变压边力下TRIP600高强钢板的成形窗口

英文标题：Formability window of TRIP600 high strength steel sheet at variable blank-holder force

作者：陈淑婉蒋敏詹艳然黄胜

分类号：TG316.3

出版年,卷(期):页码：2013,38(4):124-130

摘要：

为了提高TRIP高强钢板的冲压成形性能，在板料成形基本理论的基础上，通过单向拉伸试验和基于成形极限曲线的Naddrg模型，获得了TRIP600高强钢板的基本力学参数。在分析板料成形失效判据的基础上，提出变压边力成形窗口的建立方法，以圆筒件为例建立了TRIP600高强钢板的成形窗口，通过数值模拟和试验验证了该方法的准确性。结果表明：TRIP600高强钢板同时兼有高强度和高延伸性，但其弹性模量较低；1.2mm厚TRIP600高强钢板的平面应变点FLD0为0.397；成形窗口中的临界起皱变压边力曲线可通过实时调节压边力大小使零件始终处于临界起皱状态而获得；临界破裂变压边力曲线可通过两种极端加载模式获得；该成形窗口的建立能够有效指导TRIP高强钢板的实际冲压生产。

In order to improve the stamping formability of TRIP high strength steel effectively, based on the principal theory of sheet metal forming, the basic mechanical parameters of TRIP600 high strength steel sheet were got via uniaxial tensile test and the Naddrg model of forming limit curve (FLC). And on the basis of the analysis of failure criterion of sheet metal forming, the established method of VBHF forming window was proposed. With the example of a cylindrical part, the VBHF forming window whose accuracy was proved by numerical simulation and experiment was established. The result of the experiment and numerical simulation shows that the TRIP high strength steel material is a new type high strength material with high elongation and low elastic modulus. The plane strain (FLD0) of TRIP600 high strength steel plate with the thickness of 1.2mm is 0.397. The variable blank-holder force curve of critical wrinkless and critical fracture in formability window can be obtained by adjusting the variable blank-holder force (VBHF) to make parts in the critical wrinkling state and two extreme loading modes respectively. And the forming window can guide the practical stamping production of TRIP high strength steel.

基金项目：

福建省自然科学基金资助项目（2008J0153）

陈淑婉（1986-)，女，硕士，助教

参考文献：

［1］马鸣图，Shi M F. 先进的高强度钢及其在汽车工业上的应用[J].钢铁. 2004，39（7）：68-72. Ma M T, Shi M F. Advanced high strength steel and it's applications in automobile industry [J]. Iron and Steel, 2004, 39(7): 68-72.
［2］江海涛，唐荻，米振莉. 汽车用先进高强度钢的开发及应用进展[J].钢铁研究学报.2007，19（8）：1-5. Jiang H T, Tang D, Mi Z L. Latest progress in development and application of advanced high steel for automobiles [J]. Journal of Iron and Steel Research , 2007, 19(8): 1-5.
［3］刘林虎，李淑慧，林忠钦，等. 基于压边力设计的高强度钢板成形方法[J]. 上海交通大学报，2005，39(7)：1085-1088. Liu L H, Li S H, Lin Z Q, et al. The high strength steel formability based on blank-holder force design [J]. Journal of Shanghai Jiaotong University, 2005, 39(7):1085-1088.
［4］Stuart P K. Application and forming of higher strength steel[J]. Journal of Materials Processing Technology, 1994,(46): 443-454.
［5］Doege E, Sommer N, Optimization of blank holder force during the whole punch stroke [J], Steel Stamping, 1983, 103(3): 139-142.
［6］孙成智.基于变压边力的薄板冲压成形理论与实验研究[D].上海：上海交通大学，2004. Sun C Z. Theoretical and Experimental Study on the Processes of Sheet Metal Forming Based on Variable Blank-holder Force [D]. Shanghai:Shanghai Jiao Tong University, 2004.
［7］GB/T 5028-1999金属薄板和薄带拉伸应变硬化指数（n值）试验方法[S]. GB/T 5028-1999 Metallic materials sheet and strip determination of tensile strain hardening exponent (n values) [S].
［8］Levy S B. A comparison of empirical forming limit curves for low carbon steel with theoretical forming limit curves[A]. IDDRG WG3[C]. Ungarn, 1996.
［9］余海燕，陈关龙，李淑慧. TRIP高强度钢板成形极限的实验研究[J]. 中国机械工程. 2004，15(23)：2158-2161. Yu H Y, Chen G L, Li S H. Experimental investigation on forming limit predicting model for TRIP high strength sheet steels [J]. China Mechanical Engineering,2004，15(23)：2158-2161.
［10］Kurt Lange. Hand Book of Metal Forming[M]. New York:Mc Graw-Hill,1985.
［11］米昱. 薄板深拉深时压边力的变化规律及其最优控制的研究[D]. 重庆：重庆大学，2001. Mi Y. Study on the Change Rule and Optimal Control of Blank Holder Force of Thin Plate During Deep Drawing [D]. Chongqing:Chongqing University, 2001.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】