L型截面铝型材拉弯成形截面畸变缺陷控制研究

英文标题：Section distortion control for L-section aluminum profile part in the stretch-bending process

作者：梁继业邓钢方斌

分类号：TG306

出版年,卷(期):页码：2016,41(12):42-45

摘要：

以某轨道车辆L型截面铝型材构件为研究对象，利用数值模拟技术分析了L型截面铝型材拉弯成形中常见截面畸变缺陷的成因，研究了模具结构参数对截面变形的影响规律，提出相应截面畸变缺陷的控制措施，并通过试验进行了验证。结果表明：L型截面铝型材拉弯成形主要截面畸变缺陷为立边倾斜和横边塌陷；立边倾斜缺陷主要因挡板间隙不合理引起，优化挡板间隙能够有效控制立边倾斜缺陷；横边塌陷主要因拉弯过程中立边收缩引起，基于相应位置的立边收缩量，通过减小拉弯模具支撑面的深度能够有效控制横边塌陷缺陷。

For L-section aluminum profile part in a rail vehicle, the causes producing the section distortion defects in stretch-bending process were analyzed by the numerical simulation, and the influences of the bending die structure parameters on the section deformation were studied. Then, the corresponding defect controlling methods were proposed and verified by tests. Results show that the general section distortion defects are the vertical wall obliquing and the horizontal plate collapsing. The former is caused by the unreasonable holder gap, which can be controlled by optimizing the holder gap, while the later is mainly induced by the shrinkage of the vertical wall, which can be controlled by decreasing the depth of the die supporting surface based on the shrinkage degree of the vertical wall.

基金项目：

作者简介：梁继业（1965-），男，学士，高级工程师 E-mail： liangjiye@cccar.com.cn

参考文献：

［1］He Z, Wang H N, Wang M J, et al. Simulation of extrusion process of complicated aluminium profile and die trial
［J］. Trans. Nonferrous Met. Soc. China, 2012,(22): 1732-1737.

［2］王志成, 何桃, 王旭, 等. 铝合金复杂变截面蒙皮拉形有限元仿真与试验研究
［J］. 锻压技术, 2016,41(8):53-58.

Wang Z C, He T, Wang X, et al. Finite element simulation and experimental verification on stretch forming of aluminum alloy complex variable section aircraft skin
［J］. Forging & Stamping Technology, 2016,41(8):53-58.

［3］李双, 庄新村, 赵震. 6061铝合金温精冲工艺的有限元分析
［J］. 锻压技术, 2016,41(8):35-38.

Li S, Zhuang X C, Zhao Z. Finite element analysis on aluminum alloy 6061 in warm fine blanking process
［J］. Forging & Stamping Technology, 2016,41(8):35-38.

［4］王浩, 桂林. 汽车车身铝合金板冲压成形有限元仿真与实验研究
［J］. 锻压技术, 2014, 39(7): 30-34.

Wang H, Gui L. Experimental research and FEM simulation of aluminum alloy stamping forming of automotive body
［J］. Forging & Stamping Technology, 2014, 39(7): 30-34.

［5］金朝海, 周贤宾, 刁可山, 等. 铝合金型材拉弯成形回弹的有限元模拟
［J］. 材料科学与工艺, 2004,(12): 394-397.

Jin C H, Zhou X B, Diao K S, et al. Springback analysis for stretch bending of aluminum profile
［J］. Materials Science & Technology, 2004,(12): 394-397.

［6］刘学之, 张石磊, 李世涛, 等. 中空铝合金型材拉弯成形工艺研究
［J］. 锻压技术, 2015, 40(5): 69-73.

Liu X Z, Zhang S L, Li S T, et al. Research on stretch bending of hollow aluminum alloy profile
［J］. Forging & Stamping Technology, 2015, 40(5): 69-73.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】