多撞针超声波喷丸校形的工艺参数研究

英文标题：Research on process parameters of multi-pin ultrasonic shot peening sizing

分类号：TG668

出版年,卷(期):页码：2022,47(12):129-134

摘要：

为了提高超声波喷丸校形工艺的工作效率及可控性，以自研的65针超声波喷丸校形设备为研究对象，对其喷丸工艺参数展开了研究。通过正交试验法，分析了气体压力、撞针行程和超声波振幅对喷丸强度的影响规律。结果表明：Almen试片在气体压力为0.65 MPa、超声波振幅为25.6 μm、撞针行程为1 mm的条件下，得到的校形弧高的最大值为1.073 mm，即采用该组合获得的喷丸强度最大；另外，喷丸强度与超声波振幅及气体压力呈正相关，与撞针行程呈负相关；对薄壁件弯曲变形影响最大的工艺参数为超声波振幅，其次为撞针行程，影响最小的为气体压力。最后，通过搭建的检测系统研究了喷丸工艺参数对撞针冲击速度的影响规律，结果与正交试验的结果一致。

To improve the working efficiency and controllability of ultrasonic shot peening sizing process, the shot peening process parameters of the self-researched 65-pin ultrasonic shot peening sizing device were studied, and the influence laws of air pressure, firing pin stroke and ultrasonic amplitude on shot peening strength were analyzed by orthogonal test method. Results show that for Almen test piece, the maximum height of sizing arc obtained is 1.073 mm under the air pressure of 0.65 MPa,the ultrasonic amplitude of 25.6 μm and the firing pin stroke of 1 mm, and the maximum shot peening strength is obtained under this composition. In addition, the shot peening strength is positively correlated with the ultrasonic amplitude and the air pressure, and negatively correlated with the firing pin stroke. Furthermore, the process parameter that has the greatest impact on the bending deformation of thin-walled parts is ultrasonic amplitude, followed by the firing pin stroke, and the air pressure has the least impact. Finally, the influence laws of shot peening process parameters on impact velocity of firing pin are studied by the established detection system, and the results are consistent with that of orthogonal test.

基金项目：

宁波市“3315”创新团队(Y80929DL04);宁波市科技创新“2025”重大专项(2018B10059)

王志晖（1997-），男，硕士研究生 E-mail：18370266642@163.com 通信作者：赵夙（1981-），男，博士，研究员 E-mail：zhaosu@nimte.ac.cn

参考文献：

[1]郭超亚. 数控超声波喷丸校形工艺研究与预测模型建立[D]. 南京: 南京航空航天大学, 2014.

Guo C Y. Research on Numerical Control Ultrasonic Shot Peening Straightening Process and Prediction Model[D]. Nanjing：Nanjing University of Aeronautics and Astronautics,2014.

[2]Xue Y, Mcdowell D L, Horsten eyer M F, et al. Micro structure-based multistage modelin of aluminum alloy 7075-T651 [J]. Engineering Fracture mechanics, 2007, 74:2810-2823.

[3]门向南, 董锦亮, 黄振彪,等. 超声波喷丸技术在大型零件变形校正中的应用[J]. 热加工工艺, 2017,46(7):156-160.

Men X N, Dong J L, Huang Z B, et al.Application of ultrasonic shot peening technology in correction of large-scale parts deformation[J]. Hot Working Technology, 2017,46(7):156-160.

[4]杨辉, 徐刚,张炜,等.超声波喷丸技术在大型零件变形校正中的应用研究[J].现代制造技术与装备,2020,56(9):54-56.

Yang H, Xu G, Zhang W, et al. Application of ultrasonic shot peening technology in deformation correction of large parts[J]. Modern Manufacturing Technology and Equipment,2020,56(9):54-56.

[5]鲁世红, 朱一枫, 刘朝训,等.高能超声波喷丸成形与校形技术研究进展[J]. 航空制造技术, 2013, (11):45-47.

Lu S H, Zhu Y F, Liu C X, et al. Research progress of high energy ultrasonic peening forming and sizing technology[J].Aeronautical Manufacturing Technology, 2013, (11):45-47.

[6]刘峰, 鲁世红,张炜.超声波喷丸技术的研究进展[J].航空制造技术,2016,(14):24-28.

Liu F, Lu S H, Zhang W, Research progress of ultrasonic shot peening technology[J].Aeronautical Manufacturing Technology, 2016,(14):24-28.

[7]Friese A. One of the worlds largest shot peening machines installed at Airbus, 2004.

[8]闫琳琳. 超声喷丸技术及应用[J].制造技术与机床,2010,(6):29-31.

Yan L L. The technology and application of ultrasonic shot peening[J]. Manufacturing Technology & Machine Tool, 2010,(6):29-31.

[9]Ines Fernandez Pariente, Mario Guagliano. About the role of residual stresses and surface work hardening on fatigue △Kth of a nitride and shot penned low-alloy steel [J]. Surface & Coatings Technology, 2008,202(13):3072-3080.

[10]鲁世红, 成书民,刘朝训,等.基于有限元仿真的带孔板超声波喷丸成形工艺[J].中国表面工程, 2015, 28(2): 108-113.

Lu S H, Cheng S M, Liu C X, et al. Ultrasonic peening forming process in perforated plate based on finite element simulation[J]. China Surface Engineering, 2015,28(2):109-113.

[11]陈星. 超声波喷丸校形的应用研究[D]. 南京: 南京航空航天大学，2013.

Chen X. Research of Ultrasonic Shot Peening Technology in Straigthening [D]. Nanjing: Nanjing University of Aeronautics and Astronautics,2013.

[12]高琳. 高能超声波喷丸板料成形技术研究[D]. 南京:南京航空航天大学,2012.

Gao L. Research of High-energy Ultrasonic Shot Peening Technology in Sheet Metal Forming[D]. Nanjing: Nanjing University of Aeronautics and Astronautics, 2012.

[13]周圳, 鲁世红,张涛,等.铝合金弹性预应力超声喷丸成形试验[J].中国表面工程,2017,30(3):31-39.

Zhou Z, Lu S H, Zhang T, et al.Experimental study of elastic prestressed ultrasonic peen forming on aluminum alloy[J]. China Surface Engineering, 2017,30(3):31-39.

[14]王学深. 正交试验设计法[J]. 山西化工,1989, (3):53-58.

Wang X S. Orthogonal experimental design method[J].Shanxi Chemical Industry,1989, (3):53-58.

[15]Vijayakumar K. New look at kirchhoff's theory of plates[J]. AIAA Journal, 2009, 47(4) : 1045-1046.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】