锻压技术

Sn元素含量对汽车用Mg合金组织和性能的影响

英文标题：Effect of Sn content on the structure and property of Mg alloy

作者：麻常选

单位：烟台工程职业技术学院

分类号：TG156.3

出版年,卷(期):页码：2014,39(9):116-118

摘要：

以Mg-4%Zn-5%Al合金为研究对象，研究Sn含量变化对Mg合金物相、显微组织和拉伸性能的影响。采用XRD对样品进行物相的测定，并测试了不同Sn含量的样品的抗拉强度。结果表明，Sn的加入使Mg合金在晶界处生成共晶相，随着Sn含量增加，Mg合金抗拉强度和伸长率先增加后减小。当Sn含量为1.0%时，Mg合金抗拉强度达到最大值226.5 MPa，而未添加Sn时的Mg合金抗拉强度为189.2 MPa，此时Mg合金的伸长率为9.1%；当Sn含量继续增加时，Mg合金的抗拉强度和伸长率将下降。

For the Mg-4%Zn-5%Al alloy, the effects of varying Sn contents on the phase, microstructure and tensile property of the Mg alloy were studied. XRD was used to measure phase of samples and to test tensile strength of samples with different Sn contents. The results show that the addition of Sn forms eutectic at the grain boundary in the Mg alloy. With the increase of Sn contents, tensile strength and elongation of the alloy first increase and then decrease. When Sn content is 1.0%, the tensile strength of Mg alloy reaches the maximum of 226.5 MPa, which is higher than 189.2 MPa when the Mg alloy is without Sn，and the corresponding elongation is 9.1%. Increasing Sn content further, the tensile strength and elongation of Mg alloy will decrease.

基金项目：

2012年度山东省高等学校教学改革项目

麻常选（1968-），男，硕士，副教授

参考文献：

［1］Eliezer D, Ghion E A, Froes F H. Magnesium science technology and applications[J]. Advanced Performance Materials, 1998, (5): 201-212.
［2］王秉刚. 世界汽车工业现状与趋势[J]. 汽车工程，1996，(3)：18-23.Wang B G. Status and trends of automotive world[J]. Automotive Engineering, 1996, (3): 18-23.
［3］陈礼清，赵志江. 从镁合金在汽车及通讯电子领域的应用看其发展趋势[J].世界有色金属，2004，(7)：12-20.Chen L Q, Zhao Z J. From the application of magnesium alloys in the automotive and electronic communications field to see trends[J]. The Worlds Non-ferrous Metals,2004, (7): 12-20.
［4］Yuan G Y, Liu M P, Ding W J, et al. Mechanical properties and microstructure of Mg-Al-Zn-Si base alloy[J]. Material Transactions, 2003, (44): 458-462.
［5］杨润琪，张延杰，邓炬，等. 耐热镁合金的研究现状与发展方向[J].稀有金属材料与工程，2004,33（6）：561-565.Yang R Q, Zhang Y J, Deng J, et al. Research status and development direction of heat-resistant magnesium alloys [J]. Rare Metal Materials and Engineering, 2004, 33 (6): 561-565.
［6］燕战秋. 未来汽车材料和我国新材料研究课题[J]. 汽车工程，1993，(3)：15-18.Yan Z Q. The future of automotive materials and new materials research[J]. Automotive Engineering, 1993, (3): 15-18.
［7］袁广银，刘满平，王渠东，等. Mg-Al-Zn-Si合金的显微组织细化[J]. 金属学报，2002，38（10）：1105-1108.Yuan G Y, Liu M P, Wang Q D, et al. Microstructure refinement of Mg-Al-Zn-Si alloy [J]. Metal Journal,2002，38 (10): 1105-1108.
［8］Choi J C, Kwon H, Park J H, et al. a study on development of a die design system for die casting [J]. The International Journal of Advanced Manufacturing Technology, 2002, (20): 1-8.
［9］GB/T 228.1-2010，金属拉伸试验试样 [S].GB/T 228.1-2010，Metal tensile test specimen[S].

［10］杨群英，阎峰云，任林昌，等. 脉冲电流对铸轧Al-Mg合金组织的影响[J]. 锻压技术，2011，36(1)：136-139.Yang Q Y, Yan F Y, Ren L C, et al. Effects of pulsed current for casting of Al-Mg alloy [J]. Forging & Stamping Technology, 2011, 36(1): 136-139.

服务与反馈：

【文章下载】【加入收藏】