2618铝合金等温成形工艺热模拟试验研究
|
|
英文标题：Research on thermal simulation experiment of isothermal forming process for 2618 Al-alloy |
|
作者：李柏茹 张鹤 陈洪玉 |
|
单位：黑龙江科技学院材料科学与工程学院 |
|
关键词：2618铝合金 等温成形 热模拟 正交试验 |
|
分类号：TG316 |
|
出版年,卷(期):页码：2008,33(5):20-23 |
|
摘要：
|
|
利用Gleeble-1500型热/力模拟试验机模拟2618铝合金等温成形工艺,采用正交试验法研究工艺参数(变形温度T、应变速率.ε和变形程度ε)对晶粒尺寸的影响,确定了最佳工艺参数为:T=430℃,.ε=8×10-3s-1,ε=40%。利用此工艺参数对2618铝合金进行等温成形,金相试验表明获得的锻件晶粒细小、均匀。
|
|
The isothermal forming process of 2618 Al-alloy was simulated on the Gleeble-1500 thermal-mechanical simulator.The influence of the processing parameters(deformation temperature T,strain rate ε and deformation degree ε) on grain sizes was studied by the orthogonal test,and the optimal processing parameters,T=430 ℃,ε=8×10-3 s-1 and ε=40%,were determined,which were used to carry out isothermal forming.The microscopic examination indicates that the grain sizes of obtained forging are fine and uniform.
|
|
基金项目：
|
|
黑龙江省教育厅(指导)项目(10543037)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]黄光胜,汪凌云,陈华,等.2618铝合金的热变形和加工图[J].中国有色金属学报,2005,15(5):763-763.
[2]赵静,郭鸿镇,姚泽坤.等温压缩工艺对1933铝合金组织性能的影响[J].航空制造技术,2007,(7):82-82.
[3]张宝昌.有色金属及热处理[M].西安:西北工业大学出版社,1992.
[4]刘晓晶,刘润广,姜国栋.2618铝合金后摇臂等温体积成型工艺的研究[J].金属成型工艺,2000,18(3):44-44.
[5]牛济泰.材料和热加工领域的物理模拟技术[M].北京:国防工业出版社,1999.
[6]王祥生.铸造实验技术[M].南京:东南大学出版社,1990.
[7]张成军,纪朝辉,董广强.实验设计与数据处理及其应用[M].哈尔滨:哈尔滨工业大学出版社,2000.
[8]Oguocha INA,Yannacopohs S.Natural aging behavior ofcast aluminum particular reinforced 2618 aluminum alloy[J].J.Master.Sci.,1996,31:3145-3151.
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|