摘要：
|
|
探讨了充液成形过程中,关键工艺参数之一的液室压力大小对起皱和破裂两种失稳现象的作用和影响规律。从应力、应变、减薄率和FLD曲线等方面研究了液室压力对起皱和失稳现象的影响。首先模拟液室压力为12 MPa时的成形过程,分析了起皱的原因,再通过加大压力对起皱进行控制;而后模拟液室压力为35 MPa时的成形过程,分析了破裂的原因,再通过减小压力对破裂进行控制;最后利用难成形航空材料2806-M进行实验验证,得到了成形此零件的合理压力范围18～25 MPa。
|
|
The effect rule of one key technologic parameter in sheet hydroforming to the winkling and cracking failures of liquid pressure was discussed.The rule of liquid pressure affecting the winkling and cracking was researched from the factors of stress,strain,thinning and FLD.Firstly,the cause of winkle was analyzed by simulating lower pressure of 12 MPa,and then,wrinkling was solved by increasing the pressure.Secondly,the cause of crack was analyzed by simulating higher pressure of 35 MPa and the cracking was solved by decreasing the pressure.At last,by forming the part of 2B06-M,one of the difficult forming materials used in aerial manufacture,the better range for forming this part gained was 18～25 MPa.
|
|
基金项目：
|
|
国家自然科学基金(10577001)
|
|
作者简介：
|
|
|
|
参考文献：
|
[1]中村和彦．金属薄板的对向液压成形法[J]．技术，1985，125(9)：101-．
[2]Kim T J,Yang D Y,Han S S.Numerical modelling of the multi-stage sheet pair hydroforming process[J].J.Mater. Process Technol.,2004,151:48-53.
[3]郎利辉．杯形件液压成形的数值模拟[J]．中国有色金属报，2000，10(5)：631-634．
[4]Vollertsen F.Process layout avoiding reverse drawing wrin- kles in hydroforming of sheet metal[J].Annals of CIRP, 2002,52(1):203-208.
[5]Danckert J,Nielsen K B.Hydromechanical deep drawing with uniform pressure on the flange[J].CIRP,2000,49(1): 217-220.
[6]Lang Lihui,Danckert J,Nielsen K B.Analysis of key param- eters in sheet hydroforming combined with stretching forming and deep drawing[J].Journal of Engineering Manufacture Proceedings of the IMechE,Part B,2004,218:845-856.
[7]赵侠，傅建，余玲．数值模拟技术在汽车覆盖件成形中的应用[J]．锻压技术，2006，31(1)：15-21．
[8]王晓路，陈炜，高霖．数值模拟对薄板冲压成形工艺设计的优化[J]．锻压技术，2005，30(3)：21-25．
[9]余同希．章亮炽．塑性弯曲理论及其应用[M]．北京：科学出版社，1992．
[10]吉田弘美编，第一汽车制造厂车身分厂技术科译．冲压技术100例[M]．吉林：吉林人民出版社，1978．
[11]胡世光，陈鹤峥．板料冷压成形的工程解析[M]．北京：北京航空航天大学出版社，2004．
[12]张晓静，周贤宾。孔永明．板料成形数值模拟研究[J]．锻压技术，2001，26(1)：13-14．
|
|
服务与反馈：
|
|
【本网站尚未开通全文下载服务】【加入收藏】
|
|
|
|