［1］付荣柏.起重机钢结构制造工艺[M]. 北京: 中国铁道出版社, 1991.
［2］Jezernik N, Kramberger J, Lassen T, et al. Numerical modelling of fatigue crack initiation and growth of martensitic steels[J]. Fatigue Fract.Engng.Mater.Struct.,2011,（33）: 714-723.
［3］Tan Yefa,Cai Bin, Long He,et al. Study on tribological behavior and mechanisms of weldox960 steel[J]. Advanced Materials Research, 2012,415417:2191-2195.
［4］吴静然, 刘春哲, 韩雪松，等. Weldox 960低合金超高强精细钢焊接热影响区韧性和组织分析[J]. 金属铸锻焊接技术, 2011,40(11): 170-175.
［5］张家坤, 李家武. Weldox系列板材焊接及工程应用[J]. 建设机械技术与管理, 2006,（10）: 97-98.
［6］寇栋梁. 冷冲压工艺与压型质量[J]. 铁道技术监督, 2001,（4）: 20-22.
［7］王座莹. 中厚板冷压弯曲成形易开裂原因及防止[J]. 机械制造,1994,(1): 7-9.
［8］吴诗醇. 冲压工艺学[M]. 西安: 西北工业大学出版社, 1987.
［9］陆宏, 黄文. 高强度钢板V形弯曲板厚方向压缩对回弹的影响[J].锻压技术,2011,36(4):56-59.
［10］彭大暑.金属塑性加工原理[M].长沙:中南大学出版社，2004.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】