Al2O3/7075复合材料的摩擦磨损性能

英文标题：Friction and wear properties of Al2O3/7075 composite

作者：吉顺吴庆捷闫洪刘建龙聂俏

分类号：TG146.2+1；TG292

出版年,卷(期):页码：2018,43(11):132-136

摘要：

采用高能超声法制备了Al2O3质量分数分别为0，1.0%，2.0%和3.0%时Al2O3/7075复合材料。利用销盘式磨损试验机，对不同Al2O3含量的Al2O3/7075复合材料在不同负载下（15，30，45和60 N）进行了干滑动摩擦磨损试验。结果表明：Al2O3的加入细化了基体组织；相比于7075铝合金基体，2.0%Al2O3/7075复合材料的硬度提高了17.5%。随着负载的增加，复合材料的磨损量和摩擦系数均增加；在相同负载下，复合材料的磨损量和摩擦系数比7075铝合金基体低。相比于基体，在60 N负载下，2.0%Al2O3/7075复合材料的磨损量降低了80.5%。60 N负载下，基体合金磨损机制以黏着磨损为主，随着Al2O3含量的增加，复合材料磨损机制向剥层磨损转变。

Al2O3/7075 composite with Al2O3 mass fraction of 0, 1.0%, 2.0% and 3.0% were fabricated by high-intensity ultrasonic treatment respectively, and the dry sliding friction and wear tests of Al2O3/7075 composite with different Al2O3 content were conducted under different loads (15,30,45 and 60 N)by pin-disk type wear testing machine. The result shows that the addition of Al2O3 particles refines the matrix structure, and the hardness of 2.0% Al2O3/7075 composite increases by 17.5% compared to 7075 aluminum alloy matrix. Then, both wear volume and friction coefficient of the composite increase with the increasing of load, and the wear volume and friction coefficient of the composite are lower than that of 7075 aluminum alloy matrix under invariable load. Compared to the 7075 aluminum alloy matrix, the wear volume of 2.0%Al2O3/7075 composite under 60 N load decreases by 80.5%, and under 60 N load, the main wear mechanism of 7075 aluminum alloy matrix is adhesive wear, and with the increasing of Al2O3 content, the wear mechanism of the composite changes into the peeling wear.

基金项目：

江西省自然科学基金资助项目（20171BAB206034）

吉顺（1994-），男，硕士研究生,E-mail：1078608622@qq.com;通讯作者：闫洪（1962-），男，博士，教授，博士生导师,E-mail：yanhong_wh@163.com

参考文献：

［1］Koli D K, Agnihotri G, Purohit R. Advanced aluminium matrix composites:The critical need of automotive and aerospace engineering fields
［J］. Materials Today Proceedings, 2015, 2(4-5)：3032-3041.

［2］Radha A, Vijayakumar K R. An investigation of mechanical and wear properties of AA6061 reinforced with silicon carbide and graphene nano particles-particulate composites
［J］. Materials Today Proceedings, 2016, 3(6)：2247-2253.

［3］Bhaskar K V, Sundarrajan S, Rao B S, et al. Effect of reinforcement and wear parameters on dry sliding wear of aluminum composites-A review
［J］. Materials Today Proceedings, 2018, 5(2)：5891-5900.

［4］Rao K V S, Govindaraju. Sliding wear behavior of cast Al-7075 alloy reinforced with MgO particulates
［J］. Materials Today Proceedings, 2017, 4(10)：11096-11101.

［5］Singh K K, Singh S, Shrivastava A K. Comparison of wear and friction behavior of aluminum matrix alloy (Al 7075) and silicon carbide based aluminum metal matrix composite under dry condition at different sliding distance
［J］.Materials Today, 2017,4(8)：8960-8970.

［6］Aranke O, Gandhi C, Dixit N, et al. Influence of multiwall carbon nanotubes (MWCNT) on wear and coefficient of friction of aluminium (Al 7075)metal matrix composite
［J］. Materials Today Proceedings, 2018, 5(2)：7748-7757.

［7］Ravindranath V M, Shankar G S S, Basavarajappa S, et al. Dry sliding wear behavior of hybrid aluminum metal matrix composite reinforced with boron carbide and graphite particles
［J］. Materials Today Proceedings, 2017, 4(10)：11163-11167.

［8］Altnkok N, zsert I·, Fndk F. Dry sliding wear behavior of Al2O3/SiC particle reinforced aluminium based MMCs fabricated by stir casting method
［J］. Acta Physica Polonica, 2013, 124(1)：11-19.

［9］Wu Q J, Yan H, Zhang P X, et al. Enhancing wear resistance of A356 alloy by adding CNFs based on ultrasonic vibration casting
［J］. Acta Metallurgica Sinica, 2018，31(2)：1-10.

［10］王志伟, 闫洪, 熊俊杰. Sr变质对ADC12合金摩擦磨损性能的影响
［J］. 中国有色金属学报, 2016, 26(5)：1075-1083.

Wang Z W, Yan H, Xiong J J. Effect of Sr modification on friction and wear properties of ADC12 alloy
［J］. The Chinese Journal of Nonferrous Metals, 2016, 26(5)：1075-1083.

［11］Kumar G B V, Rao C S P, Selvaraj N. Mechanical and tribological behavior of particulate reinforced aluminum metal matrix composites-A review
［J］. Journal of Minerals & Materials Characterization & Engineering, 2010, 10(1)：59-91.

［12］Liu W, Yan H, Zhu J B. Effect of the addition of rare earth element La on the tribological behaviour of AlSi5Cu1Mg alloy
［J］. Applied Sciences, 2018, 8(2)：163.

［13］Sun Z, Zhang D, Li G. Evaluation of dry sliding wear behavior of silicon particles reinforced aluminum matrix composites
［J］. Materials & Design, 2005, 26(5)：454-458.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】