精冲1020板料接触应力变化特点

英文标题：Characteristics of contact stress variation in fine-blanking process of ASTM 1020 steel sheet

作者：丁日显张缓缓朱其超郭成

单位：西安交通大学

分类号：TG386

出版年,卷(期):页码：2012,37(4):40-42

摘要：

采用PVDF压电薄膜应力传感器对精冲ASTM 1020板料过程中板料表面接触应力进行测量。测量结果发现接触应力共出现2次波动：第1次波动是由V形齿的压入引起;第2次是由凸模冲裁板料所导致，出现峰值后单调减小。第2次波动的峰值是第1次的3.0～3.7倍，且是随着第1次波动峰值的增加先减小后增加的二阶多项式。

In fine-blanking process of 1020 steel sheet, the contact stress variation on the sheet surface was measured by the PVDF piezoelectric film stress sensor. Two fluctuations of contact stress were detected. The first one was caused by pressing the V-ring into the sheet. The second was the result of the punch squeezing metal in the shearing zone, and the contact stress peak occurred firstly, then, the contact stress decreased monotonically. Ratio of contact stress peak in the second fluctuation to the first is within 3.0~3.7 times,and is a second-order polynomial which decreases at first and then increases with the increasing of contact stress peak in the first fluctuation.

基金项目：

参考文献：

［1］Schmidt R A, Birzer F, Hofel P, et al. Cold Forming and Fineblanking-a Handbook on Cold Processing, Steel Material Properties and Part, Part Design.(2nd Edition )[M]. Bern: Carl Hanser Verlag Munchen Wien, 2006.
［2］Thipprakmas S, Jin M, Murakawa M, Study on fanged shapes in fneblanked-hole fanging process (FB-hole fanging process) using fnite element method (FEM) [J]. Journal of Materials Processing Technology, 2007, 192193: 128-133.
［3］Thipprakmas S, Jin M, Tomokazu K, et al. Prediction of Fineblanked surface characteristics using the fnite element method (FEM) [J].Journal of materials processing technology, 2008, 198: 391-398.
［4］Gram M D, Wagoner R H .Fineblanking of high strength steels: Control of material properties for tool life [J]. Journal of Materials Processing Technology, 2011, 211: 717-728.
［5］丁日显, 王连学, 陈维, 等. 精密冲裁压边圈上接触压应力变化规律研究[J].锻压技术，2011，36(5): 38-42.
［6］Douglas C Montgomery. Design and Analysis of Experiments.(6th Edition) [M].New Youk: John Wiley & Sons Inc,2007.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】