不同冲压速度下箍带弯曲成形有限元模拟

英文标题：Finite element simulation on hoop belt bending under different stamping speeds

作者：佟政阳程思佳王虎军靳凯

分类号：TG115

出版年,卷(期):页码：2022,47(2):94-99

摘要：

针对围圆冲压成形中易发生卡箍折裂的现象，使用SolidWorks建模，利用ABAQUS进行仿真运算，分析不同冲压速度下，卡箍箍带弯曲成形后的应力、应变、厚度的分布情况。结果表明：在不同冲压速度下，卡箍箍带的应力、应变以及厚度的变化趋势大致相同，均在耳圆部分和最底部出现拉应力增大、应变集中以及厚度减小的现象，表明在此3处出现变形较大的现象；经过对不同冲压速度下的卡箍箍带进行模拟仿真，得出在100 mm·s-1的冲压速度下，卡箍箍带的应力、应变以及厚度的变化分布均相对均匀，且整个箍带的变形相对平稳。

Aiming at the phenomenon that the clamp hoop was prone to crack in the process of circular stamping, the calculated model was established by SolidWorks, and the simulation calculation was conducted by ABAQUS to analyze the distribution conditions of stress, strain and thickness for clamp hoop belt after bending under different stamping speeds. The results show that under different stamping speeds, the variation trends of stress, strain and thickness of the clamp hoop belt are roughly the same, and the phenomenons of tensile stress increasing, strain concentration and thickness decreasing all appear at the ear circle and the bottom, indicating that there is a large deformation in these three places. Through the simulation of the clamp hoop belt under different stamping speeds, it is concluded that under the stamping speed of 100 mm·s-1, the distributions of stress, strain and thickness change of the clamp hoop belt all are relatively uniform, and the deformation of the whole hoop belt is relatively stable.

基金项目：

国家重点研发计划（2017YFB0703301）

作者简介：佟政阳（1993-），男，学士，高级工程师,E-mail：tzy18895330913@163.com;通信作者：靳凯（1987-），男，博士，副教授,E-mail：jinkai@nuaa.edu.cn

参考文献：

[1]郑敏，张爽，吴超.国内外导管连接卡箍发展动态研究[J].航空标准化与质量，2010，（4）：15-21.

Zheng M, Zhang S, Wu C. Development trends of coupling clamps for pipes at home and abroad [J]. Aeronautic Standardization & Quality， 2010，（4）: 15-21.

[2]郑敏, 章怡宁,景绿路,等.国外新型带垫固定卡箍分析[J].航空标准化与质量,2009，(5):12-16，45.

Zheng M, Zhang Y N, Jing L L, et al. Analysis of new foreign gasketed fixed clamps [J]. Aeronautic Standardization & Quality,2009，(5):12-16，45.

[3]丁琪, 嵇佳佳,柯文敏,等.高温合金GH4169激光焊工艺研究[J].金属加工：热加工,2020，(12):23-26.

Ding Q, Ji J J, Ke W M, et al. Research on laser welding technology of superalloy GH4169 [J]. Metal Working,2020，(12):23-26.

[4]杨正东, 隋明丽,任超,等.基于飞机环控系统的高温卡箍优化设计与应用[J].航空标准化与质量,2018，(5):21-24，36.

Yang Z D, Sui M L, Ren C, et al.The optimization design and application of hot temperature clamp based on aircraft environmental control system [J]. Aeronautic Standardization & Quality,2018，(5):21-24，36.

[5]李荣之,曹征宽,欧红燕,等.固溶时效工艺对GH4169高温合金组织和性能的影响[J].四川冶金,2021,43(4):34-37.

Li R Z, Cao Z K, Ou H Y, et al. Effect of solution aging process on microstructure and properties of GH4169 superalloy[J]. Sichuan Metallurgy, 2021,43(4):34-37.

[6]朱绍荷. 铝合金柔性导管连接卡箍简介[J].航空标准化与质量,2004，(3):35-37.

Zhu S H. Brief introduction of aluminum alloy flexible conduit connection clamp[J]. Aviation Standardization and Quality,2004，(3):35-37.

[7]邢继刚. 铝合金板材冲压成形数值模拟及变压边力技术研究[D].长春：长春工业大学,2020.

Xing J G. Research on Numerical Simulation and Variable Blank Holder Force Technology of Aluminum Alloy Sheet Stamping [D]. Changchun：Changchun University of Technology,2020.

[8]居龙, 毛婷婷,李洪波,等.冲压速度对铝合金5182-O拉深性能的影响[J].中南大学学报：自然科学版,2016,47(8):2643-2649.

Ju L, Mao T T, Li H B, et al. Effects of forming speed on drawability of aluminum alloy 5182-O[J]. Journal of Central South University: Science and Technology,2016,47(8):2643-2649.

[9]宋润华, 秦海龙,毕中南,等.GH4169合金高温动态应变时效实验及模拟[J].哈尔滨工业大学学报,2020,52(12):21-26.

Song R H, Qin H L, Bi Z N, et al. Experimental and modeling investigations of high temperature DSA behaviour for GH4169 superalloy[J]. Journal of Harbin Institute of Technology,2020,52(12):21-26.

[10]谭海波, 孙亚利.热处理工艺对GH4169高温合金锻件组织与力学性能的影响[J/OL].热加工工艺,2022，(2):114-116，109[2022-02-21].https://doi.org/10.14158/j.cnki. 1001-3814.20193633.

Tan H B, Sun Y L. Effects of heat treatment process on microstructure and mechanical properties of GH4169 superalloy forgings [J/OL]. Hot Working Technology, 2022， (2): 114-116,109 [2022-02-21].https://doi.org/10.14158/j.cnki.1001-3814. 20193633.

[11]ASTM E8/E8M—2021，Standard Test Methods for Tensien Testing of Metallic Materials[S].

[12]GB/T 228.1—2010, 金属材料拉伸试验第1部分：室温试验方法[S].

GB/T 228.1—2010, Metallic materials—tensile testing—Part 1: Method of test at room temperature [S].

服务与反馈：

【文章下载】【加入收藏】