摘要：
|
|
对IN718合金进行近等温锻造实验。结果表明:近等温锻造IN718合金微观组织和拉伸性能对温度场敏感,对变形量和应变速率不敏感,有利于IN718合金近等温加工成形。当成形温度较低时(980℃),晶粒细小,间隙相以短棒状析出,分散程度高,塑性性能高,但是屈服强度低;当成形温度较高时(1060℃),晶粒粗大,仅在晶界处有间隙相以针状析出,塑性性能较低,但是屈服强度好转;在1020℃近等温锻造IN718合金,晶粒细小,短棒状间隙相在晶内析出、针状间隙相在晶界处析出,拉伸性能优越,针状间隙相对屈服强度贡献显著。
|
|
Near isothermal forging holding in homogeneous temperature pattern from specimen to die was proposed for the economic production of complex-shaped components.The results indicate that microstructure and tensile properties are sensitive to the temperature pattern,and low sensitization of microstructure and tensile properties to deformation and strain rate is benefit to NIF of IN718 alloy.Fine microstructure and stick interstitial phase at high dispersion processed contribute to the excellent plasticity under SIF at low temperature(at 980℃).Coarse microstructure with interstitial phase precipitated as acerose in boundaries improves the yield strength obviously processed under SIF at high temperature(at 1060℃).Tensile properties of the IN718 alloy processed under NIF at 1020℃and heat treated condition are significantly improved with grain size ASTM 10.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]刘谋佶,吴泽,姚泽坤,等.700~800℃温度下GH4169合金组织演化和力学性能研究[J].锻压技术,2007,32(2):90-93.
[2]Cao W D,Kennedy R L.New deveiopments in wrought 718-type superalloys[J].Acta Metallurgica Sinica,2005,18(1):39-46.
[3]Ning Yongquan,Yao Zekun,Guo Hongzhen,et al.Ultra-fine-grained treatment process of FGH4096 alloy[J].KeyEngineering Materials,2009,(407-408):694-697.
[4]宁永权,姚择坤,吴泽,等.多火次锻造对GH4133A合金组织和性能的影响[J].塑性工程学报,2008,15(4):98-101.
[5]吕宏军,姚草根,张凯峰,等.GH4169合金细晶成形工艺与机理及其性能研究[J].机械工程材料,2003,27(1):15-18.
[6]Hongjun Lu,Xinchao Jia,Kaifeng Zhang.Fine-grainedpretreatment process and superplasticity for INCONEL718superalloy[J].Materials Science and Engineering A,2002,326,382-385.
[7]郭鸿镇,姚泽坤.合金钢与有色合金锻造[M].西安:西北工业大学出版社,1999.
[8]蔡玉林,郑运荣.高温合金的金相研究[M].北京:国防工业出版社,1986.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|