不同热轧工艺条件下镀锡板表面氧化铁皮分析
|
|
英文标题：Analysis of scale microstructure on tinplate strip with different hot rolling processes |
|
作者：王银军 |
|
单位：上海梅山钢铁公司技术中心 |
|
关键词：热轧 镀锡板 氧化铁皮 |
|
分类号：TG335.11 |
|
出版年,卷(期):页码：2008,33(4):57-59 |
|
摘要：
|
|
对不同热轧生产工艺条件的镀锡板表面氧化铁皮进行了对比试验。结果表明:由于热轧装备条件的改善,所生产的热轧镀锡板,其表面氧化铁皮厚度由原来的6~13μm减薄至4~7μm,酸洗性能也明显提高;与MR-2相比,由于MR-3在CT 680℃高温卷取,MR-3氧化铁皮厚度较厚,氧化铁皮相变反应析出更强烈,析出的Fe3O4-Fe共晶组织明显增多;粗轧出口温度RT 1010~969℃,进行较低温度轧制时,随着轧制温度的降低,氧化铁皮厚度略有减薄。
|
|
Effects of different hot rolling processes on tinplate strip surface scale microstructure were investigated.The results indicate that the thickness of the surface oxided scale is reduced from 6-13 μm to 4-7 μm for the improvement of rolling mill and the pickling quality of the strip is improved;compared MR-3 with MR-2,the MR-3 tinplate strip is coiled with the higher coiling temperature of CT 680 ℃,the thickness of the MR-3 scale is thicker,and more mixtures of Fe3O4-Fe eutectoid are formed in MR-3 scale;with lower rolling temperature,such as the finishing rough rolling temperature of RT 1010-969 ℃,the thinner scale is formed when the temperature is being reduced.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]杨荃,卿伟杰.镀锡板轧制工艺和质量控制技术研究[J].轧钢,2000,17(4):17-20.
[2]卢笙.镀锡板性能影响因素的分析[J].宝钢技术,2004,(5):57-60.
[3]傅作宝.冷轧薄板生产[M].北京:冶金工业出版社,1996.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|