Title:Experimental comparative analysis for influence of punch speed on bulging performance of DP780 dual phase steel and 304 stainless steel
Authors: Cheng Lingxia  Cao Yanggen  Deng Peiran  Su Yu 
Unit: Shanghai University of Engineering Science 
KeyWords: punch speed cupping test bulging performance 
ClassificationCode:TG386.1
year,vol(issue):pagenumber:2015,40(2):145-147
Abstract:
The cupping tests of 1 mm sheet metal for dual phase steel DP780 and 304 stainless steel were carried out using Komatsu servo press with controlled speed. The influence of punch speed on the test results was studied based on the test Er value (Erichsen value)obtained from the cupping test. Comparing the test result of DP780 dual phase steel to the one of 304 stainless steel, it is found that when the punch speed increases from 3 mm·s-1 to 30 mm·s-1 during the process, the Er value of 304 stainless steel reduces from 9.39 mm to 8.59 mm, and the Er value of dual phase steel decreases from 7.53 mm to 7.39 mm. Therefore, the influence of punch speed on the bulging performance of material is confirmed by the results above, that is,the Er value and resistance to rupture of material reduce gradually with the increasing punch speed within 3-30 mm·s-1, which means that bulge forming performance of material decreases.
Funds:
国家自然科学基金资助项目(051301105)
AuthorIntro:
程令霞(1987-),女,硕士研究生
Reference:


[1]陶友瑞,张福全,张辉.金属板料拉胀成形工艺的进展[J]. 湖南工程学院学报,2003,13(2): 53-56. Tao Y R, Zhang F Q, Zhang H. Technological progress in sheet metal stamping [J]. Journal of Hunan College of Engineering, 2003,13(2):53-56.
[2]董丹阳,刘杨,王磊,等. 应变速率对DP780钢动态拉伸变形行为的影响[J]. 金属学报, 2013,49(2): 159-166.Dong D Y, Liu Y, Wang L, et al. Effect of strain rate on dynamic deformation behavior of DP780 steel [J]. Acta Metallurgica Sinica, 2013, 49(2):159-166.
[3]郑延福,付全科,荀建民.影响杯突试验数据的因素分析[J]. 理化检验-物理分册, 2004,40(9): 446-447.Zheng Y F, Fu Q K, Xun J M. Analysis of the influence factors for Erichsen testing [J]. Physical Testing and Chemical Analysis, Part A: Physical Testing, 2004,40(9):446-447.
[4]GB/T 4156-2007, 金属板料薄板和薄带埃里克森杯突试验[S].GB/T 4156-2007, Metallic materials-Sheet and strip-Erichsen cupping test[S].
[5]李伟锋,乔明杰.杯突试验测定板料成形极限图的试验研究[J].锻压技术,2010,35(6):63-65.Li W F,Qiao M J. Experimental study on determinating forming limit diagram of sheet metal with cupping test method [J]. Forging & Stamping Technology, 2010,35 (6):63-65.
[6]许淳淳,张新生,胡钢.拉伸变形对304不锈钢应力腐蚀的影响[J].材料研究学报,2003,17(3):310-314.Xu C C, Zhang X S, Hu G. Influence of drawing deformation on stress corrosion cracking of 304 stainless steel[J]. Chinese Journal of Materials Research, 2003, 17(3):310-314.
[7]申勇峰,李晓旭,薛文颖,等.304不锈钢在拉伸变形过程中的马氏体相变[J].东北大学学报,2012,33(8):1125-1128.Shen Y F, Li X X, Xue W Y,et al. Changes in martensite fraction of 304SS in tensile deformation [J].Journal of Northeastern University, 2012, 33(8):1125-1128.
[8]田成达,李大永,彭颖红,等. DP780高强钢板动态变形力学行为研究[J].塑性工程学报,2008,15(16):102-106.Tian C D, Li D Y, Peng Y H. Research on the dynamic deformation behavior of the DP780 advanced high strength steel[J].Journal of Plasticity Engineering, 2008,15(16): 102-106.
[9]魏恒,郑少波,王淼,等. 影响低碳钢屈强比的显微因素[J].上海金属,2012,34(2):19-22.Wei H, Zheng S B, Wang M, et al. Effects of microstructure factor on yield ratio of low carbon steel[J]. Shanghai Metals, 2012, 34(2):19-22.

Service:
This site has not yet opened Download Service】【Add Favorite
Copyright Forging & Stamping Technology.All rights reserved
 Sponsored by: Beijing Research Institute of Mechanical and Electrical Technology; Society for Technology of Plasticity, CMES
Tel: +86-010-62920652 +86-010-82415085     Fax:+86-010-62920652
Address: No.18 Xueqing Road, Beijing 100083, P. R. China
 E-mail: fst@263.net    dyjsgg@163.com