锻压技术

基于响应面法发动机连杆热锻模具磨损失效分析

英文标题：Analysis on wear failure of hot forging die for engine connecting rod based on response surface method

作者：张松泓徐颖若

单位：河南工业职业技术学院

分类号：TG376.2

出版年,卷(期):页码：2021,46(7):178-184

摘要：

以发动机连杆作为研究对象，有效预测连杆终锻上模磨损最严重区域和使用寿命。基于Archard修正磨损模型，采用滑移速度﹑表面温度和表面压强作为评定终锻上模磨损量的依据，预测上模磨损最严重位置，对磨损最严重区域，选取上模材料初始硬度、摩擦因数、上模预热温度和下压速度进行单因素和多因素离散试验，以优化磨损量；对连杆进行20次模拟，并对磨损量结果进行曲线拟合，预测连杆终锻上模的使用寿命。模拟结果表明，上模P2点区域为磨损最严重位置，该区域优化后的最优磨损量为0.9615×10-6 mm，对应的最优参数组合为:预热温度为200 ℃、初始硬度为58 HRC、摩擦因数为0.3和下压速度为55 mm·s-1。试验表明，模型预测和实际磨损量数值基本相同，回归模型的预测数值可信度极高，该模型终锻上模寿命为87298次。研究结果有助于降低试模成本，提高连杆模具的研发成功率。

For the engine connecting rod, the most severely worn area and the service life of final forging upper die for connecting rod were effectively predicted, and based on the Archard modified wear model, the slip speed, surface temperature and surface pressure were used as the basis for evaluating the wear of final forging upper die. Then, the most severely worn position of the upper die was predicted, and the wear amount in the most severely worn area was optimized by single-factor and multi-factor discrete tests choosing the initial hardness of upper die material, the friction coefficient, the preheating temperature of upper die and the down pressure speed. Furthermore, twenty simulations were performed on the connecting rod, and the result of wear amount was curve-fitted to predict the service life of the final forging upper die for connecting rod. The simulation results show that the P2 point area in the upper die is the location of the most severely worn area. After optimization of this area, the optimal wear amount is 0.9615×10-6 mm, and the corresponding optimal parameter combination is the preheating temperature of 200 ℃, the initial hardness of 58 HRC, the friction coefficient of 0.3 and the down pressure speed of 55 mm·s-1. In addition, the model prediction values and the actual wear amounts are basically the same, the prediction value of the regression model is extremely reliable, and the life of the final forging upper die for the model is 87298 times. Thus, the result helps to reduce the cost of trial die and increase the successful rate of development for connecting rod die.

基金项目：

河南省科技厅科技攻关项目(172102310761）

作者简介：张松泓(1988-), 男, 硕士, 讲师，E-mail：1005165365@qq.com

参考文献：

[1]汪乐乐. 汽车发动机连杆毛坯铸锻复合成形工艺的数值模拟研究[D]. 长春：吉林大学,2018.
Wang L L. Numerical Simulation on Composite Forming Process of Forging and Casting for Car Engine Connecting Rod Blank[D]. Changchun: Jilin University,2018.
[2]莫才颂, 马李.连杆锻造模具应力模拟及失效分析[J].工具技术,2020,54(8):69-72.
Mo C S，Ma L. Stress simulation and failure analysis of connecting rod forging die[J].Tool Engineering,2020,54(8):69-72.
[3]张伟. 6061铝合金热变形行为及连杆闭塞锻造研究[D].哈尔滨：哈尔滨理工大学,2019.
Zhang W. Study on Hot Deformation Behavior of 6061 Aluminum alloy and Closed-die Forging of Connecting Rod[D]. Harbin: Harbin University of Science and Technology, 2019.
[4]陆元三, 王培安,郭欢欢.挤压次数对端盖凸模磨损的失效模拟研究[J].材料保护,2020,53(1):96-100, 119.
Lu Y S, Wang P A, Guo H H. Failure simulation of extrusion times on endface punch wear[J].Materials Protection, 2020, 53(1):96-100,119.
[5]陆元三, 李颖颖,王培安.基于Archard理论对连杆预锻凹模寿命分析[J].锻压技术,2020,45(8):164-169.
Lu Y S, Li Y Y, Wang P A. Life analysis of pre-forging die for shifting fork based on Archard theory[J].Forging & Stamping Technology, 2020,45(8):164-169.
[6]林高用, 冯迪,郑小燕,等.基于Archard理论的挤压次数对模具磨损量的影响分析[J].中南大学学报: 自然科学版, 2009, 40(5):1245-1251.
Lin G Y, Feng D, Zheng X Y, et al. Analysis of influence of extrusion times on total die wear based on Archard theory[J].Journal of Central South University: Science and Technology,2009,40(5):1245-1251.
[7]Lee R S, Jou J L. Application of numerical simulation for wear analysis of warm forging die[J].Journal of Materials Processing Technology, 2003, 140(1-3):43-48.
[8]王培安, 吴淑芳,郭欢欢.前筒挤压成形方案分析与参数优化[J].西华大学学报:自然科学版,2019,38(3):32-42.
Wang P A,Wu S F,Guo H H. Analysis and parameter optimization of extrusion forming process of the front tube[J].Journal of Xihua University: Natural Science Edition,2019,38(3):32-42.
[9]吴淑芳, 王培安,郭欢欢,等.基于正交试验的梭心冷挤压成形工艺研究及模具优化设计[J].西华大学学报: 自然科学版, 2018, 37(1):92-101．
Wu S F,Wang P A,Guo H H, et al. Bobbin cold extrusion forming process and mold optimum design based on orthogonal test[J]. Journal of Xihua University: Natural Science Edition, 2018,37(1):92-101.
[10]施渊吉, 黎军顽,吴晓春,等.汽车法兰盘热锻模具磨损失效的实验分析和数值研究[J].摩擦学学报,2016,36(2):215-225.
Shi Y J, Li J W, Wu X C, et al. Experimental and numerical study on the wear failure of hot forging die of automobile flange[J]. Tribology, 2016,36(2):215-225.
[11]Cui X H, Wang S Q, Wei M X, et al. Wear characteristics and mechanisms of H13 steel with various tempered structures[J]. Journal of Materials Engineering and Performance, 2011,20(6):1055-1062.
[12]陆元三, 李颖颖,王培安.基于Archard理论对变速叉预锻凹模寿命分析[J].锻压技术,2020,45(8):164-169.
Lu Y S, Li Y Y, Wang P A. Life analysis of pre-forging die for shifting fork based on Archard theory[J]. Forging & Stamping Technology,2020,45(8):164-169.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】