304不锈钢管热强旋成形试验研究

英文标题：Experimental research on hot power spinning of stainless steel tube 304

作者：杜军夏琴香朱宁远谢红希

单位：华南理工大学

分类号：TG302; TH142.2

出版年,卷(期):页码：2015,40(6):39-42

摘要：

针对304不锈钢常温下加工硬化严重、塑性变形抗力大的特性，对304不锈钢筒形件进行了热强旋成形试验研究以探索304不锈钢的热强旋成形规律。在HGQX-LS立式热强旋旋压机上，以二硫化钼为润滑剂，采用高频电磁感应加热方式进行3道次、总减薄率为60%的旋压成形试验。试验主要分析了成形温度和进给比对成形质量的影响，试验结果表明，热强旋是成形304不锈钢薄壁筒形件行之有效的方法之一，当温度为1000 ℃、进给比为0.4 mm·r-1时能得到成形质量良好的旋压件。

For the performance of the serious work-hardening and large deformation resistance at room temperature of stainless steel tube 304, the experimental research was carried out to explore hot power spinning forming regulation of stainless steel 304. The spinning experiments with three steps and 60% total thinning ratio were carried out by HGQX-LS vertical hot power spinning machine under the molybdenum disulfide lubricant and the high frequency electromagnetic induction heating. The influences of the forming temperature of the tubular blank and the feed rate of the roller on the forming qualities of spun workpiece were analyzed based on the experiment. The results show that hot power spinning is one of the most effective methods in manufacturing stainless steel tubes 304, and the high quality spun workpiece can be obtained under the heating temperature of the tubular blank 1000 ℃ and the feed rate of the roller 0.4 mm·r-1.

基金项目：

国家自然科学基金资助项目(51375172)；高等学校博士学科点专项科研基金资助项目（20130172110024）

杜军（1989-），男，硕士研究生;通讯作者：夏琴香（1964-），女，博士，教授

参考文献：

［1］熊云龙，娄延春，刘新峰. 不锈钢材料研究的新进展[J]. 热加工工艺，2005,（5）：51-53.Xiong Y L,Lou Y C,Liu X F. New process of stainless steel[J]. Hot Working Technology,2005,（5）：51-53.
［2］林高用，韩飞，余均武，等.SUS304-2B不锈钢薄板加工硬化及退火软化的试验研究[J].金属热处理，2004,29（3）:8-11.Lin G Y,Han F,Yu J W,et al. Work-hardening and annealing softening of SUS304-2B austenitic stainless steel[J].Heat Treatment of Metal,2004,29（3）:8-11.
［3］Qinxiang Xia,Gangfeng Xiao,Hui Long,et al. A review of process advancement of novel metal spinning[J]. International Journal of Machine Tools & Manufacture,2014,(85): 100-121.
［4］王成和，刘克璋. 旋压技术[M]. 北京：机械工业出版社，1986.Wang C H,Liu K Z. Spinning Technology[M].Beijing: China Machine Press,1986.
［5］檀雯. 1Cr18Ni9不锈钢筒形件错距旋压研究[D]. 沈阳：沈阳理工大学，2009.Tan W. Research on 1Cr18Ni9 Stainless Steel Tube Stagger Spinning[D]. Shenyang: Shenyang Ligong University,2009.
［6］朱宁远，夏琴香，肖刚锋，等. 难变形金属热强旋成形技术及研究现状[J]. 锻压技术，2014，39（6）：42-47.Zhu N Y，Xia Q X，Xiao G F，et al. Hot power spinning technology and research status of difficult-to-deform metal[J]. Forging & Stamping Technology,2014，39（6）：42-47.
［7］王宾，秦建平，王福利，等. 不锈钢管冷旋压成形试验[J]. 精密成形工程，2011,3（3）：5-9.Wang B,Qin J P,Wang F L. The research of cold spinning forming of stainless steel pipes[J]. Journal of Netshape Forming Engineering,2011,3（3）：5-9.
［8］陈适先，贾文铎,曹庚顺，等. 强力旋压工艺与设备[M]. 北京：国防工业出版社，1986.Chen S X,Jia W D,Cao G S. Power Spinning Technology and Equipment[M]. Beijing: National Defence Industry Press,1986.
［9］徐文臣，张恒大，单德彬，等，TC4钛合金轮圈热旋成形技术研究[J]. 材料科学工艺，2008,16（1）：14-18.Xu W C,Zhang H D,Shan D B,et al. Hot spinning technology of wheel rim of TC4 titanium alloy[J].Materials Science & Technology,2008,16（1）：14-18.
［10］梁淑贤，吴凤照，张淳芳. 高精度薄壁钼管旋压工艺[J]. 稀有金属材料与工程，1995,24（4）：63-64.Liang S X,Wu F Z,Zhang C F. Spinning process of high-precision thin-wall molybdenum tube[J].Rare Metal Materials and Engineering,1995,24（4）：63-64.
［11］徐文臣，单德彬，陈宇，等. 钛合金薄壁筒形件热旋成形技术研究[J]. 锻压技术，2008，33（3）：56-59.Xu W C,Shan D B,Chen Y, et al. Study on hot spinning technology of tubular workpieces for TA15 titanium alloy[J]. Forging & Stamping Technology,2008,33(3):56-59.
［12］孟亚惠. 304、410S和E01不锈钢高温力学性能研究[D]. 兰州：兰州理工大学，2009.Meng Y H. Research on High-temperature Meehanieal Behaviors of 304,410s and E01 Stainless Steels[D]. Lanzhou: Lanzhou University of Technology,2009.
［13］梁淑贤，张淳芳，吴凤照，等. 错距旋压技术在钼管生产中的应用[J]. 稀有金属材料与工程，1993,22（1）：55-58.Liang S X,Zhang C F,Wu F Z, et al. The application of stagger spinning in molybdenum tube production[J]. Rare Metal Materials and Engineering,1993，22（1）：55-58.
［14］程秀全，吴万敏，张鹏，等. 筒形件错距旋压成形工艺参数优化[J]. 塑性工程学报，2012,19（5）：104-108.Cheng X Q,Wu W M,Zhang P,et al. Optimization of process parameters for tubular parts stagger spinning[J].Journal of Plasticity Engineering,2012,19（5）：104-108.
［15］黄科，陈兴驰，梁淑贤. 薄壁钨管旋压温度控制研究[J]. 广州有色金属学报，2005,15（4）：41-43.Huang K,Chen X C,Liang S X. The research of temperature control in thin-wall tungsten tube spinning[J]. Journal of Guangdong Non-Ferrous Metals,2005,15（4）：41-43.
［16］吕昕宇，王本贤,张士宏，等，LF6合金小锥度铝筒旋压成形试验研究[J]. 锻压技术，2005,30(3)：43-46.Lv X Y,Wang B X,Zhang S H,et al. Experimental investigation on spin forming of conical LF6 aluminum alloy tubes with a small angle[J]. Forging & Stamping Technology,2005,30(3)：43-46.
［17］夏琴香，张鹏，程秀全，等. 筒形件错距旋压成形工艺参数的正交试验研究[J]. 锻压技术，2012，37（6）：42-46.Xia Q X,Zhang P,Chen X Q,et al. Orthogonal experimental study on forming process parameters of tube stagger spinning[J]. Forming & Stamping Technology,2012,37(6): 42-46.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】