稀土铈对45Cr2NiMoVSi热锻模具钢力学性能的影响
|
|
英文标题：Effect of rare earth cerium on mechanical property of 45Cr2NiMoVSi hot-forged die steel |
|
作者：李密文 郝新 |
|
单位：内蒙古工业大学材料科学与工程学院 |
|
关键词：模具钢 铈 强度 硬度 塑性 冲击韧性 |
|
分类号：TG316 |
|
出版年,卷(期):页码：2009,34(1):100-103 |
|
摘要：
|
|
研究了稀土Ce对45Cr2NiMoVSi热锻模具钢强度、硬度、塑性和冲击韧性的影响,并在相同的热处理工艺条件下,分别加入5种不同含量Ce后与不添加Ce的45Cr2NiMoVSi钢的力学性能进行对比。结果表明:Ce添加量在适当的范围内可显著提高45Cr2NiMoVSi的强度、硬度、塑性和冲击韧性,并且当Ce添加量为0.22%时,45Cr2NiMoVSi钢可获得最好的综合力学性能。
|
|
Effect of RE cerium on strength,hardness,plasticity and impact ductility of 45Cr2NiMoVSi hot die steel was studied.The mechanical properties of 45Cr2NiMoVSi steel with five different contents of RE cerium were compared with those of the 45Cr2NiMoVSi steel without RE cerium under the same heat treatment process.The result shows that strength,hardness,plasticity and impact ductility of 45Cr2NiMoVSi steel are improved greatly if the content of RE cerium is proper.And when the content of RE cerium is 0.22%(mass percent),the 45Cr2NiMoVSi steel has the best mechanical property.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈再枝.模具钢手册[M].北京:冶金工业出版社,2002.
[2]姜锡山.特殊钢缺陷分析与对策[M].北京:化学工业出版社,2006.
[3]方健儒,姜启川,韩增祥,等.热作模具钢的高温热机械疲劳寿命预测[J].机械强度,2002,24(4):571-574.
[4]黄小云.几种国产新型热作模具钢的力学性能与应用[J].机械工程材料,1997,21(5):49-51.
[5]陈列,佐辉.3Cr2W8V热作模具钢的稀土合金处理[J].特殊钢,2005,26(5):51-53.
[6]余宗森.稀土在钢铁中的应用[M].北京:冶金工业出版社,1987.
[7]陈岁元,江自应.稀土在钢铁中的作用与机理研究[J].云南冶金,1998,27(3):2-4.
[8]王龙妹,杜挺.微量稀土元素在钢中的作用机理及应用研究[J].稀土,2001,22(4):38-40.
[9]杜挺.稀土元素在金属材料中的一些物理化学作用[J].金属学报,1997,33(1):74-76.
[10]徐光宪.稀土[M].北京:冶金工业出版社,2001.
|
|
服务与反馈：
|
|
【文章下载】【加入收藏】
|
|
|
|