变形与预时效对建筑铝型材显微组织与性能的影响

英文标题：Influence of deformation and pre-aging on microstructure and properties for architectural aluminum profiles

作者：李建英姜奎罗志东张志嵩

分类号：TG146.1

出版年,卷(期):页码：2022,47(10):265-271

摘要：

采用金相显微镜、拉伸试验机、电化学工作站等手段，研究了变形和预时效对建筑用6061铝合金型材显微组织、硬度、拉伸性能和耐蚀性能的影响。结果表明：在传统的固溶和时效（G+S）处理工艺间增加变形和预时效可以缩短峰值硬度出现的时间，且硬度会有不同程度的提高；相较于G+S态6061铝合金，固溶+30%变形+时效（G+30%B+S）、固溶+60%变形+时效（G+60%B+S）和固溶+预时效+60%变形+时效（G+YS+60%B+S）态6061铝合金的抗拉强度和屈服强度均有不同程度的提高，断后伸长率有不同程度的减小，耐蚀性从高至低的顺序为G+60%B+S>G+30%B+S>G+YS+60%B+S；相同的时效时间下，电导率从小至大的顺序为G+60%B+S<G+30%B+S<G+YS+60%B+S<G+S。变形和预时效+变形有助于提高G+S态6061铝合金的硬度和强度，但预时效会降低G+60%B+S态6061铝合金的耐蚀性。

The influences of deformation and pre-aging on the microstructure, hardness, tensile properties and corrosion resistance of 6061 aluminum alloy profiles for construction were studied by means of metallographic microscope, tensile testing machine and electrochemical workstation. The results show that adding deformation and pre-aging between the traditional solution and aging (G+S) treatment processes can shorten the time of peak hardness appearance, and the hardness is improved to different degrees. Compared with 6061 aluminum alloy in G+S state, the tensile strength and yield strength of 6061 aluminum alloy in solid solution+30% deformation+aging (G+30% B+S), solid solution+60% deformation+aging (G+60% B +S) and solid solution+pre-aging+60% deformation+aging (G+YS+60% B+S) state are improved to varying degrees, and the elongation after fracture is decreased to varying degrees. The order of corrosion resistance from high to low is G+60% B+S > G+30% B+S>G+YS+60% B+S. Under the same aging time, the order of conductivity from small to large is G+60% B+S<G+30% B+S<G+YS+60% B+S<G+S. The deformation and pre-aging+deformation are helpful to improve the hardness and strength of 6061 aluminum alloy in G+S state, but the pre-aging reduces the corrosion resistance of 6061 aluminum alloy in G+60% B+S state.

基金项目：

国家自然科学基金资助项目（50978168）；吉林省自然科学基金资助项目（20170101252JC）

李建英（1982-），女，硕士，副教授，E-mail：115363115@qq.com

参考文献：

[1]陈洪根,刘月莉,张龙,等.建筑外窗用新型隔热铝合金型材的研究[J].建筑科学,2021,37(8):170-174, 210.

Chen H G, Liu Y L, Zhang L, et al. Study on new thermal barrier aluminum alloy profiles for building external windows [J]. Building Science, 2021, 37 (8): 170-174, 210.

[2]李国俊,白雪智,李碧聪,等.大型6061铝合金锥筒形件成形及组织与性能研究[J].锻压技术,2021, 46(9):216-223.

Li G J, Bai X Z, Li B C, et al. Research on forming, microstructure and properties of large-scale cone-cylinder part for 6061 aluminum alloy [J]. Forging & Stamping Technology, 2021, 46 (9): 216-223.

[3]吴璐,董万鹏,龚红英,等.铝合金的形变热处理研究进展[J].热加工工艺,2014,43(4):27-31.

Wu L, Dong W P, Gong H Y, et al. Research and progress of thermomechanical treatment of Al alloy [J]. Hot Working Technology, 2014, 43 (4): 27-31.

[4]曾凡宜, 左长兵,张海栋,等.变形-热处理流程对6082铝合金组织的影响[J].锻压技术,2021,46(9):204-211.

Zeng F Y, Zuo C B, Zhang H D, et al. Influence of deformation-heat treatment process on microstructure for 6082 aluminum alloy [J]. Forging & Stamping Technology, 2021, 46 (9): 204-211.

[5]袁珍贵,陈志国,李鸿娟,等.新型热机械处理调控Al-Zn-Mg-Cu合金微观组织与综合性能的机理[J].中国有色金属学报, 2021, 31(2): 280-288.

Yuan Z G, Chen Z G, Li H J, et al. Mechanism of novel thermomechanical treatment on microstructure and comprehensive properties of Al-Zn-Mg-Cu alloy [J]. The Chinese Journal of Nonferrous Metals, 2021, 31 (2): 280-288.

[6]李海,陈鹏,王芝秀,等.时效对固溶+冷轧7075铝合金力学性能和显微组织的影响[J].中国有色金属学报, 2018, 28(10): 1999-2008.

Li H, Chen P, Wang Z X, et al. Effect of aging on mechanical properties and microstructure of solution treated and cold-rolled 7075 Al alloy [J]. The Chinese Journal of Nonferrous Metals, 2018, 28 (10): 1999-2008.

[7]Ren J K, Chen Z G, Jing P, et al. An initial report on achieving high comprehensive performance in an Al-Mg-Si alloy via novel thermomechanical processing[J]. Journal of Alloys & Compounds, 2018, 764: 679-683.

[8]陈剑虹,李明娥,余江瑞,等.热处理工艺对6061铝合金显微组织及力学性能的影响[J].兰州理工大学学报,2010,36(2):15-17.

Chen J H, Li M E, Yu J R, et al. Influence of heat treatment on microstructure and mechanical properties of 6061 aluminum alloy [J]. Journal of Lanzhou University of Technology, 2010,36 (2): 15-17.

[9]张宜洛,黄丽平.6061铝合金模板的热处理与性能研究[J].热加工工艺,2022,51(4):111-115.

Zhang Y L, Huang L P. Study on heat treatment and properties of 6061 aluminum alloy formwork [J]. Hot Working Technology, 2022, 51 (4): 111-115.

[10]GB/T 228.1—2021, 金属材料拉伸试验第1部分: 室温试验方法[S].

GB/T 228.1—2021,Metallic materials—Tensile testing—Part 1:Method of test at room temperature [S].

[11]朱世安,李耀,项胜前,等.Al-5.87Zn-2.07Mg-2.42Cu合金形变热处理过程的组织与性能演变[J].湖南有色金属, 2018, 34(3): 42-46.

Zhu S A, Li Y, Xiang S Q, et al. Study on microstructures and mechanical properties of Al-5.87Zn-2.07Mg-2.42Cu alloy during final thermomechanical treatment [J]. Hunan Nonferrous Metals, 2018, 34 (3): 42-46.

[12]郝建强,杨刚,田佩瑶,等.6061铝合金盘件辗压成形材料流动规律及微观组织分布研究[J].锻压技术,2021,46(5):116-122.

Hao J Q, Yang G, Tian P Y, et al. Research on materials flow law and microstructure distribution on roll forming of 6061 aluminum alloy disk parts [J]. Forging & Stamping Technology, 2021,46 (5): 116-122.

[13]廖斌,曹玲飞,吴晓东,等.双级形变热处理工艺中7A55铝合金热变形行为及热加工图[J].有色金属工程, 2021,11(2):1-8.

Liao B, Cao L F, Wu X D, et al. Hot deformation behavior and processing map of 7A55 aluminum alloy in double thermo-mechanical treatment process [J]. Nonferrous Metals Engineering, 2021, 11 (2): 1-8.

[14]Scharifi E, Sajadifar S V, Moeini G, et al. Dynamic tensile deformation of high strength aluminum alloys processed following novel thermomechanical treatment strategies[J]. Advanced Engineering Materials, 2020, 22(8):193-198.

[15]Lin S P, Nie Z R, Huang H, et al. Annealing behavior of a modified 5083 aluminum alloy[J]. Materials & Design, 2010, 31(3): 1607-1612.

[16]杨洁,卢生,秦二丽.挤压与时效处理对建筑铝型材微观结构与力学性能的影响[J].锻压技术,2020,45(10):185-191.

Yang J, Lu S, Qin E L. Effect of extrusion and aging treatment on microstructure and mechanical properties of building aluminum profiles [J]. Forging & Stamping Technology, 2020,45 (10): 185-191.

[17]Hakem M, Lebaili S, Mathieu S, et al. Effect of microstructure and precipitation phenomena on the mechanical behavior of AA6061-T6 aluminum alloy weld[J]. The International Journal of Advanced Manufacturing Technology, 2019, 102: 2907-2918.

[18]仝洪伟,王浩霖,刘文义,等.预变形对预时效态AA7085铝合金板材组织和性能的影响[J].材料热处理学报,2014, 35(12): 49-55.

Tong H W, Wang H L, Liu W Y, et al. Effects of pre-strain on microstructure of pre-aged AA7085 aluminum alloy plate [J]. Transactions of Materials and Heat Treatment, 2014,35 (12): 49-55.

[19]Doan L C, Ohmori Y, Nakai K. Precipitation and dissolution reactions in a 6061 aluminum alloy[J]. Materials Transactions Jim, 2000, 41(2): 300-305.

[20]张景玉,许晓静,阮鸿雁,等.热机械处理对Al-10.78Zn-2.78Mg-2.59Cu-0.22Zr-0.047Sr铝合金固溶时效态组织及力学性能的影响[J]. 稀有金属材料与工程,2017,46(10):3033-3037.

Zhang J Y, Xu X J, Ruan H Y, et al. Effect of thermomechanical treatment on microstructure and mechanical property of solution-aged Al-10.78Zn-2.78Mg-2.59Cu-0.22Zr-0.047Sr aluminum alloy [J]. Rare Metal Materials and Engineering, 2017,46 (10): 3033-3037.

[21]孙大翔,董宇,叶凌英,等.形变热处理工艺对2519A铝合金动态变形行为的影响[J].材料工程, 2021,49(2):79-87.

Sun D X, Dong Y, Ye L Y, et al. Effect of thermo-mechanical treatments on dynamic deformation behaviors of 2519A aluminum alloy [J]. Journal of Materials Engineering, 2021,49 (2): 79-87.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】