汽车后门内板转角起皱成因分析及对策

英文标题：Reason analysis and solutions of wrinkles at corners of automobile rear door inner panel

作者：林楷尤彬波苏丹杨建谢国文谢育涛

分类号：TG386.1

出版年,卷(期):页码：2017,42(6):43-50

摘要：

针对量产车型中一种常见的冲压质量问题——汽车后门内板转角起皱进行了研究。首先通过有限元软件建立某车型后门内板的冲压成形模型，对其进行工艺性分析，并重点对其在冲压成形过程中转角出现起皱的原因进行分析。结果表明，压应力是引起转角起皱的主要应力，同时后门内板转角处的工艺补充和产品结构不合理引起板料在冲压成形过程中出现Z向失稳，这直接导致出现起皱问题。最后，经过优化拉延筋布置形式、调整工艺补充以及优化产品结构，该后门内板经过有限元分析，结果未出现起皱问题，同时实际冲压所得产品也满足生产质量要求。

According to one common quality problem of stamping which widely exists in cars of mass production,the wrinkle at the corner of automobile rear door inner panel is studied. Firstly, the stamping model of one automobile rear door inner panel was built by FEM software for process analysis. And the reasons which caused the wrinkles during stamping were focused on. The result indicates that a compressive stress is the major reason that leads to the wrinkles at corner. In the mean time, the unreasonable designs for addendums and product structures at the corner of automobile rear door inner panel cause the instability in the Z-direction of sheets during stamping, and directly lead to the wrinkling problem. By optimizing the drawbeads, addendums and product structure, wrinkles disappear after FEM analysis, and the quality of rear door inner panel fulfills all production and quality requirements.

基金项目：

林楷（1988-），男，硕士

参考文献：

［1］崔令江. 汽车覆盖件冲压成形技术[M]. 机械工业出版社, 2003.

Cui L J. Stamping Technology for Automobile Panel[M]. China Machine Press, 2003.

［2］崔令江, 杨玉英, 李硕本. 薄板冲压成形中剪应力起皱的实验研究[J]. 锻压技术, 2002, 27(2): 27-30.

Cui L J, Yang Y Y, Li S B. Test study on shear stress wrinking in sheet metal forming [J]. Forging & Stamping Technology, 2002, 27(2): 27-30.

［3］张琪.乘用车地板通道零件回弹及起皱特性分析[J]. 锻压技术，2015, 40(6): 34-38.

Zhang Q. Analysis on springback and wrinkle of car floor channel part [J]. Forging & Stamping Technology, 2015, 40(6): 34-38.

［4］韩方圆. 剪应力起皱机理及主要规律的研究[D]. 哈尔滨：哈尔滨工业大学, 2013.

Han F Y. Study on Mechanism and Main Laws of Shear Stress Wrinkling[D]. Harbin: Harbin Institute of Technology, 2013.

［5］邓劲松, 蔡孝, 回金楷, 等. 车门内板后部冲压工艺优化:续1[J]. 汽车工程师, 2012, (7): 39-41.

Deng J S, Cai X, Hui J K, et al. Stamping process optimization for the rear part of door inner panel:Continued 1 [J]. Auto Engineer, 2012, (7): 39-41.

［6］王同领, 杨杨. 车门内板褶皱问题的解决[J]. 汽车工程师, 2014, (1): 58-59.

Wang T L, Yang Y. Solution on corrugated inner door panel [J]. Auto Engineer, 2014, (1): 58-59.

［7］吴华英, 王永信, 肖春辉, 等. 轿车门内板成形工艺参数敏感性分析[J]. 锻压技术, 2012, 37(2): 38-41.

Wu H Y, Wang Y X, Xiao C H, et al. Sensitivity analysis of forming process parameters for car door inner panel [J]. Forging & Stamping Technology, 2012, 37(2): 38-41.

［8］余海燕, 高云凯, 朱文峰. 拼焊车门内板冲压成形性分析[J]. 汽车工程, 2008, 30(10): 923-926.

Yu H Y, Gao Y K, Zhu W F. Stamping formability analysis for door inner panels made of tailor welded blanks [J]. Automotive Engineering, 2008, 30(10): 923-926.

［9］马国英，黄彬兵，苏春建，等.汽车翼子板拉深成形模拟及工艺参数优化[J]. 锻压技术，2015, 40(3): 21-24.

Ma G Y, Huang B B, Su C J, et al. Simulation and parameters optimization of deep drawing for automobile fender [J]. Forging & Stamping Technology, 2015, 40(3): 21-24.

［10］郑捷，陈泽中，曾渠鸿. 发动机内盖板拉延成形的数值模拟及参数优化[J]. 塑性工程学报，2015, 22(1): 94-98.

Zheng J, Chen Z Z, Zeng Q H. Numerical simulation and parameter optimization of drawing process for engine cover [J]. Journal of Plasticity Engineering, 2015, 22(1): 94-98.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】