小径厚比金属波纹管无模成形工艺

英文标题：Dieless forming process of metal bellows with small radius-to-thickness ratio

作者：张自成戴文龙童腾腾程琦文

单位：东北大学

分类号：TH306

出版年,卷(期):页码：2023,48(5):254-259

摘要：

传统成形工艺制备的波纹管存在过度减薄及性能恶化等问题，限制了其在航空航天领域的应用，利用局部加热和轴向压缩诱导管坯发生轴向屈曲从而成形的无模成形工艺制备波纹管。为了利用无模成形工艺获得径厚比较小、波纹均匀、综合性能良好的波纹管，采用试验与有限元模拟相结合的方法，对加热温度、变形区宽度、压缩比对成形载荷、波纹管波纹形状、波峰高度、波峰间距以及波峰厚度的影响规律进行了研究。研究结果表明：随着加热温度的升高，波纹管的成形载荷显著降低；随着变形区宽度的增加，波峰高度和波峰间距呈增加趋势，而波峰厚度呈减小趋势；随着压缩比的增加，波峰高度呈增加趋势，波峰间距呈减小趋势。

The excessive thinning and performance deterioration of bellows prepared by the traditional forming process limit the application of bellows in the aerospace field. Therefore, the bellows was fabricated by the dieless forming process that induced the axial buckling of tube blank by local heating and axial compression. Furthermore, in order to obtain the bellows with small radius-to-thickness ratio, uniform corrugation and good comprehensive performance by using dieless forming process, the influence laws of heating temperature, deformation zone width and compression ratio on forming load, corrugation shape of bellows, peak height，peak spacing and peak thickness were studied by combining experiment and finite element simulation. The research results show that with the increasing of heating temperature, the forming load of bellows decreases significantly. As the width of the deformation zone increaseing, the peak height and peak spacing tend to increase, while the peak thickness tends to decrease. With the increasing of compression ratio, the peak height tends to increase, and the peak spacing shows a decreasing trend.

基金项目：

辽宁省自然科学基金计划项目（2022-YGJC-77）；国家自然科学基金资助项目（51304046）

作者简介：张自成（1981-），男，博士，副教授,E-mail：zhangzicheng@me.neu.edu.cn

参考文献：

[1]吉慧琴. 浅谈军民两用波纹管的成形 [J]. 工程与试验, 2019, 59(3): 105-107.

Ji H Q. Discussion on the forming of military and civilian dual-purpose bellows [J]. Engineering & Test, 2019, 59(3): 105-107.

[2]刘锁. 波纹管补偿器失效原因及可靠性探究 [J]. 科学技术创新, 2020, (13): 173-174.

Liu S. Investigation on the failure causes and reliability of bellows compensator [J]. Scientific and Technological Innovation, 2020, (13): 173-174.

[3]杨慧毅, 钟玉平, 张小文. 波纹管动力学分析研究进展 [J]. 材料开发与应用, 2020, 35(1): 91-95，100.

Yang H Y, Zhong Y P, Zhang X W. Development of dynamic analysis of bellows [J]. Development and Application of Materials, 2020, 35(1): 91-95，100.

[4]张益明, 余凌, 吴泽日. 国内波纹管加工发展及其特点 [J]. 中国金属通报, 2019, (5): 102-103.

Zhang Y M, Yu L, Wu Z R. Domestic bellows processing development and its characteristics [J]. China Metal Bulletin, 2019, (5): 102-103.

[5]Kumar Krovvidi S C S P, Goyal S, Bhaduri A K. Design, analysis and experimental validation of Inconel-625 bellows for critical applications [J]. Materials Today: Proceedings, 2021, 39: 1733-1737.

[6]Gomes da Silva M J, Fragoso H A P, Barrio R C A G, et al. Stress corrosion of an austenitic stainless steel expansion joint, a case study [J]. Engineering Failure Analysis, 2019, 97: 300-310.

[7]李江洋, 王伟霞. 汽车进气波纹管隔振研究 [J]. 北京汽车, 2020, (5): 28-30.

Li J Y, Wang W X. Research on vibration isolation of automobile intake bellows [J]. Beijing Automotive Engineering, 2020, (5): 28-30.

[8]唐冬. 波纹管膨胀节在高炉煤气系统中的腐蚀失效分析 [J]. 中国设备工程, 2020, (19): 133-135.

Tang D. Corrosion failure analysis of bellows expansion joints in blast furnace gas system [J]. China Plant Engineering, 2020, (19): 133-135.

[9]刘小华. 换热器波纹管使用缺陷及解决方法 [J]. 现代农机, 2020, (4): 57-58.

Liu X H. Heat exchanger bellows use defects and solutions [J]. Modern Agricultural Machinery, 2020, (4): 57-58.

[10]张丽君, 李彦男, 底柯, 等. 某船用柴油机排气波纹管故障分析与改进 [J]. 柴油机, 2020, 42(3): 25-29.

Zhang L J, Li Y N, Di K, et al. Failure analysis and design improvements on exhaust bellow of a marine diesel engine [J]. Diesel Engine, 2020, 42(3): 25-29.

[11]Lee S W. Study on the forming parameters of the metal bellows [J]. Journal of Materials Processing Technology, 2002, 130-131: 47-53.

[12]Liu J, Lyu Z Y, Liu Y, et al. Deformation behaviors of four-layered U-shaped metallic bellows in hydroforming [J]. Chinese Journal of Aeronautics, 2020，33（12）：3479-3494.

[13]Kang B H, Lee M Y, Shon S M, et al. Forming various shapes of tubular bellows using a single-step hydroforming process [J]. Journal of Materials Processing Technology, 2007, 194(1-3): 1-6.

[14]郭煜敬, 王志刚, 金光耀, 等. 液压成形波纹管减薄率的数值模拟研究 [J]. 浙江工业大学学报, 2019, 47(1): 58-62.

Guo Y J, Wang Z G, Jin G Y, et al. Numerical simulation research on thickness reduction ratio of the bellows [J]. Journal of Zhejiang University of Technology, 2019, 47(1): 58-62.

[15]Jiang L F, He Y, Lin Y C，et al. Influence of process parameters on thinning ratio and fittability of bellows hydroforming [J]. International Journal of Advanced Manufacturing Technology, 2020, 107(7-8): 3371-3387.

[16]Pavithra E, Kumar V S S. Experimental investigation and numerical analysis on fatigue life of bellows [J]. Material Today: Proceedings, 2018, 5(9): 18848-18856.

[17]全琼蕊, 陈基东, 谢善, 等. 某发动机波纹管组件裂纹原因分析 [J]. 热加工工艺, 2019, 48(24): 178-182.

Quan Q R, Chen J D, Xie S, et al. Analysis on reasons for cracks in bellow component [J]. Hot Working Technology, 2019, 48(24): 178-182.

[18]Sun E, Wang T, Zhu S Q. An experimental study of bellows-type fluidic soft bending actuators under external water pressure [J]. Smart Materials and Structures, 2020, 29(8): 087005.

[19]Zhang Z C, Furushima T, Manabe K I, et al. Development of dieless metal bellows forming process with local heating technique [J]. Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture, 2014, 229(4): 664-669.

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】