汽车侧围外板表面缺陷分析及冲压工艺优化
英文标题:Surface defect analysis and stamping process optimization on automobile side wall outer panel
作者:代丽 朱勇 
单位:上汽大众汽车有限公司 
关键词:侧围外板  表面缺陷  冲压工艺  模具结构  藏料工艺凸包 
分类号:TG386
出版年,卷(期):页码:2021,46(6):91-98
摘要:

 汽车外覆盖件的表面质量直接影响整车的外观,是冲压成形领域关注的重点之一。针对SVW斯柯达品牌某车型侧围外板在冲压成形过程中出现的开裂、起皱、圆弧轮廓不平顺等一系列表面缺陷,从工艺设计和模具结构的角度分析了缺陷产生的原因。结合CAE模拟和现场调试,在满足试模压机和生产线压机不同工况的条件下,通过优化产品表面藏料工艺凸包,同时平衡压料力和整形力,解决了最困难的表面问题,达到了生产稳定性和产品质量的要求,并在此基础上,对工艺优化产生的经济效益进行了统计。对汽车行业侧围外板产品的零件设计、侧围冲压模具工艺和结构设计、侧围冲压模具调试均具有参考意义。

 The surface quality of automobile outer panel directly affects the appearance of vehicle, which is one of the key points in stamping field. For a series of surface defects such as cracks, wrinkles, uneven arc contour, etc. in the side wall outer panel of a certain model for SVW Skoda brand during stamping process, the reasons for defects were analyzed from the perspective of process design and die structure. Then, combining CAE simulation and on-site debugging, on the basis of satisfying different working conditions of test press and production line press, the most difficult surface problem was solved by optimizing the product surface storage process convex hull and balancing the blank hold force and the shaping force, and the requirements for production stability and product quality were met. On the basis, the economic benefits produced by process optimization were calculated, and it was of reference signification for part design, stamping die process and structure design of side wall, and stamping die debugging of side wall of side wall outer panel product in automobile industry.

基金项目:
作者简介:
代丽(1988-),女,硕士,工程师 E-mail:hust_liqing@163.com
参考文献:

 [1]吴磊, 陈新平,蒋浩民,等. 侧围外板零件典型开裂与改善[J]. 塑性工程学报,201421(4)55-59.


 


Wu L, Chen X P, Jiang H M, et al. Typical cracking and improvement plans of body side outer parts[J]. Journal of Plasticity Engineering, 2014, 21(4):55-59.


 


[2]田国富, 李文杰,李君基. 基于Dynaform6016-T4P铝合金汽车机舱盖模面优化 [J]. 锻压技术,2020,45(1):55-62.


 


Tian G FLi W JLi J J. Optimization on die face of engine compartment cover for 6016-T4P aluminum alloy based on Dynaform [J]. Forging & Stamping Technology2020,45(1):55-62.


 


[3]王良芬, 李慧,高亮,等. 侧围外板起皱问题分析及控制措施[J]. 模具工业,201743(10):28-31.


 


Wang L F, Li H, Gao L, et al. Analysis and control measurements of wrinkiling for lateral outer panel[J]. Die & Mould Industry, 2017, 43(10):28-31.


 


[4]贡见秀, 沈左军,孟祥新. 解决侧围外板A柱区域冲压叠料缺陷[J]. 模具技术,2013(1):35-39.


 


Gong J X, Shen Z J, Meng X X. Solution to stamping wrinkles defects around A pillar area of body side outer[J]. Die and Mould Technology, 2013, (1):35-39.


[5]刘志军, 梁秀强,卢宁. 汽车冲压件起皱叠料问题的解决方案[J]. 模具制造,201515(2):20-23.


 


Liu Z J, Liang X Q, Lu N. Solutions for the wrinkling and folding problem of automobile satmping parts[J]. Die & Mould Manufacture, 2015, 15(2):20-23.


 


[6]胡治钰, 王银巧. 汽车外覆盖件冲压表面缺陷的产生原因及预防措施[J]. 模具技术,2012(5):35-38.


 


Hu Z Y, Wang Y Q. Reasons and preventive measures of surface defects in th autobody outside covering stamping[J]. Die and Mould Technology, 2012, (5):35-38.


 


[7]马金胜, 纪广安,董佳. 侧围凹坑缺陷的处理方案[J]. 模具制造,201717(11):18-21.


 


Ma J S, Ji G A, Dong J. The treatment scheme of the pit defect for the side girth[J]. Die & Mould Manufacture, 2017, 17(11):18-21.


 


[8]牛超, 陈新平,崔振祥. 基于AutoformDynaform软件的超高强钢零件仿真对比[J]. 精密成形工程,20179(6):53-56.


 


Niu C, Chen X P, Cui Z X. Comparison of forming simulation for UHSS part based on Autoform and Dynaform[J]. Journal of Netshape Forming Engineering, 2017, 9(6):53-56.


 


[9]Demirci H, Esner C, Yasar M. Effect of the blank holder force on drawing of aluminum alloy square cup: Theoretical and experimental investigation[J]. Journal of Materials Processing Technology, 2008,206(1-3):152-160.


 


[10]蒋磊, 龚剑,王龙,等. 翼子板试制冲压工艺与模具设计 [J]. 锻压技术,2020,45(2):73-80.


 


Jiang LGong JWang Let al. Trial stamping process and die design of fender [J]. Forging & Stamping Technology2020,45(2): 73-80.


 


[11]Eskandari M, ZareiHanzaki A, Marandi A. An investigation into the mechanical behavior of a new transformationtwinning induced plasticity steel [J]. Materials & Design, 2012, 39:279-284.


 


[12]王庆阳, 高梦迪,李磊,等. 冲压成形节能优化方法[J]. 锻压技术,201944(6):134-144.


 


Wang Q Y, Gao M D, Li L, et al. Energysaving optimization method of stamping[J]. Forging & Stamping Technology, 2019, 44(6):


134-144.

服务与反馈:
文章下载】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管  中国机械总院集团北京机电研究所有限公司 中国机械工程学会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9