淬火态2219铝合金板材加热翻边工艺
英文标题:Heating flanging process for quenched state 2219 aluminum alloy sheets
作者:张下陆1 郭慧2 赵鸿飞1 毕海娟1 龚立林1 
单位:1. 天津航天长征火箭制造有限公司 2. 北京航天动力研究所 
关键词:2219铝合金 淬火态 圆孔翻边 加热温度 力学性能 
分类号:TG146.1
出版年,卷(期):页码:2021,46(10):136-140
摘要:

 为了研究温度对淬火态2219铝合金板材圆孔翻边工艺的影响,在25~300 ℃温度范围内,对淬火态2219铝合金板材进行热拉伸试验以研究其在不同温度下的力学性能变化,并根据热拉伸试验结果进行加热状态下的圆孔翻边试验。结果表明:对于淬火态2219铝合金板材,加热可以提高其塑性,加热至150 ℃时伸长率达到40%以上,随着温度的升高,其伸长率继续提高,但超过200 ℃时,随着温度升高,其伸长率略有降低;与室温(25 ℃)状态下圆孔翻边相比,加热可以显著提高淬火态2219铝合金板材的圆孔翻边成形性能,当温度在170~180 ℃范围时,可以一次完成翻边圆孔的成形,且加热并不影响产品的最终力学性能。

 In order to study the influence of temperature on the round hole flanging process for the quenched 2219 aluminum alloy sheet, the hot tensile tests of the quenched 2219 aluminum alloy sheet were performed in the temperatures range of 25-300 ℃ to study the change of its mechanical properties at different temperatures, and the round hole flanging test under the heating state was carried out according to the result of the hot tensile test. The results show that heating can improve the plasticity of the quenched 2219 aluminum alloy sheet, and the elongation reaches more than 40% when heated to 150 ℃. As the temperature increases, the elongation continues to increase, but when it exceeds 200 °C, the elongation decreases slightly as the temperature increases. Compared with the round hole flanging at room temperature (25 ℃) , heating can significantly improve the round hole flanging formability of the quenched 2219 aluminum alloy sheet, when the temperature is 170-180 ℃, the flanging round hole can be formed at one time, and heating does not affect the final mechanical properties of the product.

 
基金项目:
作者简介:
作者简介:张下陆(1985-),男,硕士,工程师 E-mail:zxl613@126.com
参考文献:

 [1]鄢东洋, 郭彦明, 董曼红. 贮箱结构用2A14和2219铝合金的特性研究与分析[J]. 导弹与航天运载技术, 2019, 3: 102-107.


Yan D Y, Guo Y M, Dong M H. Analysis and discuss on the characteristics of 2A14 and 2219 aluminum alloy used in the rocket tank [J]. Missiles and Space Vehicles, 2019, 3: 102-107.

[2]姚君山, 周万盛,王国庆,等.航天贮箱结构材料及其焊接技术的发展[J].航天制造技术,2002,10(5):17-22.

Yao J S, Zhou W S, Wang G Q, et al. The development of materials and welding technology of the tank[J].Aerospace Manufacturing Technology, 2002, 10(5): 17-22.

[3]李寿萱. 钣金成形原理与工艺[M].西安:西北工业大学出版社,1985.

Li S X. Principle and Process of Sheet Metal Forming[M]. Xi′an: Northwestern Polytechnical University Press,1985.

[4]徐勇, 靳鹏飞, 田亚强. 铝合金局部热处理技术及其在板材成形中的应用发展现状[J].材料工程, 2018,5(46):44-55.

Xu Y, Jin P F, Tian Y Q. Development status of tailored heat treatment technology and its application on sheet metal forming of aluminum alloys[J]. Journal of Materials Engineering, 2018, 5(46): 44-55.

[5]郭亮, 湛利华. 6061-T6铝合金板材热冲压成形极限图研究[J]. 热加工工艺, 2017,(5): 131-134.

Guo L, Zhan L H. Study on forming limit diagram of hot stamping of 6061-T6 aluminum alloy sheet[J]. Hot Working Technology, 2017,(5): 131-134.

[6]刘俊伟. Mg-Al-Zn系合金板材中低温变形研究[D].长沙: 湖南大学, 2009.

Liu J W. Deformation Characteristics of Mg-Al-Zn Magnesium Alloy Sheets in Moderate Temperatures [D]. Changsha: Hunan University, 2009.

[7]张文忠, 陈浩,董占国,等.基于磁脉冲技术的铝合金板材圆孔翻边工艺研究[J].航天制造技术,2009,8(4):5-7.

Zhang W Z, Chen H, Dong Z G, et al. Research on formability of aluminum alloy flanged hole by EMF[J]. Aerospace Manufacturing Technology, 2009, 8(4):5-7.

[8]刘合军, 郎利辉, 李涛. 铝合金板材温热成形性能[J]. 塑性工程学报, 2009, 16(3): 145-148.

Liu H J, Lang L H, Li T. Investigation of formability of aluminum alloy sheet at elevated temperature [J]. Journal of Plasticity Engineering, 2009, 16(3): 145-148.

[9]Li D M, Ghosh A K. Biaxial warm forming behavior of aluminum sheet alloys[J]. Journal of Materials Processing Technology, 2004, 145(3):281-293.

[10]Finch D M, Wilson S P, Dorn J E . Deep drawing aluminum alloy at elevated temperatures:Part I [J]. Deep Drawing Cylindrical Cups. Transaction ASM, 1946, (36): 254-289.

[11]Finch D M, Wilson S P, Dorn J E. Deep drawing aluminum alloy at elevated temperatures: Part Ⅱ [J]. Deep Drawing Boxes. Transaction ASM,1946,(36): 290-310.

[12]Bolt P J, Lamboo N A P M, Rozier P J C M. Feasibility of warm drawing of aluminum products [J]. Material Processing Technology, 2001,(115): 118-121.

[13]Ayres R A, Lanning H W, Taylor B. Warming forming the GM V-6 oil pan in aluminum, SAE Paper 780180 [J]. Society of Automotive Engineers, 1978: 702-706.
服务与反馈:
本网站尚未开通全文下载服务】【加入收藏
《锻压技术》编辑部版权所有

中国机械工业联合会主管 北京机电研究所有限公司 中国机械工程学会塑性工程分会主办
联系地址:北京市海淀区学清路18号 邮编:100083
电话:+86-010-82415085 传真:+86-010-62920652
E-mail: fst@263.net(稿件) dyjsjournal@163.com(广告)
京ICP备07007000号-9