摘要：
|
|
通过对AZ31B镁合金手机壳的温冲试验研究,分析了凸、凹模温度、镁板温度和加热时间、冲压速度以及润滑条件对成形结果的影响。试验表明,在保证坯料充分退火和模具结构合理的前提下,拉深凸模温度保持在230℃,凹模及压边圈温度保持在280～320℃,用石墨对坯料凸缘和压边圈、凹模肩部进行有效润滑,同时,施加合适的压边力作用,便可以成功地冲压出镁合金壳形件。
|
|
Through the investigation on the stamping for the AZ31 magnesium alloy shell of mobile phone,the effects of the temperature of punch,die and sheet,distortion velocity,and lubricating agent on the formability were analyzed. The results show that,with sufficient annealing,proper die structure parameters and proper blank holding force, keeping the punch at 230℃,die and blank at 280～320℃,using the graphite to lubricate the blank and the shoulder part of die,the shell of the magnesium alloy can be obtained successfully.
|
|
基金项目：
|
|
教育部科技创新工程重大项目培育资金项目资助(704900)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]陈振华．变形镁合金[M]．北京：化学工业出版社，2005．
[2]刘正，张奎，曾小勤．镁基轻质合金理论基础及其应用[M]．北京：机械工业出版社，2002．
[3]Kenichi Manahea,Hiroshi Koyamaa,Shoichiro Yoshihara,et al.Development of a combination punch speed and blank-holder fuzzy control system for the deep-drawing process[J].Journal of Materials Processing Technology,2002,125-126:440-445.
[4]董海，王忠堂，张士宏，等．AZ31镁合金板热拉深成形工艺研究[J]．沈阳工业学院学报，2004，23(3)：61-64．
[5]张坤，徐永超，张士宏，等．镁合金板材温热拉深成形工艺的研究[J]．轻合金加工技术，2004．32(8)：16-18．
[6]邓明，许洪斌，刘峰．镁合金板材胀形和扩孔性能研究[J]．锻压技术，2004，29(4)：33-35．
[7]卢志文，张洪峰．汪凌云．镁合金的冲压成形工艺研究[J]．轻合金加工技术，2005，3(6)：45-48．
[8]曾志朋，刘晓飞，张艳姝，等．变形镁合金杯形件反挤压成形工艺研究[J]．锻压技术，2006，31(5)：64-66．
[9]陈振华．镁合金[M]．北京：化学工业出版社，2004．
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|