光纤激光切割工艺参数对切割质量的影响

英文标题：Influence of process parameters on cutting quality in optical fiber laser cutting

作者：何帆胡志力刘鹏

单位：1. 武汉理工大学现代汽车零部件技术湖北省重点实验室 2 武汉理工大学汽车零部件技术湖北协同创新中心 3. 东风（武汉）实业有限公司

分类号：TG485

出版年,卷(期):页码：2020,45(11):82-88

摘要：

采用3000 W光纤激光器与数控机床组成的光纤激光切割系统，对1.4 mm厚的热成形高强钢薄板切割质量的影响规律进行了研究。设计了3因素5水平的正交实验，并系统地研究了激光功率、切割速度以及辅助气体压力等工艺参数对切缝宽度和挂渣高度的影响。实验结果表明，激光功率和切割速度是影响切缝质量的主要工艺参数。当激光功率为3000 W、切割速度v为11 m·min-1、辅助气体压力F为1.1 MPa、喷嘴与工件的间距Δ为0.8 mm时，得到最小的挂渣高度为46.32 μm。

The influence law of cutting quality for thermoforming high strength steel sheet with the thickness of 1.4 mm was studied by the optical fiber laser cutting system composed of 3000 W optical fiber laser and CNC machine tool. Then, the orthogonal experiment with three factors and five levers was designed, and the influences of laser power, cutting speed, auxiliary gas pressure and other process parameters on the slit width and the slag height were systematically studied. The experimental results show that the laser power and the cutting speed are the main process parameters that affect the quality of slit. When the laser power is 3000 W, the cutting speed v is 11 m·min-1, the auxiliary gas pressure F is 1.1 MPa and the distance Δ between nozzle and workpiece is 0.8 mm, the minimum slag height obtained is 46.32 μm.

基金项目：

新能源汽车科学与关键技术学科创新引智基地（B17034）;教育部创新团队发展计划（IRT_17R83）;湖北省技术创新专项重大项目资助（2019AAA007）

何帆（1993-），男，硕士研究生 E-mail：943622677@qq.com；通讯作者：胡志力（1983-），男，博士，副教授 E-mail：zhilihuhit@163.com

参考文献：

[1]方晓汾，王静霞. 汽车轻量化用冷轧Fe-17Mn-0.05C高锰钢拉伸性能和氢脆断裂分析 [J].锻压技术，2019,44(1):157-160.

Fang X F, Wang J X. Analysis on tensile properties and hydrogen embrittlement fracture of coldrolled Fe-17Mn-0.05C high manganese steel for vehicle lightweight [J].Forging & Stamping Technology，2019, 44(1):157-160.

[2]Hyunwoo S, Famann D, Hoffmann H, et al. An investigation of the blanking process of the quenchable boron alloyed steel 22MnB5 before and after hot stamping process[J]. Journal of Materials Processing Technology, 2012, 212(2): 437-449.

[3]Meschut G, Matzke M, Hoerhold R, et al. Hybrid technologies for joining ultrahighstrength boron steels with aluminum alloys for lightweight car body structures[J]. Procedia CIRP, 2014, 23: 19-23.

[4]Rajaram N, SheikhAhmad J, Cheraghi S H. CO2 laser cut quality of 4130 steel[J]. International Journal of Machine Tools and Manufacture, 2003, 43(4): 351-358.

[5]Lamikiz A, Lacalle L N, Sánchez J A, et al. CO2 laser cutting of advanced high strength steels (AHSS)[J]. Applied Surface Science, 2005, 242(3): 362-368.

[6]Fernandes F A O, Oliveira D F, Pereira A B. Optimal parameters for laser welding of advanced highstrength steels used in the automotive industry[J]. Procedia Manufacturing, 2017, 13: 219-226.

[7]Seon S, Shin J S, Oh S Y, et al. Improvement of cutting performance for thick stainless steel plates by steplike cutting speed increase in highpower fiber laser cutting[J]. Optics & Laser Technology, 2018, 103: 311-317.

[8]Senthil K, Jayaprakash G. Parametric investigation and modelling of hardness and surface quality in CO2 laser cutting process of AISI314 stainless steel[J]. New Materials for Electro chemical Systems, 2017, 20(3): 101-107.

[9]Tahir A F M, Aqida S N. An investigation of laser cutting quality of 22MnB5 ultra high strength steel using response surface methodology[J]. Optics & Laser Technology, 2017, 92: 142-149.

[10]Chagnot C, Dinechin G, Canneau G. Cutting performances with new industrial continuous wave ND: YAG high power lasers: For dismantling of former nuclear workshops, the performances of recently introduced high power continuous wave ND: YAG lasers are assessed[J]. Nuclear Engineering and Design, 2010, 240(10): 2604-2613.

[11]Quintino L, Costa A, Miranda R, et al. Welding with high power fiber lasers-A preliminary study[J]. Materials & Design, 2007, 28(4): 1231-1237.

[12]刘会强. 高强钢热成形零件的激光切割技术研究[D]. 武汉：华中科技大学, 2014.

Liu H Q. Research on Laser Cutting Technology for Hot Forming Parts of High Strength Steel[D]. Wuhan: Huazhong University of Science and Technology, 2014.

[13]Riveiro A, Quintero F, Lusquios F, et al. Parametric investigation of CO2 laser cutting of 2024-T3 alloy[J]. Journal of Materials Processing Technology, 2010, 210(9): 1138-1152.

[14]陈聪, 高明, 顾云泽, 等. 光纤激光切割铝合金薄板工艺特性研究[J]. 中国激光, 2014, 41(6): 79-85.

Chen C, Gao M, Gun Y Z, et al. Study on the technological characteristics of aluminum alloy sheet cut by optical fiber laser [J]. China Journal of Lasers, 2014, 41(6): 79-85.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】