锻压技术

钒钛微合金化对建筑用钢成形性能的影响

英文标题：Influence of vanadium titanium microalloying on formability for construction steel

作者：魏杰赵丽丽

分类号：TG132.25

出版年,卷(期):页码：2021,46(11):244-249

摘要：

在Q235建筑用钢中复合添加不同含量的合金元素钒和钛，并进行了准静态拉伸试验、杯突试验、扩孔试验以及显微组织分析。结果表明：复合添加适量的合金元素钒和钛，可以明显改善合金内部组织、提高合金拉伸性能、胀形成形性能和冲压成形性能。合金元素含量过低或过高，均不利于钢板试样获得理想的内部组织和成形性能。与不添加合金元素的Q235建筑用钢相比，当复合添加0.15%V和0.1%Ti时钢的抗拉强度增大了33 MPa、屈服强度增大了35 MPa、断后伸长率增大了2.3%、应变硬化指数增大了0.078、杯突值增大了2.2、扩孔率增大了26.1%。

The alloying elements of vanadium and titanium with different contents were added into construction steel Q235, and quasi-static tensile test, cupping test, hole reaming test and microstructure analysis were conducted. The results show that the microstructure, tensile property, bulging formability and stamping formability of the alloy are significantly improved by adding a proper amount of alloying elements of vanadium and titanium. However, too low or too high content of alloying elements is not conducive to obtaining ideal internal structure and formability of the steel plate samples. But, compared with the construction steel Q235 without adding alloying elements, when the steel is added with 0.15%V and 0.1%Ti, the tensile strength, yield strength, elongation after fracture, strain hardening index, cupping value and hole reaming rate of the steel are increased by 33 MPa, 35 MPa, 2.3%, 0.078, 2.2 and 26.1%, respectively.

基金项目：

河南省教育厅重点项目（ZJA06027）

作者简介：魏杰（1971-），男，学士，讲师，E-mail：xingmu104029@163.com

参考文献：

[1]张宏博, 马涛,曹玉鹏, 等.含钒钛钢研究现状及展望[J].铸造技术,2018,39(6):1384-1386,1394.

Zhang H B, Ma T, Cao Y P, et al. Research status and prospects of vanadiumtitanium steels[J]. Foundry Technology, 2018, 39(6): 1384-1386,1394.

[2]刘洋, 王新华,张开钧.含铌钒钛微合金化钢连铸板坯中心偏析的影响因素[J].北京科技大学学报,2007,29(9):896-900.

Liu Y, Wang X H, Zhang K J. Influencing factors on center segregation in continuously cast NbVTicontained microalloying slabs[J].Journal of University of Science and Technology Beijing,2007,29(9):896-900.

[3]马晓艺, 徐春,黄光杰.控轧控冷工艺对钒钛微合金高强钢碳氮化合物析出的影响[J].材料导报,2007,21(z2):484-486.

Ma X Y, Xu C, Huang G J. Effect of controlled rolling processing on pricipitation phase of VTi microalloyed steels [J].Materials Review,2007,21(z2):484-486.

[4]陈强. 攀钢钒钛磁铁矿冶炼脱硫探讨[J].世界科技研究与发展,2004,26(2):73-77.

Chen Q. Primary desulfurizing research of vanadiumtitanium magnetite in Panzhihua iron & steel company[J].World SciTech R & D, 2004,26(2):73-77.

[5]牛刚, 陈银莉,武会宾, 等.钒钛微合金化耐腐蚀弹簧钢连续冷却的相变规律[J].材料热处理学报,2016,37(4):155-160.

Niu G, Chen Y L, Wu H B, et al. Phase transformation rule of VTi microalloyed corrosion resistant spring steel during continuous cooling[J].Transactions of Materials and Heat Treatment,2016,37(4):155-160.

[6]张彦恒, 周海龙,喻林, 等.钒钛铁水冶炼提升废钢比的探索与实践[J].特殊钢,2018,39(5):21-23.

Zhang Y H, Zhou H L, Yu L, et al. Practice and exploration on raising scrap ration during steelmaking with VTi hot metal[J].Special Steel,2018,39(5):21-23.

[7]纪成美, 赵辉,陆建辉.钒钛铈共渗对热作模具钢性能的影响[J].钢铁钒钛,2017,38(6):59-63.

Ji C M, Zhao H, Lu J H. Effect of copermeation of vanadiumtitaniumcerium on properties of hot work die steel[J].Iron Steel Vanadium Titanium,2017,38(6):59-63.

[8]张斌. 热处理温度对钒钛改性汽车传动轴钢性能的影响[J].钢铁钒钛,2017,38(6):55-58,63.

Zhang B. Effect of heat treatment temperature on properties of vanadium and titanium modified automobile transmission shaft steel[J].Iron Steel Vanadium Titanium,2017,38(6):55-58,63.

[9]高强健, 魏国,姜鑫, 等.印尼钒钛矿对沙钢高炉渣流动性的影响[J].材料与冶金学报,2016,15(2):88-91.

Gao Q J, Wei G, Jiang X, et al. Effect of indonesia vanadium ilmenomagnetite on fluidity of blast furnace slag in Jiangsu Sha steel [J].Journal of Materials and Metallurgy,2016,15(2):88-91.

[10]Fang W, Zhang C, Gou F, et al. The effect of micro alloying elements (vanadium, titanium) additions on the austenite grain growth behavior in medium carbon steel containing nitrogen[J]. Materialwissenschaft and Werkstofftechnik, 2020, 15(2): 230-237.

[11]Gunduz S, Erden M A, Karabulut H, et al. The effect of vanadium and titanium on mechanical properties of microalloyed PM steel[J]. Powder Metallurgy and Metal Ceramics,2016, 55(5-6): 277-287.

[12]祝家祺, 谭谆礼,张敏,等. 钒和铬对贝氏体车轮钢回火组织与性能的影响[J]. 稀有金属,2020,44(9):957-966.

Zhu J Q, Tan Z L, Zhang M, et al. Microstructure and mechanical properties of tempered bainitic railway wheel steels with addition of V and Cr[J]. Chinese Journal of Rare Metals,2020,44(9):957-966.

服务与反馈：

【文章下载】【加入收藏】