摘要：
|
|
整体锻造挤压辊是整个辊压机的关键部件,形状短粗,是大型粗短轴类零件的代表,锻透性较差;空洞型缺陷是造成产品合格率低的一个重要因素,必须消除。本文利用Deform-3D模拟软件,对两次镦拔新工艺应用于RP170-110挤压辊的第1次镦拔过程进行了理论验证。通过对镦粗后采用WHF法和FM法拔长过程的数值模拟结果进行对比,说明两次镦拔新工艺中的第1次镦拔工艺—镦粗+WHF法拔长能够在足够大的三向压应力状态下,在再结晶温度以上愈合孔洞型缺陷,提高了大型短粗轴类锻件的锻透性。8件锻件全部试制合格的结果也证明了两次镦拔新工艺第1次镦拔的合理性。
|
|
Squeeze roll of large podgy shape forged by whole forging process is a key part of roller press,which shape is short & crude and forging penetration effect is worse.Voids,an important factor resulting in eligibility rate lower, must be avoided.Using the simulation software Deform-3D,the first process of the two times upsetting and stretching was validated theoretically used in forging RP170-110 squeeze roll.Simulation results of WHF-stretching and FM- stretching after upsetting show that using the first of the two times upsetting and stretching—upsetting+WHF-stretc- hing,the enough compression stress appeared not only eliminate most voids at recrystallization temperature,but also obtain better forging penetration.Eight trial products are all up to the grade also proves the rationalization of the technical process.
|
|
基金项目：
|
|
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]魏泽辉．WHF法在轴类件生产中的应力[J]．重型机械科技，2004，(3)：32-33．
[2]王雷刚，黄瑶，刘助柏．大锻件拔长工艺研究进展与展望[J]．塑性工程学报，2002，9(2)：28-31、48．
[3]史宇麟．两次擞拔新工艺[J]．矿山机械，2000，(10)：61-62．
[4]孙前江，王高潮，黄映霞．曲轴锻造过程的数值模拟[J]．锻压技术，2006，31(2)：4-6．
[5]何利东，张光明．模拟技术在大型锻件工艺改进方面的应用[J]．锻压技术，2006，31(6)：12-16．
[6]李淑红，童放．浅谈曲轴自由锻造的下料计算[J]．锻压技术，2005，30(4)：1-2．
[7]崔振山，任广生，徐秉业，等．大锻件空洞的局部效应与锻合压下率研究[J]．工程力学，2003，20(2)：55-59．
[8]黄华贵，杜凤山，臧新良．大型零件M锻造法及其空洞缺陷锻合过程的数值模拟[J]．锻压技术，2005，30(增刊)：34-37．
[9]粱晨，刘助柏．LZ锻造的砧宽比、料宽比的临界值研究[J]．锻压技术，2004，29(3)：14-16．
[10]邓冬梅．大型锻件锻造新理论与新工艺的数值模拟[D]．秦皇岛：燕山大学，2001．
[11]袁朝龙，钟约先，马庆贤．大型锻件内部孔隙性缺陷修复规律的研究[J]．锻压技术，2002，27(3)：3-6．
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|