摘要：
|
|
气门热精锻模具失效的主要形式是热磨损和压塌。 0 1 2 Al钢(5 Cr4Mo3Si Mn VAl)的室温及高温的硬度、磨损抗力、屈服强度和热稳定性 ,以及氮化能力比 3Cr2 W8V较高 ,因此用 0 1 2 Al钢替代传统应用的 3Cr2 W8V钢在理论上是合理的。再者 ,由于气门热精锻模具甚少因断裂失效 ,而且 0 1 2 Al钢比 3Cr2 W8V钢有较高的韧性 ,因而可以较大地提高 0 1 2 Al钢的淬火温度 (约 5 0℃ ) ,适当地降低加火温度 (约 30℃ ) ,在保证有足够韧性前提下 ,提高模具的室温及高温的硬度、磨损抗力、屈服强度和热稳定性 ,以提高模具寿命。生产试验表明 ,0 1 2 Al钢制气门热精锻模具的工作寿命是 3Cr2 W8V钢的 1 .8～ 2 .2倍。
|
|
The main failure mode of the finish hot- forging dies for Valves are the hot wear of col- lapse.The hardness,yield strength,Wear resistance at the room and the high temperature,and the ther- mal stability ,the nitrided capabitity of 0 12 Al steel ( 5Cr4 Mo3Si Mn VAl) are better than that of 3Cr2 W8V steel,so in theory the dies made of0 12 Al steel could have a longer service life than the con- ventional3Cr2 W8V Steel.Because the dies were hardly cracken of fractured itwould be possible in theo- ry to lengthen the die service life by means of increasing the hardness,yield strength,wear resistance at the room and high temperature,and the thermal stability of the dies made of0 12 Al steel,For this rea- son,We will raise the quanching temperature about50℃ and decrease the tempering temperature about 30℃ during die heat treatment.The production tests shown that the die service life of0 12 Al steel was 1.8～ 2 .2 times of3Cr2 W8V steel.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
1 冯晓曾等 .模具用钢和热处理 .北京 :机械工业出版 ,1984.
2 贵阳钢厂 .新模具钢 0 12 Al研制工作总结 ,中国金属学会第一届特殊钢年会论文 ,1983.
3 陈蕴博等 .热作模具钢的选择与应用 .北京 :国防工业出版社 ,1993.
4 冯晓曾 .热冲头模具的失效机制和强韧性处理 .中国机械工程学会热处理学会第四届年会论文论 ,1987.
5 郭俊杰 .提高 3Cr2 W8V钢的热穿孔冲头寿命的热处理工艺 .金属热处理 ,1990 (8) .
6 [美 ]J C Benedyk,王德文译 .金属热处理 (增刊 ) ,1985 .
7 崔鸿璞 .4Cr5 Mo Si Vl钢热挤压模具热处理研究 .大型铸锻件 ,1991(1- 2 ) .
8 张荣祥 .H13钢挤压轴热处理工艺探讨 .四省市热处理学术协作网第四届学术信息交流会议论文集 ,1994.
9 朱心昆 .淬火温度对 H12钢性能的影响 .金属热处理 ,1994(8) :2 8～ 30
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|