304不锈钢壳级进模变薄拉深工艺及数值模拟

英文标题：Ironing process and numerical simulation of progressive die for

单位：广东工业大学

分类号：

出版年,卷(期):页码：2015,40(1):33-38

摘要：

根据经验公式和理论数据对某304不锈钢壳进行直径减小、壁厚变薄的变薄拉深级进模设计,并运用Deform-3D对连续变薄拉深成形过程进行数值模拟,揭示了成形过程等效应力和行程载荷曲线的分布规律。模拟与试验结果表明：成形过程中，坯料的最大应力集中在与凹模圆角和凹模工作带相接触的区域；随着凸模圆角减小，凸模圆角与直壁连接处应力增大，出现危险区域；为防止最后一道拉深过程中凸模容易磨损及产品被拉伤，应合理设计拉深系数、变薄量及凹模圆角；直径减小壁厚变薄拉深件的直壁壁厚均匀。

According to empirical formula and theoretical data, ironing progressive die with reducing in diameter and thinning in wall thickness for stainless steel 304 shell was designed. The forming process of continuous ironing was numerically simulated by Deform-3D software. The equivalent stress fields and the regulation of load-stroke curves in the ironing process were revealed. The results of simulation and test show that the maximum stress of the blank focuses on the contacting areas of the die radius and the die work location. The hazardous areas will appear with the decrease of punch radius because the contact stress between the vertical wall and punch radius increases. In order to prevent the last drawing punch from wearing, the product strain, drawing coefficient, thinning and die radius should be reasonably designed. The vertical wall thickness of the drawn parts with reducing in diameter and thinning in wall thickness is homogenizing.

基金项目：

广东省战略性新兴产业项目（2012A090100014）

白建雄（1990-），男，硕士研究生

参考文献：

［1］彭成允，胡敬佩. 不锈钢薄板拉深时出现的问题及对策[J]. 重庆工学院学报，2002，（5）：25-26.Peng C Y, Hu J P. The problems appearing in stainless steel sheet when being stretched and the counter measures[J]. Journal of Chongqing Institute of Technology，2002，（5）：25-26.

［2］卢日杨，王雷刚，黄瑶.奥氏体不锈钢变薄拉深过程的数值模拟[J].模具技术，2008，（2）：40-43.Lu R Y, Wang L G, Huang Y. Numerical simulation of the ironing process of austenitic stainless steel[J]. Die and Mould Technology，2008，（2）：40-43.

［3］Gau J T, Teegala S, Huang K M. Using micro deep drawing with ironing stages to form stainless steel 304 micro cups[J]. Journal of Manufacturing Processes，2013，15（2）：298-305.

［4］孙镇和.枪弹药筒制造工艺学[M].北京：国防工业出版社，1977.Sun Z H. Gun Cartridge Manufacturing Technology[M]. Beijing:National Defense Industry Press，1977.

［5］王孝培.冲压手册 [M].2版.北京：机械工业出版社，2000.Wang X P. Stamping Handbook [M]. Second Edition.Beijing: China Machine Press，2000.

［6］李二玲，邓沛然，杨尚磊，等. 薄板拉深过程中压边力与破裂关系的研究[J]. 锻压技术，2014，39（6）：55-59.Li E L，Deng P R，Yang S L，et al. Analysis of blank holder force and fracture during the process of deep drawing for thin sheet [J]. Forging & Stamping Technology，2014，39（6）：55-59.

［7］邓明，李庆.不锈钢成形分析和防止拉深缺陷的对策[J].锻压技术，2006，31（5）：121-124.Deng M, Li Q. Analysis of stainless steel sheet forming and preventive measures for the defects in deep-drawing[J]. Forging & Stamping Technology，2006，31（5）：121-124.

［8］李潍. 圆拉方拉深凹模的结构改进[J]. 锻压技术，2011，36（2）：97-99.Li W. Die structure improvement for drawing cylinder into box [J]. Forging & Stamping Technology，2011，36（2）：55-59.

［9］徐胜利，王波，龚小涛，等.薄壁不锈钢筒形件级进模设计[J].模具工业，2007，33（9）：20-22.Xu S L, Wang B, Gong X T, et al. Development of progressive die for stainless steel thin-shell cylindrical part[J]. Die & Mould Industry，2007，33（9）：20-22.

［10］张莉,李升军. Deform在金属塑性成形中的应用[M].北京：机械工业出版社，2009.Zhang L, Li S J. Deform in the Metal Forming[M]. Beijing: China Machine Press，2009.

［11］余均武，彭大署，林启权，等.不锈钢拉深润滑剂的研制与应用[J].湘潭大学自然科学学报，2004，26（3）：116-119.Yu J W, Peng D S, Lin Q Q, et al. Development of deep drawing lubrication oil of 304 stainless steel[J]. Natural Science Journal of Xiangtan University，2004，26（3）：116-119.

［12］俞汉清，陈金德.金属塑性成形原理[M].北京：机械工业出版社，2011.Yu H Q, Chen J D. Principles of Metal Forming[M]. Beijing：China Machine Press，2011.

服务与反馈：

【文章下载】【加入收藏】