韧性断裂准则及损伤模型在冲裁有限元模拟中的应用研究

英文标题：Research on the application of ductile fracture criteria and damage models in finite element simulation of blanking process

作者：刘倩韩静涛刘靖王晓雄

单位：北京科技大学

关键词：有限元模拟冲裁韧性断裂准则损伤模型

分类号：TG386

出版年,卷(期):页码：2015,40(6):28-33

摘要：

在冲裁有限元模拟中，韧性断裂准则的选择会对冲裁件断面质量与尺寸精度产生很大影响。为了获得符合实际的模拟结果，进而优化冲裁工艺，重点研究了一些常用的韧性断裂判定依据，并从物理学角度阐述了韧性断裂机制。基于试验的韧性断裂准则，考虑了变形历史中的应力应变关系，使用由反求法确定的临界值来判定韧性断裂的发生与否。基于连续损伤力学建立的损伤模型，考虑了变形过程中损伤累积对材料本构关系的影响，能够更准确地描述断裂过程。此外，还分析了冲裁有限元模拟中的关键技术，如采用任意拉格朗日欧拉方法来解决网格畸变问题，使用单元分裂、单元分离与单元删除等技术来处理裂纹的萌发与扩展。探讨了目前韧性断裂模拟中存在问题以及未来发展方向。

In finite element simulation of blanking process, the choice of ductile fracture criterion has a great impact on edge quality and dimensional accuracy of blanking parts. In order to obtain reasonable results and optimize blanking process, some commonly used ductile fracture criteria were mainly studied, and the ductile fracture mechanism was analyzed from the perspective of physics. The stress-strain relationship in deformation history was considered according to the ductile fracture criteria based on experiments and a critical value obtained by an inverse method was used to determine whether ductile fracture occurs or not. The influence of damage accumulation on constitutive equation was considered according to the damage models based on continuum damage mechanics so that they can accurately describe the ductile fracture process. Furthermore, the key techniques in numerical simulation of blanking process were analyzed, including an Arbitrary Lagrangian Eulerian method used to solve mesh distortion as well as methods of element split, element separation and element deletion used to deal with crack generation and propagation. In the end, the current issues and future development in the field of ductile fracture simulation were discussed.

基金项目：

刘倩（1987-），男，博士研究生;通讯作者：韩静涛（1957-），男，博士，教授，博士生导师

参考文献：

［1］Miguel V J, Jose D B. A computational approach to blanking processes[J]. Journal of Materials Processing Technology, 2002, 125-126: 206-212.
［2］Klingenberg W, Singh U P. Finite element simulation of the punching/blanking process using in-process characterization of mild steel [J]. Journal of Materials Processing Technology, 2003, 134(3): 296-302.
［3］Atkins A G. On cropping and related processes[J]. International Journal of Mechanical Sciences, 1980, 22: 215-231.
［4］Zhou Q, Wierzbicki T. A tension model of punching and tearing of ductile metal plates[J]. International Journal of Mechanical Sciences, 1996, 38(3): 303-324.
［5］Marouani H, Rachik M, Hug E. Experimental investigations and FEM simulations of parameters influencing the Fe(wt.3%) Si shearing process[J]. Mechanics and Industry, 2012, 13: 271-278.
［6］Farzin M, Javani H R, Mashayekhi M, et al. Analysis of blanking process using various damage criteria[J]. Journal of Materials Processing Technology, 2006, 177: 287-290.
［7］Soares J A, Gipiela M L, Lajarin S F, et al. Study of the punch-die clearance influence on the sheared edge quality of thick sheets [J]. The International Journal of Advanced Manufacturing Technology, 2013, 65: 451-457.
［8］Hambli R. Comparison between Lemaitre and Gurson damage models in crack growth simulation during blanking process[J]. International Journal of Mechanical Sciences, 2001, 43: 2769-2790.
［9］Klingenberg W, Singh U P. Further observations and review of numerical simulations of sheet metal punching[J]. The International Journal of Advanced Manufacturing Technology, 2006, 30: 638-644.
［10］Li H, Fu M W, Lu J, et al. Ductile fracture: experiments and computations[J]. International Journal of Plasticity, 2011, 27: 147-180.
［11］郭钊，唐文亭，曹立勋. 圆管异形孔冲裁工艺设计及有限元模拟[J]. 锻压技术，2014, 39(8): 140-145,155.Guo Z, Tang W T, Cao L X. Process design and numerical simulation on shaped hole blanking of steel round pipe[J]. Forging & Stamping Technology，2014, 39(8): 140-145,155.
［12］Hambli R, Reszka M. Fracture criteria identification using an inverse technique method and blanking experiment[J]. International Journal of Mechanical Sciences, 2002, 44: 1349-1361.
［13］Goijaerts A M, Govaert L E, Baaijens F P T. Prediction of ductile fracture in metal blanking[J]. Journal of Manufacturing Science and Engineering, 1999, 122(3): 476-483.
［14］Taupin E, Breitling J, Wu W T, et al. Material fracture and burr formation in blanking results of FEM simulations and comparison with experiments[J]. Journal of Materials Processing and Technology, 1996, 59: 68-78.
［15］Abbassi F, Belhadj T, Mistou S, et al. Parameter identification of a mechanical ductile damage using Artificial Neural Networks in sheet metal forming[J]. Materials & Design, 2013,45: 605-615.
［16］Lemaitre J. A continuous damage mechanics model for ductile fracture[J]. Journal of Engineering Materials and Technology, 1985, 107: 83-89.
［17］陈志英，董湘怀. GTN细观损伤模型参数对板料损伤行为的影响[J]. 锻压技术，2012, 37(3): 23-27.Chen Z Y, Dong X H. Influence of GTN meso-damage model parameters on sheet forming damage behavior[J]. Forging & Stamping Technology, 2012, 37(3): 23-27.
［18］方刚，曾攀. 金属板料冲裁过程的有限元模拟[J]. 金属学报，2001, 37(6): 653-657.Fang G, Zeng P. Finite element simulation for blanking process of sheet metal[J]. Acta Metallurgica Sinca, 2001, 37(6): 653-657.
［19］Lee T C, Chan L C, Zheng P F. Application of the finite-element deformation method in the fine blanking process[J]. Journal of Materials Processing Technology, 1997, 63: 744-749.
［20］方刚，雷丽萍，曾攀. 金属塑性成形过程延性断裂的准则及其数值模拟[J]. 机械工程学报，2002, 38（S1）: 21-25.Fang G, Lei L P, Zeng P. Criteria of metal ductile fracture and numerical simulation for metal forming [J]. Chinese Journal of Mechanical Engineering, 2002, 38（S1）: 21-25.
［21］Wu Z G, Li S H, Zhang W G, et al. Ductile fracture simulation of hydropiercing process based on various criteria in 3D modeling[J]. Materials & Design, 2010, 31: 3661-3671.
［22］Goijaerts A M, Govaert L E, Baaijens F P T. Experimental and numerical investigation on the influence of process speed on the blanking process[J]. Transactions of the ASME, 2002, 124: 416-419.
［23］Goijaerts A M, Govaert L E, Baaijens F P T. Evaluation of ductile fracture models for different metals in blanking[J]. Journal of Materials Processing Technology, 2001, 110: 312-323.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】