硅线石颗粒／LY12搅融混合后半固态挤压成形件组织与性能研究

英文标题：Research on microstructure and properties of particulate reinforced sillimanite / LY12composite manufactured by semi-solid extrusion from stired mixture

作者：罗守胡连喜张磊霍文灿

单位：哈尔滨工业大学

关键词：硅线石颗粒铝合金半固态挤压组织性能

分类号：TG146.21

出版年,卷(期):页码：1996,21(2):0-0

摘要：

采用搅融混合并半固态挤压成形后，使硅线石颗粒与基体ＬＹ１２复合。试验测定结果表明，半固态挤压得到的复合材料制件组织为变形后的再结晶组织，有良好的力学性能和低的热膨胀系数，为硅线石增强铝基复合材料研究和应用奠定了基础。

Semi-solid extrusion of the stired sillimanite particulate / LY12 mixture was performed to form the particulate-reinforced sillimanite/ LY12 Composite. Experimental investigation including the testing of the mechanical properties and the thermal expansion coefficient of the composite and the observation of the microsturcture was carried out. It was revealed that the microstructure of the composite is deformation-induced recrystallization microstructure and that the composite possesses good mechanical properties and low coefficient of thermal expansion. This provides a basis for further study and application of the sillimanite reinforced aluminium matrix composites.

基金项目：

黑龙江省自然科学基金

参考文献：

1赖宝衡．液态模锻模具硅线五材料的研究。哈尔滨工业大学硕士学位论文，1990．2蒋鹏．硅线石烧结材料的研究及在液态模锻模具中的应用．哈尔滨工业大学硕士学位论文，1992．3王文旭．硅线石莫来化材料的研制及其在液态模锻模具中的应用，哈尔滨工业大学硕士学位论文，1994．4王祝堂，田荣璋主编．铝合金及其加工手册．长沙：中南工业大学出版社，1989．5张磊．硅线五颗粒／LY12复合材料搅融混合及半固态挤压的研究。哈尔滨工业大学硕士学位论文，19956苏云卿，硅酸铝质耐火材料．北京：冶金工业出版社，19887吕炎，锻件组织分析．北京：国防工业出版社，1988．

服务与反馈：

【本网站尚未开通全文下载服务】【加入收藏】