DEFORM模拟支撑辊的锻造

英文标题：Simulation on forging of back-up roll by DEFORM

作者：王玉红马廷威

单位：营口理工学院

关键词：支撑辊钢锭 DEFORM 等效应变 WHF法缺陷

分类号：TG316.1

出版年,卷(期):页码：2017,42(8):185-190

摘要：

轧机中的关键零件之一支撑辊在轧制设备运行的过程中承受轧辊传来的交变应力。大型支撑辊由大型钢锭锻造而成，但大型钢锭中存在种种缺陷，给支撑辊的质量带来很多问题。针对此问题，采用WHF法能够锻合锻件内部组织缺陷，可改善锻件质量。采用DEFORM软件，模拟WHF法拔长，研究WHF法在锻造拔长过程中对锻件心部的作用。实验研究表明，WHF法在拔长的第3道次时，锻件心部的应力状态由拉应力完全转变为压应力。同时，到第6道次后，锻件心部等效应变达到1.2。通过锻件心部压应力和等效应变值可知，WHF法能够完全破碎锻件内部的组织缺陷，生产出质量合格的支撑辊锻件。

The back-up roll is one of important roles in rolling equipment and bears the alternating stress that comes from the roll when the rolling equipment works. However, the huge back-up roll was forged by huge ingot, and some defects existed could cause a lot of quality problems. For the above problem, the ingot defects were forged by WHF method, and the forging quality was improved. Then, WHF pulling was simulated by DEFORM software, the effect of WHF on the core of forging during the processes of forging and pulling was studied. The experiment study shows that stress in the core of forging transfers from tensile stress into compressive stress on the third pass. At the same time, the equivalent strain in the core of forging reaches 1.2 after the sixth pass. Therefore, the WHF method can completely avoid the internal defects of forging, and produces the qualified back-up roll forgings according to the values of the compressive stress and equivalent strain in the core of forging.

基金项目：

2015年度营口理工学院院级科研项目（QNL201512）

王玉红（1983-），女，硕士，讲师马廷威（1978-），男，硕士，副教授

参考文献：

［1］陈拂晓,蔡志伟,王园园,等. 70Cr3Mo钢动态再结晶临界条件研究[J].锻压技术,2015,40(11):107-111.Chen F X, Cai Z W, Wang Y Y, et al. Research on critical conditions of dynamic recrystallization for steel 70Cr3Mo[J]. Forging & Stamping Technology, 2015,40(11):107-111.
［2］赵俊伟. 大型支撑辊锻件锻造工艺与模拟技术研究[D]. 洛阳: 河南科技大学,2009.Zhao J W. Forging Technology and Numerical Simulation for Heavy Supporting Roll [D]. Luoyang: Henan University of Science and Technology,2009.
［3］刘倩,黄放,吴玉忠.大型锻件心部空洞型缺陷控制的数值模拟研究[J].锻压技术,2014,39(2):132-136.Liu Q, Huang F, Wu Y Z. Numerical simulation study on central void defects control for heavy forgings [J]. Forging & Stamping Technology, 2014,39(2):132-136.
［4］Liu X R, Zhou X D. The forging penetration efficiency of C45 steel stepped shaft radial forging with GFM forging machine [J]. Advanced Materials Research, 2010, 154-155:593-596.
［5］邓冬梅.大型锻件锻造新理论与新工艺的数值模拟[D].秦皇岛：燕山大学,2001.Deng D M. Numerical Simulation of New Theory and New Technology of Heavy Forgings[D]. Qinhuangdao：Yanshan University,2001.
［6］刘晓斐,苏娟华,许莹莹.整锻挤压辊两次镦拔新工艺的数值模拟[J].锻压技术,2007，32(6):50-53.Liu X F, Su J H, Xu Y Y, Numerical simulation of two times upsetting and stretching process for squeeze roll whole forging [J]. Forging & Stamping Technology, 2007，32(6):50-53.
［7］梁晨,刘助柏. LZ锻造的砧宽比、料宽比的临界值研究[J].锻压技术,2004，29(3):14-16.Liang C, Liu Z B. Study on critical value of tool width ratio and blank width ratio of LZ forging [J]. Forging & Stamping Technology, 2004,29(3):14-16.
［8］余琼,董湘怀,吴云剑.径向压下率与送进率对径向锻造工件质量的影响[J].锻压技术，2015，40(8):64-70.Yu Q, Dong X H, Wu Y J. Influences of radial reduction ratio and feed ratio on radial forging quality[J]. Forging & Stamping Technology, 2015,40(8):64-70.
［9］陈锟,杨弋涛,邵光杰.钢锭内部孔隙性缺陷锻合过程的数值模拟[J].塑性工程学报,2010,17(1):6-10.Chen K, Yang Y T, Shao G J. Simulation of void closure in ingots during forging[J].Journal of Plasticity Engineering, 2010,17(1):6-10.
［10］李庆华,冀方冉,李付国.塑性变形中应力状态与应力状态参数的关系[J].锻压技术,2014,39(3):122-126.Li Q H, Ji F R, Li F G.Relationship of stress state and stress state parameters in plastic deformation[J]. Forging & Stamping Technology, 2014,39(3):122-126.

服务与反馈：

【文章下载】【加入收藏】