镦粗过程中摩擦对空洞演变行为的影响

英文标题：Influence of friction on void evolution behavior during upsetting

作者：秦敏刘建生李景丹

单位：太原科技大学

分类号：TG316

出版年,卷(期):页码：2020,45(2):24-29

摘要：

采用有限元模拟方法，模拟计算了摩擦因子为0.3，0.5和0.7时，锻件不同位置空洞的闭合情况。分析了不同摩擦因子下，锻件不同位置的空洞高度的变化规律，结果发现：锻件内部空洞比边缘的空洞更容易闭合，并且随着摩擦因子的增大，内部空洞闭合速度加快，边缘空洞闭合速度减慢。分析摩擦因子、静水应力、等效应变、空洞闭合速度的关系发现：在锻件的内部位置，随摩擦因子增大,静水应力绝对值增大、等效应变增大、空洞闭合速度增大；在锻件的边缘位置，随着摩擦因子增大，等效应变减小、空洞闭合速度减小。摩擦因子对锻件边缘位置空洞闭合情况和等效应变的影响大于对锻件内部位置空洞的影响。

The void closure in different positions of forgings was simulated by the finite element method when the friction factors were 0.3, 0.5 and 0.7, and the change laws of void height in different positions of forgings under different friction factors were analyzed. The result show that the inner voids are easier to close than the edge voids, the closing speed of the inner voids increases with the increasing of friction factor, and the closing speed of the edge voids slows down. By analyzing the relationship among friction factor, hydrostatic stress, equivalent strain and closing speed of voids, it is found that in the internal position of forgings, with the increasing of friction factor, the absolute value of hydrostatic stress increases, the effective strain increases, and the closing speed of voids increases. At the edge of forgings, with the increasing of friction factor, the effective strain decreases, and the closing speed of voids decreases. Thus, the influence of the increased friction factor on the void closure and the equivalent strain at the edge position of forgings is greater than that in the center of forgings.

基金项目：

山西省自然科学基金重点基金资助项目（201601D011002）

秦敏（1980-），女，博士研究生，讲师，E-mail：wsqm2008@163.com；通讯作者：刘建生（1958-），男，博士，教授，博士生导师，E-mail：jiansliu@163.com

参考文献：

[1]任耀,王强,张治民,等.不同镦粗温度对AZ80镁合金空洞闭合演化规律的影响研究[J].热加工工艺，2019，48(5)：154-157.
Ren Y, Wang Q, Zhang Z M, et al. Effect of different upsetting temperature on evolution of void closure in AZ80 magnesium alloy[J].Hot Working Technology,2019，48(5)：154-157.
[2]柯百龙,李霞,赵东,等. 大锻件内空洞形状对闭合影响的模拟研究[J].金属铸锻焊技术, 2011, 40（15）:3-7.
Ke B L, Li X, Zhao D, et al. Simulation on effect of shape of interior cavity in heavy forgings on closure[J].Casting Forging Welding,2011，40（15）:3-7.
[3]吴玉忠. 平砧拔长长方体钛合金锻件的数值模拟研究[J].现代机械,2017,(5):67-70.
Wu Y Z. Numerical simulation research of flat anvil pulling long rectangle titanium alloy forgings[J].Modern Machinery,2017，（5）:67-70.
[4]田端阳,束学道,王雨,等.浮压法压实楔横轧轴件心部空洞的机理研究[J].机械科学与技术,2017,36（7）:1079-1084.
Tian D Y,Shu X D,Wang Y,et al. Study on compacting mechanism of core void for cross wedge rolling shaft using floating-pressure method[J].Mechanical Science and Technology for Aerospace Engineering，2017,36（7）:1079-1084.
[5]蒋智,任广升,徐春国,等.圆柱体热锻件内部单空洞闭合的模拟分析[J].塑性工程学报,2005,12（1）:47-49.
Jiang Z, Ren G S, Xu C G, et al. An analyse simulation for single pore closure in hot cylinder ingots[J]. Journal of Plasticity Engineering, 2005,12（1）:47-49.
[6]崔振山,徐秉业,任广升,等.圆柱体内部空洞热锻闭合过程的数值模拟[J].塑性工程学报,2002,9（1）:49-52.
Cui Z S, Xu B Y, Ren G S，et al. Numerical simulation of fore closure in solid cylinder under hot forging[J].Journal of Plasticity Engineering,2002,9（1）:49-52.
[7]崔振山,任广升,徐秉业,等. 圆柱体内部空洞的热锻合条件[J].清华大学学报: 自然科学版,2003，43 (2):227-233.
Cui Z S, Ren G S，Xu B Y, et al. Void closing conditions for solid cylinders during hot forging[J].Journal of Tsinghua University: Science and Technology,2003，43 (2):227-233.
[8]刘丽娟，崔振山.大锻件裂隙型缺陷焊合规律[J]. 塑性工程学报，2010，17 (1): 1-5.
Liu L J, Cui Z S. Study on the bonding condition of inner crack defects in heavy forgings[J].Journal of Plasticity Engineering,2010，17 (1): 1-5.
[9]黄华贵,杜凤山,许志强.影响大锻件内部孔隙性缺陷扩散焊合的因素[J].钢铁研究学报,2007,19(11):55-59.
Huang H G, Du F S, Xu Z Q. Factors affecting diffusion welding of internal porosity defects in heavy forgings[J]. Journal of Iron and Steel Research,2007,19(11):55-59.
[10]张效迅,崔振山.非线性塑性材料内部空洞闭合模型的研究[J].应用数学和力学,2009,30（5）：587-597.
Zhang X X, Cui Z S. Theoretical study of void closure in nonlinear plastic materials[J].Applied Mathematics and Mechanics,2009,30（5）：587-597.
[11]张效迅.大锻件锻造成形过程中内部空洞型缺陷演化规律的研究[D].上海: 上海交通大学,2009.
Zhang X X. Research on Void Evolution in Large Ingot During Hot Forging[D].Shanghai: Shanghai Jiao Tong University,2009.
[12]李妍.大锻件镦粗成形中内部空洞型缺陷的演化规律研究[D].上海: 上海交通大学,2009.
Li Y, Research on Evolution of Void Defects in Heavy Forgings During Upsetting Process[D].Shanghai: Shanghai Jiao Tong University,2009.

服务与反馈：

【文章下载】【加入收藏】