锻压技术

双级时效对7XXX系铝合金力学性能及晶间腐蚀性能的影响

英文标题：Influence of two-step aging on mechanical properties and intergranular corrosion performance of 7XXX aluminum alloy

作者：林洪刘利

单位：重庆工业职业技术学院

关键词：7XXX系铝合金时效时间力学性能晶间腐蚀

分类号：

出版年,卷(期):页码：2015,40(10):122-125

摘要：

采用常温拉伸、电导率、硬度、金相显微镜、扫描电镜及晶间腐蚀实验，研究了二级时效时间对7XXX系铝合金力学性能和微观性能的影响。结果表明，7XXX系铝合金经双级固溶、二级时效处理后，屈服强度、硬度及电导率随时效时间的增加而增大，抗拉强度变化不明显，断裂伸长率随时效时间的延长不断下降；二级时效165 ℃、16 h后屈服强度、硬度、电导率、抗拉强度、断裂伸长率分别为661 MPa、70 HRB、34.68%IACS、684 MPa和13.67%；金相照片显示合金内部存在未溶第二相及杂质相，经EDS能谱分析显示为Al7Cu2Fe相和含Si杂质相；二级时效165 ℃、16 h后，晶间腐蚀深度达到最小值23.34 μm，耐晶间腐蚀等级由3级提高至2级。

The influences of the two-step aging time on mechanical properties and microstructure of 7XXX aluminum alloy were studied by the experiments of normal temperature tensile, electrical conductivity, optical microscopy (OM), scanning electron microscopy (SEM) and inter-granular corrosion. The results show that after the two-step solid solution and two-step aging on 7XXX aluminum，its yield strength, hardness and electrical conductivity increase with the increase of aging time，and the tensile strength changes little while the rupture extension decreases with the increase of aging time. The yield strength, hardness， electrical conductivity, tensile strength, and rupture extension reach 661 MPa，70 HRB，34.68% IACS， 684 MPa，13.67% respectively when two-step aging is at 165 ℃ for 16 h. The undissolved second phases and impurity phase are found in alloy by metallograph，which are confirmed as Al7Cu2Fe and impurity phase containing Si by EDS. The intergranular corrosion depth reaches the maximum 23.34 μm, and the grade of intergranular corrosion resistance improves from the third grade to the second grade after two-step aging at 165 ℃ for 16 h.

基金项目：

林洪（1973-），女，本科，讲师

参考文献：

[1]Heinz A, Haszler A, Keidel C E, et al. Recent development in aluminum alloys for aerospace applications[J]. Materials Science and Engineering A,2000,280(1):102-107.

[2]方华婵,陈康华,巢红，等.Al-Zn-Mg-Cu系超强铝合金的研究现状与展望[J].粉末冶金材料科学与工程,2009,14(6):351-358.

Fang H C, Chen K H, Chao H,et al. Current research status and prespects of ultra strength Al-Zn-Mg-Cu aluminum alloy [J].Materials Science and Engineering of Powder Metallurgy，2009,14(6):351-358.

[3]Oliveira A F, Barros M C, Cardoso K R, et al. The effect of RRA on the strength and SCC resistance on AA7050 and AA7150 aluminum alloys[J]. Materials Science and Engineering , 2004,379(2): 321-326.

[4]冯春,刘志义,宁爱林，等.RRA处理对超高强铝合金抗应力腐蚀性能的影响[J].中南大学学报:自然科学版,2006,37(6):1054-1059.

Feng C，Liu Z Y, Ning A L,et al. Effect of retrogression and reaging treatment on stress corrosion cracking resistance of super- high strength aluminum alloy [J].Journal of Central South University:Science and Technology,2006,37(6):1054-1059.

[5]黄乐瑜.回归再时效处理制度对7055铝合金组织和性能的影响[D].长沙：中南大学，2011.

Hu L Y.Effect of Retrogression and Reaging on the Microstructure and Properties of 7055 Strength Aluminum Alloy [D].Changsha：Central South University，2011.

[6]黄兰萍,陈康华,李松，等.高温预析出后7055铝合金局部腐蚀性能和时效硬化[J].稀有金属材料与工程,2007,36(9):1628-1633.

Huang L P, Chen K H, Li S, et al. Influence of high-temperature pre-precipitation on local corrosion behaviors and ageing harden of 7055 aluminum alloy [J]. Rare Metal Material and Engineering,2007,36(9):1628-1633.

[7]GB/T 228—2002，金属材料室温拉伸试验方法[S].

GB/T 228—2002，Metallic materials-Tensile testing at ambient temperature[S].

[8]GB/T 7998—2005，铝合金晶间腐蚀测定方法[S].

GB/T 7998—2005，Test method for intergranular corrosion of aluminium alloy[S].

[9]高红选,古文全,吴建,等.固溶时效处理对铝合金电阻率及力学性能的影响[J].热加工工艺,2014,43(12):211-215.

Gao H X, Gu W Q, Wu J,et al. Effect of solution and aging treatment on electrical resistivity and mechanical properties of Al-Mg-Si Al alloy [J].Hot Working Technology,2014,43(12):211-215.

[10]Buha J, Lumley R N, Crosky A G. Secondary aging in an aluminum alloy 7050[J]. Materials Science and Engineering A,2008, 492(1): 1-10.

[11]张新明,宋丰轩,刘胜胆,等.双级时效对7050铝合金板材剥蚀性能的影响[J].中南大学学报:自然科学版,2011, 42(8):2252-2259.

Zhang X M, Song F X, Liu S D, et al. Influence of two-step aging on exfoliation corrosion properties of 7050 aluminum alloy plate [J].Journal of Central South University:Science and Technology,2011, 42(8):2252-2259.

服务与反馈：

【文章下载】【加入收藏】